Discovery of Li2(Pd,Pt)3B superconductors
P. Badica, K. Togano, H. Takeya, K. Hirata, S. Awaji, K. Watanabe
arXiv:cond-mat/0607626 · 2006-07-25
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Critical temperature Tc of the Li2(Pd1-xPtx)3B was reported to be 7-8K for x=0 and 2.2-2.8K for x=1. In this article we present our preliminary results on behavior of magnetization-temperature curves with starting composition of Pd-B precursor, y-Li concentration in LiyPd3B and post-annealing of the Pd-end compound. Results suggest that to maximize Tc ratio Pd:B should be close to 3:1, while y-Li has to be optimum. The lowest Tc for LiyPd3B was 4.4-4.6K, while post-annealings at 560 deg. C allowed enhancement of Tc up to 8.2-8.4K. Compositions Li2Z3B with Z=Ni, Ru, Rh, Re, Ag are not superconducting down to 1.8K. Exception is composition with Re showing superconductivity due to Re3B compound. All samples were prepared by arc melting.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Li2Pd3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.5 | Pressure not reported | unknown |
| Li2Pt3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.5 | Pressure not reported | unknown |
| LiyPd3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4.5 | Pressure not reported | unknown |
| LiyPd3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.3 | Pressure not reported | unknown |
| Re3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Superconductivity in metal rich Li-Pd-B ternary Boride
similarity 0.90K. Togano et al. · 2004 · arXiv:cond-mat/0402232
Source status unknown — claims are unverified
Abrupt enhancement of noncentrosymmetry and appearance of a spin-triplet superconducting state in Li2(Pd1−xPtx)3B beyond x=0.8
similarity 0.90S. Harada et al.
Source status unknown — claims are unverified
Specific-heat studies of the spin-orbit interaction in noncentrosymmetric Li2(Pd1−xPtx)3B (x=0,0.5,1) superconductors
similarity 0.89H. Takeya et al.
Source status unknown — claims are unverified
Superconductivity in the Metal Rich Li-Pd-B Ternary Boride
similarity 0.89K. Togano et al.
Source status unknown — claims are unverified
Critical temperature and upper critical field of LiPdCuB (x=0.0, 0.1, 0.2)superconductors
similarity 0.89A. A. Castro et al. · 2017 · arXiv:1703.02669
Source status unknown — claims are unverified
Low-temperature specific-heat and neutron-diffraction studies on Li2Pd3B and Li2Pt3B superconductors
similarity 0.88H. Takeya et al.
Source status unknown — claims are unverified