200 MeV Ag+15 ion irradiation created columnar defects and enhanced critical current density of La-2125 type superconducting thin films
K. R. Mavani, D. S. Rana, S. Rayaprol, R. N. Parmar, D. G. Kuberkar, Ravi Kumar, M. Tonouchi, J. John, R. Nagarajan
arXiv:cond-mat/0608213 · DOI 10.1016/j.ssc.2007.03.027 · 2006-08-09 · Solid State Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We have deposited c-axis oriented thin films of La1.5Dy0.5CaBa2Cu5Oz (La-2125) tetragonal superconductor on LaAlO3 (001) by Pulsed Laser Deposition. These films were irradiated with 200 MeV Ag+15 ions. Atomic Force Microscopy and Elastic Recoil Detection Analysis indicate that the irradiation has created columnar defects along the entire thickness (2000 A) of these films. With ion irradiation up to 1*10^11 ions/cm2, the critical current density (Jc(H)) is found to enhance by almost five folds, which is attributed to the augmented flux pinning by the columnar defects. A further increase in irradiation to 1*10^12 ions/cm2 causes reduction in Jc(H) due to distorted morphology of the film. Our work shows that the enhancement in Jc (H) of the irradiated La-2125 film is comparable to that in irradiated RE-123. Also, as the La-2125 type films have greater chemical stability than RE-123 (RE = rare earth ion), La-2125 type superconductors are potential candidates for applications. Interesting to note that there are partial flux jumps observed to occur symmetrically in the magnetic hysteresis of irradiated La-2125 thin films with enhanced Jc(H).
Similar papers
Neutron Diffraction Studies on La2-xDyxCa2xBa2Cu4+2xOz Superconductors
similarity 0.84S. Rayaprol et al. · 2004 · arXiv:cond-mat/0408333
Source status unknown — claims are unverified
Structural and Magnetic Studies on La2-xDyxCa2xBa2Cu4+2xOz Type Superconducting Oxides
similarity 0.84S. Rayaprol et al. · 2004 · arXiv:cond-mat/0408334
Source status unknown — claims are unverified
Effect of columnar defects on the pinning properties of NdFeAsO0.85 conglomerate particles
similarity 0.83J. D. Moore et al. · 2009 · arXiv:0907.0217
Source status unknown — claims are unverified
Critical current density and flux pinning in La2-xPrxCa2xBa2Cu4+2xOz (x = 0.1 - 0.5) superconductors
similarity 0.82S. Rayaprol et al. · 2004 · arXiv:cond-mat/0405506
Source status unknown — claims are unverified
Hall coefficient and Hc2 in underdoped LaFeAsO0.95F0.05
similarity 0.82Y. Kohama et al. · 2008 · arXiv:0806.4215
Source status unknown — claims are unverified
Enhancement in transition temperature and critical current density of CeO0.8F0.2FeAs by yttrium doping
similarity 0.82J. Prakash et al. · 2009 · arXiv:0908.3372
Source status unknown — claims are unverified