Switching Dynamics of Bi$_{2}$Sr$_{2}$CaCu$_{2}$O$_{8+δ}$ Intrinsic Josephson junctions: Macroscopic Quantum Tunneling and Self-Heating Effect

H. Kashiwaya, T. Matsumoto, H. Shibata, S. Kashiwaya, H. Eisaki, Y. Yoshida, S. Kawabata, Y. Tanaka

arXiv:cond-mat/0609615 · DOI 10.1143/JPSJ.77.104708 · 2006-09-24

T1theoretical35 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The switching dynamics of current-biased Bi$_{2}$Sr$_{2}$CaCu$_{2}$O$_{8+δ}$ intrinsic Josephson junctions (IJJs) was studied to clarify the effect of d-wave superconductivity and the stack structure on the switching properties. High quality IJJs were fabricated, and then the temperature dependence of the switching probability distribution was measured for the first and second switchings. Although the standard deviation of the distribution detected for both switchings showed similar saturation characteristics with decreasing temperature, the temperature at saturation was about 13 times higher for the second switching than for the first switching. The properties of the first switching can be explained in terms of a conventional underdamped JJ, that is, macroscopic quantum tunneling below the crossover temperature, and thermal activation with quality factor of 70$\pm$20 above the crossover temperature. In contrast, the relatively higher effective temperature for the second switching evaluated from the switching probability distribution suggests a dominant thermal activation process under the influence of the self-heating effect even at sufficiently low temperature.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Bi2Sr2CaCu2O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	Pressure not reported	unknown
Bi2Sr2CaCu2O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	80	Pressure not reported	unknown
YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	—