Improved critical current densities in MgB2 tapes with ZrB2 doping
Xianping Zhang, Zhaoshun Gao, Dongliang Wang, Zhengguang Yu, Yanwei Ma, S. Awaji, K. Watanabe
arXiv:cond-mat/0610286 · DOI 10.1063/1.2357884 · 2006-10-11 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
MgB2/Fe tapes with 2.5-15 at.% ZrB2 additions were prepared through the in situ powder-in-tube method. Compared to the pure tape, a significant improvement in the in-field critical current density Jc was observed, most notably for 10 at.% doping, while the critical temperature decreased slightly. At 4.2 K, the transport Jc for the 10 at.% doped sample increased by more than an order of magnitude than the undoped one in magnetic fields above 9 T. Nanoscale segregates or defects caused by the ZrB2 additions which act as effective flux pinning centers are proposed to be the main reason for the improved Jc field performance.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route
similarity 0.95Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601223
Source status unknown — claims are unverified
Improvement of critical current density in Fe-sheathed MgB2 tapes by ZrSi2, ZrB2 and WSi2 doping
similarity 0.95Yanwei Ma et al. · 2003 · arXiv:cond-mat/0306652
Source status unknown — claims are unverified
Strongly enhanced critical current density in Fe-sheathed MgB2 tapes by stearic acid and stearate doping
similarity 0.93Zhaoshun Gao et al. · 2007 · arXiv:cond-mat/0701373
Source status unknown — claims are unverified
Enhancement of JC-B Properties in MoSi2 doped MgB2 tapes
similarity 0.92Xianping Zhang et al. · 2006 · arXiv:cond-mat/0602402
Source status unknown — claims are unverified
Large irreversibility field in nanoscale C-doped MgB2/Fe tape conductors
similarity 0.91Yanwei Ma et al. · 2006 · arXiv:cond-mat/0608308
Source status unknown — claims are unverified
Effect of nano-C doping on the in-situ processed MgB2 tapes
similarity 0.91Xianping Zhang et al. · 2005 · arXiv:cond-mat/0509475
Source status unknown — claims are unverified