Non-linear effects in hopping conduction of single-crystal La_{2}CuO_{4 + δ}

B. I. Belevtsev, N. V. Dalakova, A. S. Panfilov

arXiv:cond-mat/9807297 · DOI 10.1063/1.593683 · 1998-07-22 · Low Temperature Physics

T2theoretical5 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The unusual non-linear effects in hopping conduction of single-crystal La_{2}CuO_{4 + δ} with excess oxygen has been observed. The resistance is measured as a function of applied voltage U (10^{-3} V - 25 V) in the temperature range 5 K < T < 300 K. At relatively high voltage (U > 0.1 V) the conduction of sample investigated corresponds well to Mott's variable-range hopping (VRH). An unusual conduction behavior is found, however, in low voltage range (approximately below 0.1 V), where the influence of electric field and (or) electron heating effect on VRH ought to be neglected. Here we have observed strong increase in resistance at increasing U at T < 20 K, whereas at T > 20 K the resistance decreases with increasing U. The magnetoresistance of the sample below 20 K has been positive at low voltage and negative at high voltage. The observed non-Ohmic behavior is attributable to inhomogeneity of the sample, and namely, to the enrichment of sample surface with oxygen during the course of the heat treatment of the sample in helium and air atmosphere before measurements. At low enough temperature (below 20 K) the surface layer with increased oxygen concentration is presumed to consist of disconnected superconducting regions (with T_{c} about 20 K) in poor-conducting matrix. The results obtained demonstrate that transport properties of cuprate oxides may be determined in essential degree by structural or stoichimetric inhomogeneities. This should be taken into account at evaluation of "quality" of high-temperature superconductors on the basis of transport properties measurements.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La2CuO4+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	Pressure not reported	unknown
La2CuO4+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure not reported	unknown