A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>
Rongping Wang, Yueliang Zhou, Shaohua Pan, Meng He, Zhenghao Chen, Guozhen Yang
arXiv:cond-mat/9912065 · DOI 10.1016/S0921-4534(99)00487-6 · 1999-12-04 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
YBCO films were successfully prepared on biaxially textured Ag{110}<211> substrates by using pulsed laser deposition. X-ray diffraction results showed that the degree of preferential orientation of Ag{110}<211> substrates varied with increasing annealing temperature. With a thin template layer deposited at low temperature, YBCO film with c-axis orientation and in-plane biaxial alignment could be obtained at high deposition temperature. Scanning electron microscopy observation revealed that YBCO grains enlarged but Ag grains on the surface of the YBCO films became smaller with increasing deposition temperature. At optimal deposition conditions, Ag atoms diffuse into the YBCO grain boundaries, and then fill in the weak-link regions in the YBCO film, resulting in the conduction easier. Jc value of 5105A/cm2 was obtained at 77K and zero magnetic field for the best YBCO film in our work.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Incommensurate Spin Dynamics in High Temperature Superconductor of Optimally Doped YBa2Cu3O7
similarity 0.93M. Arai et al. · 1999 · arXiv:cond-mat/9912233
Source status unknown — claims are unverified
Peak effect in a superconducting DyBa2Cu3O7-y film at microwave frequencies
similarity 0.91A. R. Bhangale et al. · 2001 · arXiv:cond-mat/0102192
Source status unknown — claims are unverified
Superconducting joining of melt-textured Y-Ba-Cu-O bulk material
similarity 0.90T. Prikhna et al. · 2000 · arXiv:cond-mat/0007461
Source status unknown — claims are unverified
Thickness independence of field induced time reversal symmetry breaking in Y/sub1 Ba/sub2 Cu/sub3 O/sub7-delta thin films
similarity 0.90Y. Dagan & G. Deutscher · 2001 · arXiv:cond-mat/0104012
Source status unknown — claims are unverified
Specific temperature dependence of pseudogap in YBaCuO nanolayers
similarity 0.90A. L. Solovjov et al. · 2018 · arXiv:1804.06119
Source status unknown — claims are unverified
Charge transport along the c-axis in high-T_c cuprates
similarity 0.89Yoichi Ando · 1999 · arXiv:cond-mat/9910320
Source status unknown — claims are unverified