Tc max
35.0 K
Tc ambient
35.0 K
arXiv year
2006
Papers
18
Tc exp.
35.0 K
Tc theo.
—
Evidence
experimental
Tc max measured at single_crystal, STM, DOI: 10.1103/PhysRevX.9.021021, confirmed by 7 papers
Evidence (29 records from 18 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 35.0 | — | single_crystal | STM | — | 2019 | T1 | DOI: 10.1103/PhysRevX.9.021021 |
| 35.0 | — | single_crystal | muSR | d-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.020511 |
| 35.0 | — | single_crystal | muSR | d-wave | 2010 | — | 1004.1275 |
| 35.0 | — | single_crystal | susceptibility | — | 2008 | T1 | 0806.1907 |
| 35.0 | — | single_crystal | susceptibility, muSR | d-wave | 2008 | T1 | DOI: 10.1103/PhysRevLett.101.227002 |
| 35.0 | — | single_crystal | ARPES, resistivity, susceptibility | d-wave | 2007 | T1 | DOI: 10.1103/PhysRevLett.98.267004 |
| 35.0 | — | single_crystal | ARPES, susceptibility, resistivity | d-wave | 2006 | T1 | cond-mat/0611517 |
| 34.8 | — | single_crystal | susceptibility, muSR | d-wave | 2009 | T1 | DOI: 10.1103/PhysRevB.79.180507 |
| 34.8 | — | single_crystal | susceptibility | d-wave | 2008 | T1 | 0811.2077 |
| 33.0 | — | single_crystal | resistivity | — | 2018 | T1 | DOI: 10.1103/PhysRevB.98.144507 |
| 33.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevLett.119.097001 |
| 33.0 | — | single_crystal | RIXS | — | 2017 | T1 | 1708.00663 |
| 32.0 | — | single_crystal | STM | — | 2019 | T1 | DOI: 10.1103/PhysRevX.9.021021 |
| 32.0 | — | single_crystal | ARPES | d-wave | 2014 | T1 | 1403.0492 |
| 32.0 | — | single_crystal | ARPES | d-wave | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.157003 |
| 31.0 | — | single_crystal | susceptibility | — | 2006 | T2 | cond-mat/0608409 |
| 29.0 | — | single_crystal | muSR | d-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.020511 |
| 29.0 | — | single_crystal | muSR | d-wave | 2010 | — | 1004.1275 |
| 25.0 | — | single_crystal | STM | — | 2019 | T1 | DOI: 10.1103/PhysRevX.9.021021 |
| 23.0 | — | single_crystal | ARPES | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.110.217006 |
| 23.0 | — | single_crystal | ARPES | — | 2012 | T1 | 1212.0335 |
| 23.0 | — | single_crystal | muSR | d-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.020511 |
| 23.0 | — | single_crystal | muSR | d-wave | 2010 | — | 1004.1275 |
| 15.0 | — | single_crystal | STM | — | 2019 | T1 | DOI: 10.1103/PhysRevX.9.021021 |
| 15.0 | — | single_crystal | resistivity | — | 2018 | T1 | DOI: 10.1103/PhysRevB.98.144507 |
| 14.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevLett.119.097001 |
| 14.0 | — | single_crystal | RIXS | — | 2017 | T1 | 1708.00663 |
| 11.0 | — | single_crystal | resistivity | — | 2018 | T1 | DOI: 10.1103/PhysRevB.98.144507 |
| — | — | — | — | d-wave | 2014 | T3 | 1403.2316 |
Superconducting parameters
- Pairing symmetry
- d-wave
- Gap structure
- nodal
- Hc2
- 60.0 T (0 K, H parallel c)
- λ_eph (e–ph coupling)
- —
Samples & pressure
- Sample form
- single_crystal
- Doping type
- hole
- Doping level
- 0.160