Ba(Fe0.94Co0.06)2As2
iron_based · body-centered tetragonal
ambient SCunconventionalcompeting order
Tc max
24.5 K
Tc ambient
24.0 K
arXiv year
2009
Papers
16
Tc exp.
24.5 K
Tc theo.
—
Evidence
experimental
Tc max measured at single_crystal, resistivity, DOI: 10.1103/PhysRevB.97.220501, confirmed by 2 papers
Evidence (16 records from 16 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 26.0 | — | single_crystal | susceptibility | — | 2009 | T1 | 0912.4945 |
| 24.5 | — | single_crystal | resistivity | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.220501 |
| 24.0 | — | single_crystal | resistivity, specific_heat | — | 2013 | T1 | 1310.2681 |
| 24.0 | — | single_crystal | susceptibility | — | 2012 | T1 | 1210.6386 |
| 23.7 | — | single_crystal | resistivity | — | 2016 | T1 | 1612.01961 |
| 22.0 | — | single_crystal | STM | — | 2017 | T1 | 1702.00419 |
| 20.0 | — | single_crystal | — | — | 2018 | — | 1801.02791 |
| 19.5 | — | single_crystal | resistivity | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.214515 |
| — | — | thin_film | STM | — | 2026 | T1 | 2601.15873 |
| — | — | — | neutron | — | 2018 | T3 | 1806.05581 |
| — | — | single_crystal | neutron | — | 2014 | T1 | 1410.5155 |
| — | — | — | optical_conductivity | s-wave | 2010 | T1 | 1003.5038 |
| — | — | single_crystal | STM | s_pm | 2010 | T1 | 1007.5086 |
| — | — | — | — | s_pm | 2010 | — | 1003.2609 |
| — | — | — | Raman | — | 2010 | T3 | 1008.0032 |
| — | — | single_crystal | susceptibility | — | 2009 | T3 | 0907.3973 |
Structure
- Crystal structure
- body-centered tetragonal
- Space group
- I4/mmm
- Lattice a (Å)
- 3.950
- Lattice c (Å)
- 12.980
Superconducting parameters
- Pairing symmetry
- s_pm
- λ_eph (e–ph coupling)
- —
Competing orders
- Competing order
- SDW
Samples & pressure
- Sample form
- single_crystal
- Pressure type
- none
- Doping type
- electron
- Doping level
- 0.060