Ba(Fe_0.9Co_0.1)₂As₂

iron_based · 122

ambient SCunconventional

Tc max

25.0 K

Tc ambient

22.5 K

arXiv year

2008

Papers

Tc exp.

25.0 K

Tc theo.

29.7 K

Evidence

experimental

Tc max measured at thin_film, resistivity, DOI: 10.1103/PhysRevB.82.224507, confirmed by 4 papers

Evidence (24 records from 20 papers)

the flat columns above are aggregates — each line here is one paper's claim

Tc (K)	P (GPa)	Sample	Method	Pairing	Year	Tier	Paper
29.7	—	—	—	s_pm	2010	—	1009.1572
26.0	—	thin_film	—	s_pm	2015	T1	1511.05017
25.0	—	thin_film	resistivity	s_pm	2010	T1	DOI: 10.1103/PhysRevB.82.224507
25.0	—	thin_film	resistivity	—	2010	T1	1005.0692
25.0	—	single_crystal	resistivity	—	2008	T1	0811.2621
24.0	—	single_crystal	susceptibility	—	2008	T1	0811.2621
22.5	—	single_crystal	—	—	2014	T1	1401.3706
22.5	—	single_crystal	ARPES	unknown	2014	T1	1408.4260
22.3	—	thin_film	resistivity	—	2010	—	1001.2505
22.0	—	thin_film	resistivity	s_pm	2011	T1	1112.4636
22.0	—	thin_film	resistivity	s_pm	2010	T1	DOI: 10.1103/PhysRevB.82.224507
22.0	—	thin_film	—	s_pm	2010	T1	1005.0692
20.0	—	thin_film	resistivity	s-wave	2011	T1	DOI: 10.1103/PhysRevB.83.140502
20.0	—	thin_film	—	s_pm	2010	T1	1008.3473
20.0	—	thin_film	resistivity	s-wave	2010	T1	DOI: 10.1103/PhysRevB.81.060509
20.0	—	thin_film	resistivity	s-wave	2009	T1	0912.1256
19.5	—	single_crystal	susceptibility	—	2011	T1	1109.5479
19.3	—	single_crystal	susceptibility	—	2011	—	1106.6065
19.0	ambient	single_crystal	specific_heat	unknown	2010	T1	1011.4808
—	—	single_crystal	resistivity, susceptibility	—	2012	T1	1207.2457
—	—	—	resistivity	—	2011	T1	1103.4501
—	—	—	—	s_pm	2010	—	1003.2609
—	—	single_crystal	resistivity	unknown	2009	T1	0910.4230
—	—	single_crystal	resistivity	—	2008	T1	0811.2621