Tc max
25.8 K
Tc ambient
25.1 K
arXiv year
2008
Papers
96
Tc exp.
25.8 K
Tc theo.
—
Evidence
experimental
Tc max measured at P=3.65 GPa, single_crystal, resistivity, DOI: 10.1103/PhysRevB.97.144515, confirmed by 2 papers
Evidence (165 records from 96 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 29.0 | — | thin_film | resistivity | — | 2025 | T1 | DOI: 10.1103/jmrh-347m |
| 25.8 | 3.6 | single_crystal | resistivity | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.144515 |
| 25.8 | 3.5 | single_crystal | susceptibility | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.144515 |
| 25.5 | — | thin_film | resistivity | — | 2012 | — | 1205.4103 |
| 25.1 | — | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064521 |
| 25.0 | — | single_crystal | susceptibility, neutron, ARPES | — | 2016 | T1 | 1605.04257 |
| 25.0 | — | — | resistivity | s-wave | 2013 | T1 | 1308.1294 |
| 25.0 | — | single_crystal | neutron | s_pm | 2010 | T1 | DOI: 10.1103/PhysRevB.81.140501 |
| 24.8 | — | single_crystal | resistivity | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.020507 |
| 24.8 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 24.8 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.220504 |
| 24.8 | — | thin_film | resistivity | — | 2010 | T1 | 1004.5557 |
| 24.8 | — | single_crystal | resistivity | — | 2010 | T1 | 1009.2848 |
| 24.7 | — | single_crystal | — | s-wave | 2010 | T1 | 1007.0720 |
| 24.7 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.180521 |
| 24.6 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 24.5 | — | single_crystal | ARPES | s_pm | 2012 | T1 | DOI: 10.1103/PhysRevB.85.144508 |
| 24.5 | — | single_crystal | resistivity | s_pm | 2010 | T1 | DOI: 10.1103/PhysRevLett.105.237002 |
| 24.5 | — | thin_film | — | — | 2009 | T1 | 0909.4902 |
| 24.4 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 24.4 | — | thin_film | resistivity | — | 2010 | T1 | 1004.5557 |
| 24.3 | — | single_crystal | susceptibility | — | 2018 | T1 | 1806.10689 |
| 24.1 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 24.0 | — | single_crystal | susceptibility | — | 2022 | T1 | DOI: 10.1103/PhysRevLett.129.187002 |
| 24.0 | — | — | susceptibility | — | 2019 | — | 1903.00053 |
| 24.0 | — | single_crystal | resistivity | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.064515 |
| 24.0 | — | single_crystal | ARPES | — | 2011 | T1 | DOI: 10.1103/PhysRevB.83.064516 |
| 24.0 | — | — | STM | s_pm | 2011 | T1 | 1107.0697 |
| 24.0 | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.180510 |
| 24.0 | — | single_crystal | resistivity, specific_heat | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.014506 |
| 24.0 | — | single_crystal | — | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.172504 |
| 23.7 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 23.5 | — | single_crystal | susceptibility | — | 2014 | T1 | 1403.6152 |
| 23.5 | — | single_crystal | — | s-wave | 2010 | T1 | 1007.0720 |
| 23.5 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.180521 |
| 23.3 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 23.0 | — | thin_film | — | s_pm | 2022 | T1 | 2207.05958 |
| 23.0 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.217001 |
| 23.0 | — | single_crystal | — | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.094507 |
| 22.9 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 22.5 | — | single_crystal | susceptibility | s_pm | 2010 | T1 | DOI: 10.1103/PhysRevB.82.060518 |
| 22.5 | ambient | single_crystal | susceptibility | s_pm | 2010 | T1 | 1003.2959 |
| 22.4 | — | single_crystal | susceptibility | s_pm | 2010 | T1 | 1012.3436 |
| 22.2 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevLett.104.067002 |
| 22.2 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 22.2 | — | single_crystal | resistivity | — | 2010 | T1 | 1003.0383 |
| 22.1 | — | single_crystal | resistivity | — | 2010 | T1 | 1003.0383 |
| 22.1 | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.214518 |
| 22.0 | — | single_crystal | resistivity, STM | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.134520 |
| 22.0 | — | single_crystal | ARPES | — | 2017 | T1 | DOI: 10.1103/PhysRevB.95.144513 |
| 22.0 | — | single_crystal | ARPES | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.195147 |
| 22.0 | — | single_crystal | resistivity | unknown | 2012 | T1 | DOI: 10.1103/PhysRevLett.109.027006 |
| 22.0 | — | single_crystal | — | s-wave | 2010 | T1 | 1007.0720 |
| 22.0 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.180521 |
| 22.0 | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.180510 |
| 22.0 | — | single_crystal | susceptibility | — | 2008 | — | 0811.1617 |
| 21.8 | — | single_crystal | susceptibility | — | 2009 | — | 0906.2125 |
| 21.8 | — | single_crystal | susceptibility | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.140501 |
| 21.6 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 21.1 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 21.0 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.217001 |
| 21.0 | — | single_crystal | — | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.172504 |
| 20.5 | — | single_crystal | resistivity | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.020507 |
| 20.5 | — | single_crystal | — | s-wave | 2010 | T1 | 1007.0720 |
| 20.5 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.180521 |
| 20.0 | — | single_crystal | STM | s-wave | 2011 | T1 | DOI: 10.1103/PhysRevLett.106.087004 |
| 20.0 | — | — | STM | s_pm | 2011 | T1 | 1107.0697 |
| 20.0 | — | single_crystal | — | s-wave | 2010 | T1 | 1007.0720 |
| 20.0 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.180521 |
| 19.6 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 19.6 | — | single_crystal | susceptibility | unknown | 2010 | T1 | 1012.3436 |
| 19.0 | — | single_crystal | susceptibility, neutron, ARPES | — | 2016 | T1 | 1605.04257 |
| 18.6 | — | single_crystal | susceptibility | unknown | 2010 | T1 | 1012.3436 |
| 18.0 | — | thin_film | resistivity | — | 2025 | — | 2506.16276 |
| 17.7 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 17.2 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 17.1 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevLett.104.067002 |
| 17.0 | — | single_crystal | susceptibility | — | 2018 | T1 | DOI: 10.1103/PhysRevLett.121.267001 |
| 17.0 | — | single_crystal | ARPES | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.195147 |
| 17.0 | — | single_crystal | neutron | — | 2010 | T1 | DOI: 10.1103/PhysRevB.81.140510 |
| 16.7 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 16.6 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 16.2 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 16.2 | — | thin_film | — | — | 2009 | T1 | 0909.4902 |
| 15.8 | — | single_crystal | susceptibility | unknown | 2010 | T1 | 1012.3436 |
| 15.5 | — | single_crystal | susceptibility | unknown | 2010 | T1 | 1012.3436 |
| 15.2 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 15.1 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.220504 |
| 15.1 | — | single_crystal | resistivity | — | 2010 | T1 | 1009.2848 |
| 15.0 | — | single_crystal | ARPES | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.195147 |
| 15.0 | — | single_crystal | susceptibility | — | 2008 | — | 0811.1617 |
| 14.8 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 14.8 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 14.6 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevLett.104.067002 |
| 14.6 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 14.5 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 14.4 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 14.2 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 14.0 | — | single_crystal | STM | s-wave | 2011 | T1 | DOI: 10.1103/PhysRevLett.106.087004 |
| 14.0 | — | — | STM | s_pm | 2011 | T1 | 1107.0697 |
| 13.9 | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.064502 |
| 13.7 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 13.5 | — | single_crystal | susceptibility | unknown | 2010 | T1 | 1012.3436 |
| 13.0 | — | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevLett.109.027004 |
| 13.0 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 12.8 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.220504 |
| 12.8 | — | single_crystal | resistivity | — | 2010 | T1 | 1009.2848 |
| 12.5 | — | single_crystal | specific_heat, susceptibility | — | 2011 | — | 1110.3403 |
| 11.6 | — | single_crystal | specific_heat | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.224509 |
| 11.0 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 10.8 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 10.2 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 10.1 | — | single_crystal | resistivity | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevLett.104.067002 |
| 9.7 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 9.3 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 8.4 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 8.2 | — | single_crystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064501 |
| 8.0 | — | — | resistivity | s-wave | 2013 | T1 | 1308.1294 |
| — | — | — | — | s+d | 2024 | T1 | 2402.17945 |
| — | — | — | susceptibility | — | 2019 | — | 1903.00053 |
| — | — | single_crystal | resistivity, susceptibility | — | 2019 | T3 | 1911.03390 |
| — | — | single_crystal | susceptibility | — | 2019 | T1 | DOI: 10.1103/PhysRevApplied.11.014035 |
| — | — | — | — | — | 2018 | — | 1804.04987 |
| — | — | single_crystal | — | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.014511 |
| — | — | single_crystal | susceptibility | — | 2018 | T1 | DOI: 10.1103/PhysRevLett.121.267001 |
| — | — | — | STM | — | 2018 | T1 | 1803.01983 |
| — | — | — | — | s_pm | 2018 | T3 | 1812.10118 |
| — | — | single_crystal | susceptibility | — | 2017 | T1 | 1701.01578 |
| — | — | single_crystal | resistivity | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.085147 |
| — | — | — | resistivity | — | 2016 | T3 | 1608.05474 |
| — | — | thin_film | resistivity | — | 2016 | T1 | 1606.02865 |
| — | — | single_crystal | — | — | 2013 | T1 | 1310.5608 |
| — | — | single_crystal | resistivity | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.110.207001 |
| — | — | single_crystal | susceptibility | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.207201 |
| — | — | thin_film | resistivity | — | 2013 | T1 | 1302.3696 |
| — | — | single_crystal | susceptibility, resistivity | s_pm | 2013 | T1 | 1308.0537 |
| — | — | single_crystal | susceptibility | — | 2013 | T1 | 1310.4080 |
| — | — | single_crystal | resistivity | — | 2013 | T1 | 1308.6133 |
| — | — | single_crystal | specific_heat | — | 2012 | T1 | 1208.2492 |
| — | — | — | susceptibility | — | 2012 | — | 1205.5822 |
| — | — | single_crystal | resistivity | — | 2012 | T1 | 1208.1575 |
| — | — | single_crystal | resistivity, susceptibility | — | 2012 | T1 | 1209.3586 |
| — | — | thin_film | resistivity | — | 2012 | T1 | 1211.3879 |
| — | — | thin_film | — | — | 2012 | T1 | 1211.6464 |
| — | — | single_crystal | ARPES | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.020509 |
| — | — | single_crystal | susceptibility | s_pm | 2011 | T1 | DOI: 10.1103/PhysRevLett.106.067001 |
| — | — | single_crystal | neutron | s_pm | 2011 | T1 | DOI: 10.1103/PhysRevLett.106.257001 |
| — | — | single_crystal | — | — | 2011 | T1 | 1107.5934 |
| — | — | — | — | — | 2011 | T3 | 1109.2703 |
| — | 0.0 | single_crystal | resistivity | — | 2010 | — | 1002.3364 |
| — | — | single_crystal | — | — | 2010 | T1 | 1004.3804 |
| — | — | single_crystal | susceptibility | — | 2010 | T1 | DOI: 10.1103/PhysRevB.81.184513 |
| — | — | single_crystal | specific_heat | — | 2010 | T1 | DOI: 10.1103/PhysRevB.81.184518 |
| — | — | single_crystal | muSR | — | 2010 | T3 | 1005.2136 |
| — | — | — | neutron | — | 2010 | — | 1002.3350 |
| — | — | single_crystal | susceptibility | — | 2009 | T1 | 0902.0201 |
| — | — | single_crystal | resistivity | — | 2009 | T1 | 0904.3134 |
| — | — | single_crystal | specific_heat | — | 2009 | T1 | 0905.2955 |
| — | ambient | — | — | — | 2009 | T1 | 0906.1548 |
| — | — | single_crystal | susceptibility | — | 2009 | T3 | 0906.5184 |
| — | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.060501 |
| — | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.140508 |
| — | — | single_crystal | susceptibility | — | 2009 | T1 | 0910.3600 |
| — | — | — | — | unknown | 2009 | T1 | 0907.3741 |
| — | — | single_crystal | specific_heat | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.220516 |
Structure
- Crystal structure
- tetragonal
- Space group
- I4/mmm
- Lattice c (Å)
- 1.239
Superconducting parameters
- Hc2
- 60.0 T (90 kOe applied field)
- λ_eph (e–ph coupling)
- 0.30
Competing orders
- T_SDW
- 60.0 K
- T_AFM
- 47.0 K
- ρ(T) exponent
- 1.00
Samples & pressure
- Sample form
- single_crystal
- Substrate
- SrTiO3
- Pressure type
- none
- Doping type
- electron
- Doping level
- 0.074