Tc max
32.6 K
Tc ambient
29.0 K
arXiv year
2008
Papers
11
Tc exp.
32.6 K
Tc theo.
—
Evidence
experimental
Tc max measured at powder, susceptibility, arXiv:1108.4307, confirmed by 2 papers
Evidence (12 records from 11 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 33.0 | — | single_crystal | susceptibility | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.184514 |
| 32.6 | — | powder | susceptibility | s_pm | 2011 | T1 | 1108.4307 |
| 30.3 | — | single_crystal | resistivity | s_++ | 2023 | T1 | 2306.08703 |
| 30.0 | — | single_crystal | — | — | 2013 | T1 | DOI: 10.1103/PhysRevB.88.184514 |
| 29.0 | — | single_crystal | resistivity | — | 2011 | T1 | 1106.4256 |
| 28.7 | — | single_crystal | resistivity, susceptibility | — | 2008 | — | 0807.0759 |
| 28.3 | ambient | single_crystal | resistivity | — | 2008 | T1 | 0808.2392 |
| 28.0 | — | single_crystal | resistivity | — | 2018 | T1 | 1806.02097 |
| 28.0 | — | single_crystal | susceptibility | — | 2018 | T1 | 1801.04972 |
| 28.0 | — | single_crystal | susceptibility | — | 2017 | T1 | DOI: 10.1103/PhysRevB.95.134509 |
| 25.0 | — | single_crystal | neutron | — | 2024 | T1 | 2412.16870 |
| — | — | single_crystal | resistivity, specific_heat | — | 2018 | T1 | 1810.08628 |
Structure
- Crystal structure
- tetragonal
Superconducting parameters
- λ_eph (e–ph coupling)
- —
Competing orders
- Competing order
- AFM
- T_AFM
- 90.0 K
Samples & pressure
- Sample form
- single_crystal
- Pressure type
- none
- Doping type
- hole
- Doping level
- 0.250