Tc max
39.0 K
Tc ambient
39.0 K
arXiv year
2008
Papers
99
Tc exp.
39.0 K
Tc theo.
34.0 K
Evidence
experimental
Tc max measured at single_crystal, susceptibility, arXiv:1406.2369, confirmed by 6 papers
Evidence (162 records from 99 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 39.8 | — | thin_film | — | — | 2022 | T1 | 2207.06629 |
| 39.0 | — | single_crystal | resistivity, specific_heat | unknown | 2016 | T1 | DOI: 10.1103/PhysRevB.93.214519 |
| 39.0 | — | — | thermal_conductivity | — | 2016 | T1 | 1602.03914 |
| 39.0 | — | single_crystal | susceptibility | s_pm | 2014 | T1 | 1406.2369 |
| 39.0 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.104514 |
| 39.0 | — | single_crystal | susceptibility | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.014517 |
| 38.7 | — | — | susceptibility | s_pm | 2019 | T1 | 1905.01189 |
| 38.7 | — | single_crystal | susceptibility | — | 2011 | — | 1105.2265 |
| 38.6 | — | single_crystal | magnetization, resistivity | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.064516 |
| 38.4 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184511 |
| 38.4 | ambient | single_crystal | specific_heat | s-wave | 2016 | T1 | DOI: 10.1103/PhysRevB.94.205113 |
| 38.4 | — | single_crystal | resistivity | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.184522 |
| 38.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.95.085125 |
| 38.0 | — | single_crystal | resistivity | — | 2014 | T1 | 1404.3664 |
| 38.0 | — | single_crystal | ARPES | — | 2014 | T1 | DOI: 10.1103/PhysRevB.89.064514 |
| 38.0 | — | single_crystal | ARPES | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.195124 |
| 38.0 | — | — | — | — | 2009 | T1 | 0902.1085 |
| 38.0 | — | — | — | — | 2008 | T1 | 0807.4096 |
| 37.3 | — | polycrystal | specific_heat | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.81.014529 |
| 37.3 | — | polycrystal | specific_heat | s-wave | 2009 | T1 | 0910.0389 |
| 37.2 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184511 |
| 37.0 | — | — | susceptibility | — | 2018 | T1 | 1802.09868 |
| 37.0 | — | single_crystal | susceptibility | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.104514 |
| 37.0 | — | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.180502 |
| 37.0 | — | single_crystal | ARPES | s-wave | 2011 | T1 | DOI: 10.1103/PhysRevB.83.020501 |
| 37.0 | ambient | single_crystal | resistivity | s_pm | 2008 | T1 | 0811.4668 |
| 37.0 | — | single_crystal | resistivity, susceptibility | unknown | 2008 | T1 | 0808.2185 |
| 37.0 | — | single_crystal | ARPES | — | 2008 | T1 | DOI: 10.1103/PhysRevB.78.184508 |
| 36.5 | — | polycrystal | specific_heat | s-wave | 2009 | T1 | 0910.0389 |
| 36.4 | — | single_crystal | ARPES | — | 2026 | T1 | DOI: 10.1103/yry8-qdm6 |
| 36.0 | — | thin_film | resistivity | — | 2021 | T1 | DOI: 10.1103/PhysRevMaterials.5.014801 |
| 36.0 | — | thin_film | — | — | 2020 | T1 | 2012.13723 |
| 36.0 | — | single_crystal | resistivity, ARPES | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.235135 |
| 36.0 | — | polycrystal | specific_heat | s-wave | 2009 | T1 | 0910.0389 |
| 35.6 | — | single_crystal | resistivity | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.104512 |
| 34.6 | — | single_crystal | specific_heat | — | 2008 | — | 0810.1944 |
| 34.0 | — | — | — | s-wave | 2024 | T1 | DOI: 10.1103/PhysRevResearch.6.013121 |
| 33.2 | — | single_crystal | susceptibility | — | 2011 | T1 | DOI: 10.1103/PhysRevB.83.094519 |
| 33.1 | — | single_crystal | susceptibility | — | 2010 | T1 | 1010.3581 |
| 32.8 | — | single_crystal | STM | — | 2010 | T1 | 1008.2880 |
| 32.7 | — | single_crystal | susceptibility | — | 2010 | T1 | 1008.2880 |
| 32.7 | — | single_crystal | susceptibility | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.054513 |
| 32.7 | — | single_crystal | susceptibility | — | 2009 | — | 0902.1252 |
| 32.7 | — | single_crystal | susceptibility | s-wave | 2009 | T1 | DOI: 10.1103/PhysRevB.80.014518 |
| 32.6 | — | polycrystal | susceptibility | — | 2011 | T1 | DOI: 10.1103/PhysRevLett.107.237001 |
| 32.0 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.104514 |
| 32.0 | — | single_crystal | muSR, ARPES, resistivity, susceptibility | — | 2009 | — | 0901.2329 |
| 32.0 | — | single_crystal | muSR, ARPES | — | 2009 | T1 | DOI: 10.1103/PhysRevLett.102.187005 |
| 32.0 | — | single_crystal | resistivity, susceptibility | — | 2009 | T1 | 0903.4537 |
| 32.0 | — | single_crystal | ARPES | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.054517 |
| 32.0 | ambient | single_crystal | susceptibility | — | 2009 | T1 | DOI: 10.1103/PhysRevLett.102.117006 |
| 32.0 | — | single_crystal | ARPES | — | 2008 | T1 | 0809.4455 |
| 32.0 | — | single_crystal | susceptibility | — | 2008 | T1 | 0811.2224 |
| 31.2 | — | single_crystal | susceptibility, resistivity | s-wave | 2009 | T1 | DOI: 10.1103/PhysRevLett.102.207001 |
| 31.0 | — | single_crystal | microwave | — | 2022 | T2 | 2208.13577 |
| 31.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.95.085125 |
| 31.0 | — | single_crystal | resistivity | — | 2009 | T1 | 0907.2598 |
| 30.1 | ambient | single_crystal | resistivity | — | 2016 | T1 | DOI: 10.1103/PhysRevB.93.144401 |
| 30.0 | — | single_crystal | susceptibility | — | 2011 | — | 1105.2265 |
| 30.0 | — | single_crystal | resistivity | unknown | 2009 | T1 | 0904.4049 |
| 30.0 | — | single_crystal | susceptibility | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.020501 |
| 30.0 | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.140503 |
| 29.0 | — | single_crystal | resistivity | s-wave | 2009 | T1 | DOI: 10.1103/PhysRevLett.102.147002 |
| 28.5 | — | polycrystal | susceptibility | — | 2011 | T1 | DOI: 10.1103/PhysRevLett.107.237001 |
| 28.2 | — | single_crystal | resistivity | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.184522 |
| 28.0 | — | single_crystal | resistivity | — | 2015 | — | 1505.01645 |
| 28.0 | — | single_crystal | resistivity | — | 2015 | T1 | DOI: 10.1103/PhysRevLett.115.027003 |
| 28.0 | — | single_crystal | susceptibility | — | 2009 | — | 0902.1252 |
| 28.0 | — | single_crystal | susceptibility | s-wave | 2009 | T1 | DOI: 10.1103/PhysRevB.80.014518 |
| 27.0 | — | single_crystal | microwave | — | 2022 | T2 | 2208.13577 |
| 26.2 | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.014514 |
| 26.0 | — | single_crystal | resistivity, ARPES | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.235135 |
| 26.0 | — | — | thermal_conductivity | — | 2016 | T1 | 1602.03914 |
| 26.0 | — | single_crystal | ARPES | s-wave | 2011 | T1 | DOI: 10.1103/PhysRevB.83.020501 |
| 26.0 | — | single_crystal | resistivity | unknown | 2009 | T1 | 0904.4049 |
| 26.0 | — | single_crystal | resistivity | s-wave | 2009 | T1 | DOI: 10.1103/PhysRevLett.102.147002 |
| 26.0 | — | single_crystal | resistivity | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.140503 |
| 26.0 | ambient | single_crystal | — | — | 2009 | T1 | DOI: 10.1103/PhysRevLett.102.117006 |
| 25.8 | — | single_crystal | ARPES | — | 2026 | T1 | DOI: 10.1103/yry8-qdm6 |
| 25.6 | — | single_crystal | susceptibility | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.014514 |
| 25.4 | ambient | single_crystal | resistivity | — | 2016 | T1 | DOI: 10.1103/PhysRevB.93.144401 |
| 25.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.95.085125 |
| 23.0 | — | polycrystal | susceptibility | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.81.014529 |
| 22.9 | — | polycrystal | specific_heat | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.81.014529 |
| 22.9 | — | polycrystal | specific_heat | — | 2009 | T1 | 0910.0389 |
| 22.7 | — | polycrystal | susceptibility | — | 2011 | T1 | DOI: 10.1103/PhysRevLett.107.237001 |
| 22.5 | — | single_crystal | magneto-optic | — | 2022 | T2 | 2208.13577 |
| 22.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184511 |
| 22.0 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.89.115112 |
| 21.0 | — | single_crystal | specific_heat | — | 2023 | T1 | DOI: 10.1103/PhysRevB.108.054504 |
| 20.8 | ambient | single_crystal | resistivity | — | 2016 | T1 | DOI: 10.1103/PhysRevB.93.144401 |
| 20.0 | — | single_crystal | susceptibility | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.094508 |
| 20.0 | — | — | susceptibility | — | 2018 | T1 | 1809.00762 |
| 20.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184511 |
| 20.0 | 1.0 | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.140502 |
| 20.0 | — | single_crystal | ARPES | s-wave | 2012 | T1 | DOI: 10.1103/PhysRevB.86.165117 |
| 20.0 | — | single_crystal | ARPES | — | 2012 | T1 | 1204.0326 |
| 19.6 | — | single_crystal | resistivity | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.094508 |
| 19.6 | — | — | resistivity | — | 2018 | T1 | 1809.00762 |
| 19.0 | — | single_crystal | resistivity | — | 2023 | T1 | DOI: 10.1103/PhysRevB.108.054504 |
| 19.0 | — | single_crystal | specific_heat | — | 2022 | T1 | 2212.01183 |
| 19.0 | — | single_crystal | resistivity | — | 2012 | T1 | 1202.3833 |
| 18.6 | — | single_crystal | susceptibility | — | 2011 | — | 1105.2265 |
| 18.0 | — | single_crystal | resistivity, ARPES | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.235135 |
| 18.0 | — | single_crystal | susceptibility | — | 2015 | — | 1505.01645 |
| 18.0 | — | single_crystal | susceptibility | — | 2015 | T1 | DOI: 10.1103/PhysRevLett.115.027003 |
| 18.0 | ambient | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.140502 |
| 15.5 | — | single_crystal | susceptibility | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.094508 |
| 15.5 | — | — | susceptibility | — | 2018 | T1 | 1809.00762 |
| 15.0 | ambient | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.140502 |
| 14.5 | — | single_crystal | susceptibility | — | 2011 | — | 1105.2265 |
| 14.0 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.104514 |
| 13.0 | — | single_crystal | specific_heat | — | 2015 | T1 | 1506.00058 |
| 12.6 | ambient | — | resistivity, specific_heat | — | 2022 | T3 | 2212.13515 |
| 12.0 | — | single_crystal | ARPES | — | 2026 | T1 | DOI: 10.1103/yry8-qdm6 |
| 12.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184511 |
| 11.7 | — | single_crystal | resistivity | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.184522 |
| 11.2 | — | single_crystal | susceptibility | — | 2011 | — | 1105.2265 |
| 11.0 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.89.115112 |
| 11.0 | — | single_crystal | resistivity | — | 2012 | T1 | 1202.3833 |
| 10.5 | ambient | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.140502 |
| 10.0 | — | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184511 |
| 7.3 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.89.115112 |
| 7.3 | ambient | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.140502 |
| 7.2 | — | single_crystal | specific_heat | — | 2015 | T1 | 1506.00058 |
| 7.0 | — | single_crystal | resistivity, specific_heat | unknown | 2016 | T1 | DOI: 10.1103/PhysRevB.93.214519 |
| 7.0 | — | — | thermal_conductivity | — | 2016 | T1 | 1602.03914 |
| 7.0 | — | single_crystal | susceptibility | unknown | 2014 | T1 | 1406.2369 |
| 7.0 | — | single_crystal | susceptibility | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.014517 |
| 6.0 | — | — | — | — | 2016 | T1 | 1610.08593 |
| 5.6 | — | single_crystal | specific_heat | — | 2015 | T1 | 1506.00058 |
| 5.5 | — | single_crystal | ARPES | — | 2026 | T1 | DOI: 10.1103/yry8-qdm6 |
| 3.7 | — | single_crystal | resistivity | — | 2014 | T1 | DOI: 10.1103/PhysRevB.89.115112 |
| 3.5 | — | single_crystal | resistivity | — | 2013 | T1 | 1308.6133 |
| — | — | single_crystal | resistivity | — | 2025 | T1 | 2501.11936 |
| — | — | — | — | — | 2023 | — | 2309.12615 |
| — | — | — | resistivity | s_pm | 2021 | T1 | 2105.09159 |
| — | — | — | resistivity | — | 2019 | T3 | 1903.07960 |
| — | — | — | — | — | 2019 | T3 | 1906.05789 |
| — | — | single_crystal | resistivity | — | 2019 | T1 | DOI: 10.1103/PhysRevLett.122.217002 |
| — | — | single_crystal | specific_heat, susceptibility, muSR | s-wave | 2018 | T1 | 1809.03610 |
| — | — | single_crystal | susceptibility | — | 2017 | T1 | 1708.00683 |
| — | — | single_crystal | muSR, resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.95.054512 |
| — | — | single_crystal | susceptibility | — | 2017 | T1 | 1701.01578 |
| — | — | single_crystal | — | s_pm | 2017 | T1 | 1703.07749 |
| — | — | single_crystal | resistivity | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.085147 |
| — | — | — | resistivity, susceptibility | — | 2016 | T3 | 1608.05474 |
| — | — | single_crystal | susceptibility, resistivity | s_pm | 2016 | T1 | 1605.04183 |
| — | ambient | single_crystal | specific_heat | s-wave | 2016 | T1 | 1605.05485 |
| — | — | single_crystal | specific_heat, susceptibility | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.064502 |
| — | — | single_crystal | specific_heat | — | 2014 | T1 | 1412.7038 |
| — | — | — | — | s_pm | 2014 | T3 | 1412.7439 |
| — | — | — | ARPES | — | 2014 | T1 | 1404.6486 |
| — | — | single_crystal | ARPES | — | 2014 | T1 | DOI: 10.1103/PhysRevX.4.031041 |
| — | — | single_crystal | resistivity, susceptibility | — | 2014 | T1 | 1403.0227 |
| — | — | — | specific_heat | unknown | 2013 | T1 | 1308.1473 |
| — | — | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.85.064522 |
| — | — | — | — | s_pm | 2012 | T1 | 1203.0991 |
| — | — | single_crystal | resistivity | — | 2011 | T1 | DOI: 10.1103/PhysRevLett.107.067001 |
| — | — | — | — | — | 2008 | — | 0810.2694 |
| — | — | single_crystal | ARPES | — | 2008 | T1 | DOI: 10.1103/PhysRevLett.101.177005 |
| — | — | single_crystal | resistivity | — | 2008 | T1 | DOI: 10.1103/PhysRevB.78.140501 |
Structure
- Crystal structure
- I4/mmm
- Space group
- I4/mmm
- Lattice c (Å)
- 13.000
Superconducting parameters
- Pairing symmetry
- s-wave
- Hc2
- 75.0 T
- λ_eph (e–ph coupling)
- 4.12
Competing orders
- Competing order
- SDW
- T_SDW
- 121.0 K
- T_AFM
- 91.0 K
- ρ(T) exponent
- 2.00
Samples & pressure
- Sample form
- single_crystal
- Substrate
- MgO
- Pressure type
- none
- Doping type
- hole
- Doping level
- 0.300