Tc max
9.0 K
Tc ambient
—
arXiv year
2021
Papers
2
Tc exp.
9.0 K
Tc theo.
71.0 K
Evidence
mixed
Tc max measured at P=142 GPa, polycrystal, resistivity, arXiv:2603.14051
Evidence (2 records from 2 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 71.0 | 3.0 | — | — | — | 2021 | T1 | 2112.02131 |
| 9.0 | 142.0 | polycrystal | resistivity | — | 2026 | T1 | 2603.14051 |
Hydride Tc parameters (13)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| BaSiH8 | 71.0 | 3.0 | — | — | — | DFT | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| BaSiH8 | 71.0 | 3.0 | — | — | — | DFT | 2023 | 2311.01656 |
| BaSiH8 | 71.0 | 3.0 | — | — | — | cited | 2023 | 2311.01656 |
| BaSiH8 | 71.0 | 3.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| BaSiH8 | 71.0 | 3.0 | — | 0.10 | — | Eliashberg | 2021 | 2112.02131 |
| BaSiH8 | 71.0 | 5.0 | 1.61 | 0.10 | 33 | Eliashbergcheck | 2021 | 2112.02131 |
| BaSiH8 | 94.0 | 20.0 | — | — | — | DFT | 2024 | 2403.13496 |
| BaSiH8 | 92.0 | 30.0 | — | 0.10 | — | DFT | 2023 | 2310.00056 |
| BaSiH8 | 92.0 | 30.0 | — | 0.10 | — | Eliashberg | 2023 | 2310.00056 |
| BaSiH8 | 87.0 | 30.0 | — | 0.10 | — | DFT | 2023 | 2310.00056 |
| BaSiH8 | 87.0 | 30.0 | — | 0.10 | — | Eliashberg | 2023 | 2310.00056 |
| BaSiH8 | 9.0 | 142.0 | — | — | — | resistivity | 2026 | 2603.14051 |
| BaSiH8 | 100.0 | — | — | 0.10 | — | Eliashberg | 2022 | 2212.09789 |
Structure
- Crystal structure
- Fm-3m
- Space group
- Fm-3m
Superconducting parameters
- Hc2
- 13.0 T (0 K)
- λ_eph (e–ph coupling)
- —