Tc max
5.4 K
Tc ambient
5.4 K
arXiv year
2012
Papers
24
Tc exp.
5.4 K
Tc theo.
4.5 K
Evidence
experimental
Tc max measured at ambient, single_crystal, resistivity, arXiv:1207.5905, confirmed by 2 papers
Evidence (31 records from 24 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 6.2 | — | thin_film | STM | p-wave | 2016 | T1 | 1607.07551 |
| 5.4 | ambient | single_crystal | resistivity, susceptibility | — | 2012 | — | 1207.5905 |
| 5.3 | ambient | single_crystal | resistivity | — | 2012 | — | 1207.5905 |
| 5.2 | — | single_crystal | — | s-wave | 2025 | — | 2507.08740 |
| 5.2 | — | single_crystal | STM | s-wave | 2025 | T1 | DOI: 10.1103/75p3-2x2h |
| 5.2 | — | single_crystal | resistivity | s-wave | 2021 | T1 | DOI: 10.1103/PhysRevB.104.045406 |
| 5.0 | — | single_crystal | STM | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.184502 |
| 5.0 | — | single_crystal | specific_heat, resistivity, STM | s-wave | 2016 | T1 | DOI: 10.1103/PhysRevB.93.144502 |
| 5.0 | ambient | single_crystal | resistivity | s-wave | 2015 | T1 | 1506.01411 |
| 5.0 | — | single_crystal | resistivity, susceptibility, STM | s-wave | 2015 | T1 | DOI: 10.1103/PhysRevB.92.054507 |
| 5.0 | ambient | single_crystal | specific_heat | — | 2012 | — | 1207.5905 |
| 5.0 | ambient | single_crystal | resistivity, specific_heat | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.134505 |
| 4.9 | — | thin_film | resistivity | p-wave | 2025 | T1 | DOI: 10.1103/k7b8-6rp3 |
| 4.5 | — | single_crystal | — | s-wave | 2017 | T1 | DOI: 10.1103/PhysRevB.95.014512 |
| 4.5 | — | — | — | s-wave | 2017 | T1 | 1703.03012 |
| 4.4 | — | single_crystal | — | s-wave | 2017 | T1 | DOI: 10.1103/PhysRevB.95.014512 |
| 3.5 | — | thin_film | resistivity | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.L060504 |
| 3.4 | — | thin_film | resistivity | p-wave | 2024 | T1 | DOI: 10.1103/PhysRevLett.132.056001 |
| 3.1 | — | thin_film | resistivity | p-wave | 2025 | T1 | DOI: 10.1103/k7b8-6rp3 |
| 3.1 | — | thin_film | resistivity | p-wave | 2020 | — | 2003.00603 |
| 2.7 | — | thin_film | resistivity | p-wave | 2020 | — | 2003.00603 |
| 2.6 | — | thin_film | resistivity | p-wave | 2018 | T1 | 1810.11265 |
| 2.5 | — | thin_film | resistivity | p-wave | 2020 | — | 2003.00603 |
| 1.9 | ambient | thin_film | — | — | 2020 | T1 | DOI: 10.1103/PhysRevB.102.155406 |
| — | — | — | — | unknown | 2025 | T2 | 2509.24581 |
| — | — | single_crystal | STM | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.245403 |
| — | — | — | STM | — | 2021 | T3 | 2111.02473 |
| — | — | thin_film | ARPES | p-wave | 2019 | — | 1904.11638 |
| — | — | single_crystal | — | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.104527 |
| — | — | single_crystal | STM | s-wave | 2018 | T1 | DOI: 10.1103/PhysRevLett.120.167001 |
| — | ambient | single_crystal | specific_heat | s-wave | 2015 | T1 | 1506.01411 |
Structure
- Crystal structure
- tetragonal
- Space group
- I4/mmm
- Lattice a (Å)
- 3.360
- Lattice c (Å)
- 12.970
Superconducting parameters
- Gap structure
- full_gap
- Hc2
- 0.6 T (150 mK, H parallel c)
- λ_eph (e–ph coupling)
- 0.97
- ω_log
- 74 K
Competing orders
- ρ(T) exponent
- 2.00
Samples & pressure
- Sample form
- single_crystal
- Substrate
- MgO