Bi-2223

I4/mmm

ambient SCunconventional2D / interfacedisputed

Tc max

110.0 K

Tc ambient

110.0 K

Discovery

1995

Papers

Tc max measured at ambient, single_crystal, resistivity, arXiv:cond-mat/0205121, confirmed by 4 papers

Evidence (30 records from 25 papers)

the flat columns above are aggregates — each line here is one paper's claim

Tc (K)	P (GPa)	Sample	Method	Pairing	Year	Paper
120.0	ambient	—	—	—	1995	supr-con/9506003
110.0	ambient	single_crystal	resistivity	—	2004	cond-mat/0401448
110.0	ambient	—	—	—	2003	cond-mat/0306680
110.0	ambient	single_crystal	resistivity	—	2002	cond-mat/0205121
108.0	ambient	single_crystal	ARPES	d-wave	2003	cond-mat/0304505
108.0	ambient	single_crystal	susceptibility	—	2002	cond-mat/0205121
108.0	ambient	single_crystal	ARPES	d-wave	2001	cond-mat/0108386
108.0	ambient	single_crystal	ARPES, susceptibility	—	2001	cond-mat/0108415
107.0	ambient	single_crystal	resistivity	—	2002	cond-mat/0205341
105.0	ambient	single_crystal	—	—	2002	cond-mat/0211423
102.0	ambient	single_crystal	resistivity	—	2002	cond-mat/0205341
97.0	ambient	single_crystal	resistivity	—	2002	cond-mat/0205341
77.0	ambient	wire	—	—	2002	cond-mat/0202386
72.0	ambient	wire	susceptibility	—	2003	cond-mat/0308344
70.0	23.0	single_crystal	susceptibility	—	2026	2603.15102
70.0	11.0	single_crystal	susceptibility	—	2026	2603.15102
—	ambient	—	ARPES	d-wave	2004	cond-mat/0402304
—	ambient	single_crystal	—	—	2003	cond-mat/0307509
—	ambient	polycrystal	resistivity, susceptibility	—	2003	cond-mat/0308343
—	ambient	—	—	—	2003	cond-mat/0312219
—	ambient	—	ARPES	—	2002	cond-mat/0202083
—	ambient	wire	susceptibility	—	2002	cond-mat/0206229
—	ambient	—	resistivity	—	2002	cond-mat/0207511
—	ambient	wire	—	—	2002	cond-mat/0208333
—	ambient	thin_film	resistivity	—	2002	cond-mat/0209176
—	ambient	single_crystal	ARPES	—	2001	cond-mat/0110523
—	ambient	thin_film	resistivity	—	1999	cond-mat/9905098
—	ambient	wire	—	—	1999	cond-mat/9907271
—	ambient	polycrystal	resistivity	—	1998	cond-mat/9811269
—	ambient	—	neutron	—	1995	supr-con/9506003

Structure

Crystal structure: I4/mmm
Space group: I4/mmm
Lattice c (Å): 37.119

Superconducting parameters

Pairing symmetry: d-wave
Gap structure: nodal
λ_eph (e–ph coupling): —

Competing orders

ρ(T) exponent: 1.00

Samples & pressure

Substrate: NdGaO_3
Pressure type: none
Doping type: hole
Doping level: 0.185