Tc max
97.5 K
Tc ambient
—
arXiv year
2020
Papers
1
Tc exp.
—
Tc theo.
97.5 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=128 GPa, arXiv:2012.14985
Evidence (1 record from 1 paper)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 97.5 | 128.0 | — | — | — | 2020 | T1 | 2012.14985 |
Hydride Tc parameters (15)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| CaSH3 | 101.0 | 128.0 | 1.64 | 0.10 | 630 | Eliashberg | 2020 | 2012.14985 |
| CaSH3 | 100.0 | 128.0 | — | — | — | cited | 2023 | 2401.00088 |
| CaSH3 | 94.0 | 128.0 | 1.64 | 0.13 | 630 | Eliashberg | 2020 | 2012.14985 |
| CaSH3 | 78.0 | 128.0 | 1.64 | 0.10 | 630 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 71.0 | 128.0 | 1.64 | 0.13 | 630 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 91.0 | 140.0 | 1.18 | 0.10 | 861 | Eliashberg | 2020 | 2012.14985 |
| CaSH3 | 82.0 | 140.0 | 1.18 | 0.13 | 861 | Eliashberg | 2020 | 2012.14985 |
| CaSH3 | 75.0 | 140.0 | 1.18 | 0.10 | 861 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 66.0 | 140.0 | 1.18 | 0.13 | 861 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 54.0 | 200.0 | 0.82 | 0.10 | 1102 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 44.0 | 200.0 | 0.82 | 0.13 | 1102 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 46.0 | 250.0 | 0.74 | 0.10 | 1171 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 36.0 | 250.0 | 0.74 | 0.13 | 1171 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 42.0 | 300.0 | 0.70 | 0.10 | 1211 | Allen-Dynes | 2020 | 2012.14985 |
| CaSH3 | 32.0 | 300.0 | 0.70 | 0.13 | 1211 | Allen-Dynes | 2020 | 2012.14985 |
Structure
- Crystal structure
- P6̅m2
- Space group
- P6̅m2
Superconducting parameters
- λ_eph (e–ph coupling)
- —