Tc max
30.2 K
Tc ambient
30.2 K
arXiv year
2017
Papers
18
Tc exp.
30.2 K
Tc theo.
—
Evidence
experimental
Tc max measured at ambient, single_crystal, specific_heat, arXiv:1811.06379, confirmed by 3 papers
Evidence (26 records from 18 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 30.5 | ambient | single_crystal | resistivity | s-wave | 2019 | T1 | DOI: 10.1103/PhysRevB.99.144501 |
| 30.2 | — | single_crystal | specific_heat | unknown | 2019 | T1 | DOI: 10.1103/PhysRevB.99.020502 |
| 30.2 | ambient | single_crystal | specific_heat | — | 2018 | T3 | 1811.06379 |
| 30.0 | — | single_crystal | ARPES | unknown | 2026 | T1 | DOI: 10.1103/vy32-xtt9 |
| 29.8 | ambient | single_crystal | resistivity | s-wave | 2019 | T1 | DOI: 10.1103/PhysRevB.99.144501 |
| 29.4 | ambient | single_crystal | resistivity, susceptibility | s-wave | 2019 | T1 | DOI: 10.1103/PhysRevB.99.144501 |
| 29.4 | — | single_crystal | resistivity, susceptibility | s-wave | 2018 | T1 | 1811.05706 |
| 29.3 | — | single_crystal | resistivity | unknown | 2019 | T1 | DOI: 10.1103/PhysRevB.99.020502 |
| 29.3 | ambient | single_crystal | resistivity | — | 2018 | T3 | 1811.06379 |
| 29.2 | — | single_crystal | susceptibility | unknown | 2019 | T1 | DOI: 10.1103/PhysRevB.99.020502 |
| 29.2 | ambient | single_crystal | susceptibility | — | 2018 | T3 | 1811.06379 |
| 29.0 | — | single_crystal | resistivity | unknown | 2025 | T1 | DOI: 10.1103/PhysRevB.111.L081110 |
| 29.0 | — | — | — | — | 2024 | — | 2410.16610 |
| 29.0 | — | single_crystal | resistivity | s-wave | 2019 | — | 1903.06466 |
| 29.0 | — | single_crystal | resistivity, susceptibility | unknown | 2019 | T1 | DOI: 10.1103/PhysRevB.99.125119 |
| 28.9 | — | polycrystal | neutron | unknown | 2020 | T1 | 2004.03567 |
| 28.5 | — | single_crystal | resistivity | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.104512 |
| 28.3 | — | polycrystal | muSR | d-wave | 2018 | T1 | DOI: 10.1103/PhysRevB.97.060506 |
| 28.3 | — | polycrystal | muSR | s-wave | 2018 | T1 | DOI: 10.1103/PhysRevB.97.060506 |
| 28.3 | — | — | muSR | unknown | 2017 | T1 | 1712.04436 |
| 28.2 | — | polycrystal | resistivity, susceptibility | — | 2017 | T1 | 1704.01051 |
| 28.0 | — | polycrystal | susceptibility | — | 2018 | T1 | DOI: 10.1103/PhysRevB.97.060506 |
| 24.0 | — | thin_film | — | — | 2023 | — | 2311.14559 |
| — | — | single_crystal | STM | s_pm | 2026 | T2 | 2603.27217 |
| — | — | — | ARPES | — | 2026 | T1 | 2601.07380 |
| — | — | — | ARPES | — | 2024 | — | 2408.00469 |
Structure
- Space group
- I4/mmm
- Lattice c (Å)
- 32.363
Superconducting parameters
- Pairing symmetry
- s-wave
- Gap structure
- multi_gap
- Hc2
- 50.0 T (0 K, H perpendicular to ab plane)
- λ_eph (e–ph coupling)
- 0.23
Competing orders
- T_AFM
- 10.0 K
- ρ(T) exponent
- 1.50
Samples & pressure
- Sample form
- single_crystal
- Pressure type
- none
- Doping type
- hole
- Doping level
- 0.250