Tc max
183.0 K
Tc ambient
—
arXiv year
2015
Papers
8
Tc exp.
—
Tc theo.
183.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=200 GPa, arXiv:1502.02832, confirmed by 4 papers
Evidence (12 records from 8 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 183.0 | 200.0 | — | — | — | 2015 | — | 1502.02832 |
| 160.0 | — | — | — | — | 2026 | T2 | 2602.03576 |
| 159.0 | 150.0 | — | — | — | 2015 | T1 | 1511.05322 |
| 152.0 | 200.0 | — | — | — | 2015 | — | 1502.02832 |
| 147.0 | 150.0 | — | — | — | 2015 | T1 | 1511.05322 |
| 141.0 | 200.0 | — | — | — | 2015 | — | 1501.06336 |
| — | 160.0 | — | — | s-wave | 2025 | T1 | 2510.25902 |
| — | 200.0 | — | — | s-wave | 2025 | T1 | 2510.25902 |
| — | 162.0 | — | — | — | 2021 | T1 | 2103.12055 |
| — | 250.0 | — | — | — | 2021 | T1 | 2103.12055 |
| — | — | — | resistivity | — | 2017 | — | 1703.04034 |
| — | 173.0 | powder | resistivity | — | 2015 | T1 | 1509.03156 |
Hydride Tc parameters (41)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| D3S | 103.0 | 130.0 | — | — | — | DFT | 2015 | 1502.00936 |
| D3S | 159.0 | 150.0 | 2.06 | 0.09 | — | Eliashberg | 2015 | 1511.05322 |
| D3S | 147.0 | 150.0 | 2.06 | 0.13 | — | Eliashberg | 2015 | 1511.05322 |
| D3S | 119.0 | 150.0 | — | — | — | DFT | 2015 | 1502.00936 |
| D3S | 150.0 | 155.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.104.064510 |
| D3S | 168.0 | 160.0 | 1.94 | 0.16 | 952 | Eliashberg | 2025 | 2510.25902 |
| D3S | 165.0 | 160.0 | 1.94 | 0.16 | 952 | Eliashberg | 2025 | 2510.25902 |
| D3S | 164.5 | 160.0 | — | — | — | resistivity | 2025 | 2510.25902 |
| D3S | 159.0 | 160.0 | 1.94 | 0.16 | 952 | Eliashberg | 2025 | 2510.25902 |
| D3S | 151.0 | 160.0 | 1.94 | 0.16 | 952 | Eliashberg | 2025 | 2510.25902 |
| D3S | 163.0 | 170.0 | — | — | — | DFT | 2015 | 1502.00936 |
| D3S | 150.0 | 170.0 | — | — | — | resistivity | 2016 | 1607.02348 |
| D3S | 154.0 | 172.0 | — | — | — | DFT | 2021 | 2103.12055 |
| D3S | 150.4 | 180.0 | 2.48 | — | 730 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 149.1 | 185.0 | 2.22 | — | 827 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 146.5 | 195.0 | 1.91 | — | 740 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 183.0 | 200.0 | 2.64 | 0.16 | 795 | Eliashberg | 2015 | 1502.02832 |
| D3S | 180.0 | 200.0 | 2.29 | 0.16 | 917 | Eliashberg | 2025 | 2510.25902 |
| D3S | 174.0 | 200.0 | 2.29 | 0.16 | 917 | Eliashberg | 2025 | 2510.25902 |
| D3S | 170.0 | 200.0 | 2.20 | 0.15 | — | Allen-Dynes | 2015 | 1501.03950 |
| D3S | 170.0 | 200.0 | — | — | — | Allen-Dynes | 2015 | DOI: 10.1103/PhysRevB.91.184511 |
| D3S | 166.0 | 200.0 | 2.29 | 0.16 | 917 | Eliashberg | 2025 | 2510.25902 |
| D3S | 160.0 | 200.0 | — | — | — | DFT | 2016 | 1607.02348 |
| D3S | 157.0 | 200.0 | 2.29 | 0.16 | 917 | Eliashberg | 2025 | 2510.25902 |
| D3S | 152.0 | 200.0 | 1.78 | 0.16 | 986 | Eliashberg | 2025 | 2510.25902 |
| D3S | 152.0 | 200.0 | 1.87 | 0.16 | 851 | Eliashberg | 2015 | 1502.02832 |
| D3S | 150.0 | 200.0 | 1.78 | 0.16 | 986 | Eliashberg | 2025 | 2510.25902 |
| D3S | 145.4 | 200.0 | 1.81 | — | 967 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 144.0 | 200.0 | — | — | — | resistivity | 2025 | 2510.25902 |
| D3S | 143.0 | 200.0 | 1.78 | 0.16 | 986 | Eliashberg | 2025 | 2510.25902 |
| D3S | 141.0 | 200.0 | 2.41 | — | 952 | DFT | 2015 | 1501.06336 |
| D3S | 132.0 | 200.0 | 1.78 | 0.16 | 986 | Eliashberg | 2025 | 2510.25902 |
| D3S | 90.0 | 200.0 | — | — | — | resistivity | 2015 | 1502.02832 |
| D3S | 90.0 | 200.0 | — | — | — | resistivity | 2015 | 1501.06336 |
| D3S | 144.1 | 205.0 | 1.73 | — | 987 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 206.0 | 210.0 | — | — | — | DFT | 2015 | 1502.00936 |
| D3S | 142.9 | 210.0 | 1.66 | — | 1026 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 141.6 | 215.0 | 1.59 | — | 1053 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 140.4 | 220.0 | 1.54 | — | 1090 | Eliashberg | 2026 | DOI: 10.1103/dyxf-5mdl |
| D3S | 180.0 | 230.0 | — | — | — | DFT | 2015 | 1502.00936 |
| D3S | 164.0 | 250.0 | — | — | — | DFT | 2015 | 1502.00936 |
Structure
- Crystal structure
- body-centered cubic
- Space group
- Im-3m (#204)
Superconducting parameters
- λ_eph (e–ph coupling)
- 2.64
- ω_log
- 1192 K