Tc max
15.3 K
Tc ambient
15.3 K
arXiv year
2009
Papers
18
Tc exp.
15.3 K
Tc theo.
—
Evidence
experimental
Tc max measured at single_crystal, resistivity, DOI: 10.1103/PhysRevB.108.214509, confirmed by 2 papers
Evidence (23 records from 18 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 16.0 | — | thin_film | resistivity | — | 2016 | T1 | 1608.01170 |
| 15.4 | — | thin_film | resistivity | — | 2016 | T1 | 1608.01170 |
| 15.3 | — | single_crystal | resistivity | s-wave | 2023 | T1 | DOI: 10.1103/PhysRevB.108.214509 |
| 14.6 | — | single_crystal | susceptibility, resistivity | — | 2014 | — | 1406.7383 |
| 14.5 | — | single_crystal | susceptibility | — | 2018 | T1 | 1812.08995 |
| 14.3 | — | — | specific_heat | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.100501 |
| 14.3 | — | single_crystal | resistivity | s-wave | 2023 | T1 | DOI: 10.1103/PhysRevB.108.214509 |
| 14.1 | — | single_crystal | susceptibility | s-wave | 2023 | T1 | DOI: 10.1103/PhysRevB.108.214509 |
| 14.0 | — | single_crystal | susceptibility | s-wave | 2023 | T1 | DOI: 10.1103/PhysRevB.108.214509 |
| 14.0 | — | single_crystal | neutron | — | 2014 | T1 | DOI: 10.1103/PhysRevB.90.100501 |
| 14.0 | — | single_crystal | STM | s-wave | 2013 | T1 | DOI: 10.1103/PhysRevB.88.155124 |
| 14.0 | — | single_crystal | STM | anisotropic s-wave | 2013 | T1 | 1308.4339 |
| 14.0 | — | single_crystal | neutron | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.024518 |
| 14.0 | — | single_crystal | susceptibility | unknown | 2011 | T1 | DOI: 10.1103/PhysRevB.84.132503 |
| 14.0 | — | — | neutron | — | 2011 | T1 | 1105.4923 |
| 14.0 | — | single_crystal | susceptibility, resistivity | s_pm | 2011 | T1 | 1106.1485 |
| 14.0 | — | single_crystal | susceptibility, resistivity | s_pm | 2011 | T1 | 1107.0095 |
| 14.0 | — | single_crystal | neutron | — | 2010 | T1 | 1001.1505 |
| 14.0 | — | single_crystal | neutron, resistivity, susceptibility, specific_heat | s_pm | 2009 | T1 | DOI: 10.1103/PhysRevLett.103.067008 |
| 14.0 | — | single_crystal | neutron | s_pm | 2009 | T1 | 0905.3559 |
| — | — | single_crystal | resistivity | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.219901 |
| — | — | single_crystal | STM | — | 2020 | T1 | 2002.10004 |
| — | — | single_crystal | resistivity | — | 2010 | — | 1004.1038 |
Structure
- Crystal structure
- tetragonal
- Space group
- P4/nmm
- Lattice a (Å)
- 3.786
- Lattice c (Å)
- 6.061
Superconducting parameters
- λ_eph (e–ph coupling)
- —
Competing orders
- ρ(T) exponent
- 2.00
Samples & pressure
- Sample form
- single_crystal
- Substrate
- CaF2
- Doping level
- 0.300