Tc max
28.0 K
Tc ambient
11.4 K
arXiv year
2008
Papers
5
Tc exp.
28.0 K
Tc theo.
—
Evidence
experimental
Tc max measured at P=6.4 GPa, resistivity, arXiv:1210.3645, confirmed by 2 papers
Evidence (11 records from 5 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 37.0 | 4.2 | polycrystal | resistivity | — | 2009 | T1 | 0903.2594 |
| 28.0 | 6.4 | — | resistivity | — | 2012 | — | 1210.3645 |
| 21.0 | 3.6 | polycrystal | resistivity | — | 2009 | T1 | 0903.2594 |
| 11.4 | — | thin_film | resistivity | — | 2010 | T1 | 1005.0192 |
| 8.4 | — | polycrystal | susceptibility | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.024517 |
| 8.3 | — | thin_film | resistivity | — | 2010 | T1 | 1005.0192 |
| 8.0 | — | polycrystal | resistivity | — | 2008 | T1 | 0808.0040 |
| 7.0 | — | polycrystal | susceptibility | — | 2008 | T1 | 0808.0040 |
| 6.0 | — | polycrystal | NMR | — | 2008 | T1 | 0808.0040 |
| — | — | thin_film | susceptibility | — | 2010 | T1 | 1005.0192 |
| — | — | polycrystal | NMR | — | 2008 | T1 | 0808.0040 |
Structure
- Crystal structure
- P4/nmm
- Space group
- P4/nmm (#129)
- Lattice a (Å)
- 3.769
- Lattice c (Å)
- 5.490
Superconducting parameters
- Hc2
- 56.0 T (H=7 T)
- λ_eph (e–ph coupling)
- —
Competing orders
- T_SDW
- 120.0 K
Samples & pressure
- Sample form
- polycrystal
- Substrate
- SrTiO3