Tc max
17.7 K
Tc ambient
17.0 K
arXiv year
2009
Papers
18
Tc exp.
17.7 K
Tc theo.
—
Evidence
experimental
Tc max measured at thin_film, resistivity, arXiv:1111.3923, confirmed by 2 papers
Evidence (21 records from 18 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 23.0 | — | thin_film | resistivity | — | 2015 | — | 1502.00758 |
| 17.7 | — | thin_film | resistivity | — | 2011 | — | 1111.3923 |
| 17.0 | — | thin_film | — | — | 2015 | T1 | 1512.02524 |
| 15.0 | ambient | single_crystal | specific_heat | — | 2014 | T1 | 1407.8266 |
| 14.0 | ambient | single_crystal | resistivity | — | 2023 | T1 | DOI: 10.1103/PhysRevX.13.011032 |
| 14.0 | — | single_crystal | resistivity | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.224516 |
| 13.0 | — | polycrystal | resistivity, susceptibility | — | 2009 | T1 | 0904.3851 |
| 6.7 | — | thin_film | resistivity | — | 2009 | T1 | 0908.1316 |
| 5.6 | — | single_crystal | resistivity | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.224516 |
| 5.5 | — | thin_film | resistivity | — | 2009 | T1 | 0908.1316 |
| 2.6 | — | thin_film | resistivity | — | 2009 | T1 | 0908.1316 |
| — | — | thin_film | susceptibility | unknown | 2025 | T1 | 2505.16184 |
| — | — | — | resistivity, susceptibility | — | 2024 | T1 | 2402.18082 |
| — | — | single_crystal | resistivity | — | 2024 | — | 2412.16171 |
| — | — | thin_film | resistivity | — | 2023 | T2 | 2312.11155 |
| — | — | thin_film | resistivity | — | 2021 | T1 | DOI: 10.1103/PhysRevB.104.014505 |
| — | — | — | resistivity | — | 2021 | T1 | 2103.08865 |
| — | — | thin_film | susceptibility | — | 2021 | T1 | 2103.17031 |
| — | — | single_crystal | specific_heat | s-wave | 2011 | T1 | 1110.5445 |
| — | — | thin_film | resistivity | — | 2011 | — | 1108.5194 |
| — | — | single_crystal | resistivity, specific_heat | — | 2010 | T1 | 1003.3812 |
Superconducting parameters
- λ_eph (e–ph coupling)
- —
Competing orders
- ρ(T) exponent
- 1.00
Samples & pressure
- Substrate
- CaF2
- Pressure type
- none
- Doping type
- isovalent