Tc max
14.1 K
Tc ambient
14.0 K
arXiv year
2009
Papers
12
Tc exp.
14.1 K
Tc theo.
—
Evidence
experimental
Tc max measured at single_crystal, susceptibility, arXiv:2211.05355, confirmed by 2 papers
Evidence (14 records from 12 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 14.5 | — | single_crystal | susceptibility | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.205117 |
| 14.1 | — | single_crystal | susceptibility | — | 2022 | T1 | 2211.05355 |
| 14.0 | — | single_crystal | susceptibility | — | 2023 | T1 | DOI: 10.1103/PhysRevLett.130.046702 |
| 14.0 | — | single_crystal | susceptibility, resistivity | — | 2015 | T1 | 1502.04284 |
| 14.0 | — | single_crystal | susceptibility | — | 2014 | T1 | 1404.1412 |
| 13.7 | — | single_crystal | susceptibility | — | 2019 | T1 | 1904.13020 |
| 13.3 | — | thin_film | resistivity | — | 2014 | T1 | 1412.4667 |
| 13.0 | — | thin_film | resistivity | — | 2025 | T1 | 2509.13969 |
| 13.0 | — | single_crystal | — | — | 2014 | T1 | 1405.1172 |
| 13.0 | — | single_crystal | ARPES | — | 2014 | T1 | DOI: 10.1103/PhysRevB.89.140506 |
| 13.0 | — | single_crystal | susceptibility | — | 2009 | T1 | DOI: 10.1103/PhysRevB.80.104506 |
| 12.9 | — | thin_film | — | — | 2014 | T1 | 1412.4667 |
| 12.3 | — | thin_film | resistivity | — | 2014 | T1 | 1412.4667 |
| — | — | thin_film | resistivity | — | 2024 | — | 2410.12624 |
Structure
- Crystal structure
- P4/nmm
- Space group
- P4/nmm
- Lattice a (Å)
- 3.800
- Lattice c (Å)
- 6.100
Superconducting parameters
- λ_eph (e–ph coupling)
- —
Competing orders
- ρ(T) exponent
- 1.00
Samples & pressure
- Sample form
- single_crystal
- Substrate
- CaF2
- Doping level
- 0.300