Tc max
225.0 K
Tc ambient
—
arXiv year
2021
Papers
1
Tc exp.
—
Tc theo.
225.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=200 GPa, arXiv:2108.09437
Evidence (4 records from 1 paper)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 225.0 | 200.0 | — | — | — | 2021 | T1 | 2108.09437 |
| 205.0 | 250.0 | — | — | — | 2021 | T1 | 2108.09437 |
| 199.0 | 200.0 | — | — | — | 2021 | T1 | 2108.09437 |
| 179.0 | 250.0 | — | — | — | 2021 | T1 | 2108.09437 |
Hydride Tc parameters (6)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| H24S7Si | 217.5 | 200.0 | 1.99 | 0.12 | 1155 | Eliashberg | 2021 | DOI: 10.1103/PhysRevResearch.3.043102 |
| H24S7Si | 217.5 | 200.0 | 1.99 | 0.12 | 1155 | Eliashberg | 2021 | 2108.09437 |
| H24S7Si | 190.5 | 200.0 | 1.99 | 0.12 | 1155 | Allen-Dynes | 2021 | 2108.09437 |
| H24S7Si | 196.5 | 250.0 | 1.59 | 0.12 | 1294 | Eliashberg | 2021 | DOI: 10.1103/PhysRevResearch.3.043102 |
| H24S7Si | 196.5 | 250.0 | 1.59 | 0.12 | 1294 | Eliashberg | 2021 | 2108.09437 |
| H24S7Si | 170.0 | 250.0 | 1.59 | 0.12 | 1294 | Allen-Dynes | 2021 | 2108.09437 |
Superconducting parameters
- λ_eph (e–ph coupling)
- 1.99
- ω_log
- 1294 K
Samples & pressure
- Doping level
- 0.125