Tc max
190.0 K
Tc ambient
—
arXiv year
2014
Papers
12
Tc exp.
190.0 K
Tc theo.
250.0 K
Evidence
theoretical
Tc max measured at P=150 GPa, resistivity, arXiv:1412.0460
Evidence (14 records from 12 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 250.0 | — | — | — | — | 2018 | — | 1801.03438 |
| 250.0 | — | — | — | — | 2016 | T1 | 1603.02879 |
| 250.0 | — | — | — | — | 2016 | T1 | DOI: 10.1103/PhysRevB.93.184510 |
| 190.0 | 150.0 | — | resistivity | — | 2014 | T1 | 1412.0460 |
| 150.0 | — | — | — | — | 2018 | T1 | 1802.07506 |
| 150.0 | 200.0 | — | resistivity | — | 2014 | T1 | 1412.0460 |
| 92.0 | — | — | — | — | 2018 | T1 | 1802.07506 |
| 88.0 | 180.0 | — | — | — | 2014 | — | 1412.8640 |
| 80.0 | 160.0 | — | — | — | 2014 | T1 | 1402.2721 |
| 50.0 | 130.0 | — | — | — | 2015 | T1 | DOI: 10.1103/PhysRevB.91.224513 |
| 50.0 | — | — | — | — | 2015 | — | 1502.00936 |
| 34.0 | 140.0 | — | — | — | 2016 | T1 | DOI: 10.1103/PhysRevB.93.094525 |
| 34.0 | 140.0 | — | — | — | 2015 | T1 | 1512.07365 |
| — | 225.0 | — | — | — | 2016 | T3 | 1607.02162 |
Hydride Tc parameters (55)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| H2S | 203.0 | 90.0 | — | — | — | resistivity | 2018 | 1807.05049 |
| H2S | 203.0 | 90.0 | — | — | — | cited | 2016 | DOI: 10.1103/PhysRevB.93.094522 |
| H2S | 203.0 | 90.0 | — | — | — | cited | 2015 | 1512.01245 |
| H2S | 80.0 | 90.0 | — | — | — | resistivity | 2015 | 1506.08190 |
| H2S | 150.0 | 100.0 | — | — | — | resistivity | 2015 | 1512.06680 |
| H2S | 20.0 | 100.0 | — | — | — | resistivity | 2014 | 1412.6251 |
| H2S | 200.0 | 110.0 | — | — | — | resistivity | 2016 | 1602.02686 |
| H2S | 30.0 | 110.0 | — | — | — | resistivity | 2015 | 1508.03900 |
| H2S | 50.0 | 130.0 | — | 0.15 | — | DFT | 2015 | DOI: 10.1103/PhysRevB.91.224513 |
| H2S | 29.4 | 130.0 | 0.80 | 0.15 | 913 | DFT | 2015 | 1502.00936 |
| H2S | 66.0 | 140.0 | — | — | — | Eliashberg | 2015 | 1512.07365 |
| H2S | 63.0 | 140.0 | — | — | — | Eliashberg | 2015 | 1512.07365 |
| H2S | 56.0 | 140.0 | — | — | — | Eliashberg | 2015 | 1512.07365 |
| H2S | 44.0 | 140.0 | 0.73 | — | — | Eliashberg | 2015 | 1512.07365 |
| H2S | 40.0 | 140.0 | 1.10 | 0.12 | 1000 | Allen-Dynescheck | 2015 | DOI: 10.1103/PhysRevB.91.184511 |
| H2S | 40.0 | 140.0 | 1.10 | 0.12 | 1000 | DFTcheck | 2015 | 1501.03950 |
| H2S | 34.0 | 140.0 | — | — | — | Eliashberg | 2016 | DOI: 10.1103/PhysRevB.93.094525 |
| H2S | 34.0 | 140.0 | 0.64 | — | 1034 | Eliashberg | 2015 | 1512.07365 |
| H2S | 200.0 | 150.0 | — | — | — | DFT | 2025 | DOI: 10.1103/sn9r-3cx2 |
| H2S | 190.0 | 150.0 | — | — | — | resistivity | 2014 | 1412.6251 |
| H2S | 150.0 | 150.0 | — | — | — | cited | 2020 | 1905.12308 |
| H2S | 133.0 | 150.0 | — | — | — | cited | 2017 | 1704.02228 |
| H2S | 80.0 | 150.0 | — | — | — | DFT | 2017 | DOI: 10.1103/PhysRevB.95.020104 |
| H2S | 47.1 | 150.0 | 1.00 | 0.17 | 914 | DFT | 2015 | 1502.00936 |
| H2S | 203.0 | 153.0 | — | — | — | resistivity | 2018 | DOI: 10.1103/PhysRevB.98.174101 |
| H2S | 203.0 | 155.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| H2S | 203.0 | 155.0 | — | — | — | resistivity | 2017 | 1701.04004 |
| H2S | 203.0 | 155.0 | — | — | — | resistivity | 2016 | 1609.03670 |
| H2S | 203.0 | 155.0 | — | — | — | resistivity | 2015 | 1508.03900 |
| H2S | 59.5 | 155.0 | — | 0.15 | — | Eliashberg | 2014 | 1412.8640 |
| H2S | 205.0 | 160.0 | — | — | — | resistivity | 2015 | 1507.03921 |
| H2S | 80.0 | 160.0 | 1.10 | 0.12 | 1000 | DFT | 2015 | 1501.03950 |
| H2S | 80.0 | 160.0 | — | — | — | Allen-Dynes | 2015 | DOI: 10.1103/PhysRevB.92.205125 |
| H2S | 80.0 | 160.0 | 1.10 | 0.12 | 1000 | Allen-Dynes | 2015 | DOI: 10.1103/PhysRevB.91.184511 |
| H2S | 80.0 | 160.0 | — | — | — | Allen-Dynes | 2015 | 1509.01297 |
| H2S | 80.0 | 160.0 | — | — | — | DFT | 2015 | 1509.05455 |
| H2S | 80.0 | 160.0 | — | — | — | DFT | 2014 | 1402.2721 |
| H2S | 80.0 | 160.0 | 1.28 | — | 960 | Eliashberg | 2014 | 1412.8640 |
| H2S | 66.9 | 170.0 | 1.20 | 0.17 | 968 | DFT | 2015 | 1502.00936 |
| H2S | 190.0 | 190.0 | — | — | — | resistivity | 2015 | 1507.03921 |
| H2S | 56.3 | 190.0 | 1.03 | 0.17 | 1044 | DFT | 2015 | 1502.00936 |
| H2S | 203.0 | 200.0 | — | — | — | cited | 2016 | 1608.08587 |
| H2S | 197.5 | 200.0 | — | — | — | cited | 2023 | 2301.09032 |
| H2S | 190.0 | 200.0 | — | — | — | resistivity | 2015 | DOI: 10.1103/PhysRevLett.114.157004 |
| H2S | 190.0 | 200.0 | — | — | — | resistivity | 2014 | 1501.00196 |
| H2S | 150.0 | 200.0 | — | — | — | cited | 2015 | 1510.04415 |
| H2S | 150.0 | 200.0 | — | — | — | resistivity | 2015 | 1508.03900 |
| H2S | 150.0 | 200.0 | — | — | — | resistivity | 2014 | 1412.6251 |
| H2S | 55.4 | 210.0 | 0.94 | 0.15 | 1097 | DFT | 2015 | 1502.00936 |
| H2S | 45.4 | 230.0 | 0.88 | 0.16 | 1121 | DFT | 2015 | 1502.00936 |
| H2S | 41.8 | 250.0 | 0.85 | 0.16 | 1124 | DFT | 2015 | 1502.00936 |
| H2S | 203.0 | — | 2.00 | — | 1200 | Eliashberg | 2016 | DOI: 10.1103/PhysRevB.93.184510 |
| H2S | 190.0 | — | — | 0.13 | — | resistivity | 2015 | DOI: 10.1103/PhysRevB.91.224513 |
| H2S | 92.0 | — | — | — | 255 | BCS | 2018 | 1802.07506 |
| H2S | 82.0 | — | — | 0.15 | — | Eliashberg | 2018 | 1804.09760 |
Structure
- Crystal structure
- P1̅
- Space group
- P1̅
Superconducting parameters
- λ_eph (e–ph coupling)
- 1.28
- ω_log
- 1034 K
Samples & pressure
- Pressure type
- hydrostatic