Tc max
160.0 K
Tc ambient
—
arXiv year
2015
Papers
6
Tc exp.
—
Tc theo.
160.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=200 GPa, DOI: 10.1103/PhysRevB.93.224513, confirmed by 2 papers
Evidence (6 records from 6 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 200.0 | 64.0 | — | — | — | 2024 | T2 | 2408.10625 |
| 160.0 | 200.0 | — | — | — | 2016 | T1 | DOI: 10.1103/PhysRevB.93.224513 |
| 100.0 | — | — | — | — | 2019 | — | 1903.03255 |
| 100.0 | 190.0 | — | — | — | 2015 | T1 | 1507.02522 |
| 100.0 | — | — | — | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.060508 |
| 75.0 | 120.0 | — | — | — | 2015 | T1 | 1502.02607 |
Hydride Tc parameters (22)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| H3Se | 200.0 | 64.0 | 4.10 | 0.10 | — | Eliashberg | 2024 | 2408.10625 |
| H3Se | 115.0 | 110.0 | — | — | — | DFT | 2022 | DOI: 10.1103/PhysRevB.105.L180508 |
| H3Se | 110.0 | 120.0 | — | — | — | cited | 2025 | DOI: 10.1103/2l5v-x76p |
| H3Se | 75.0 | 120.0 | — | — | — | DFT | 2015 | 1502.02607 |
| H3Se | 130.0 | 125.0 | — | — | — | Allen-Dynes | 2024 | 2408.10625 |
| H3Se | 121.0 | 175.0 | — | — | 1338 | Allen-Dynes | 2024 | 2408.10625 |
| H3Se | 113.0 | 175.0 | — | — | 1239 | Allen-Dynes | 2024 | 2408.10625 |
| H3Se | 100.0 | 190.0 | — | — | — | DFT | 2024 | 2408.10625 |
| H3Se | 100.0 | 190.0 | 1.35 | 0.10 | 975 | DFT | 2015 | 1507.02522 |
| H3Se | 163.0 | 200.0 | — | — | — | DFT | 2024 | 2408.10625 |
| H3Se | 160.0 | 200.0 | — | 0.12 | — | DFT | 2016 | DOI: 10.1103/PhysRevB.93.224513 |
| H3Se | 160.0 | 200.0 | — | 0.12 | — | DFT | 2015 | 1507.08525 |
| H3Se | 131.0 | 200.0 | — | — | — | DFT | 2019 | 1911.09293 |
| H3Se | 131.0 | 200.0 | — | — | — | DFT | 2018 | 1806.00163 |
| H3Se | 130.0 | 200.0 | — | — | — | DFT | 2024 | 2408.10625 |
| H3Se | 118.0 | 200.0 | 1.13 | 0.10 | 353 | Allen-Dynescheck | 2019 | 1903.03255 |
| H3Se | 116.0 | 200.0 | — | — | — | DFT | 2025 | 2507.06749 |
| H3Se | 114.0 | 200.0 | — | — | — | DFT | 2024 | 2408.10625 |
| H3Se | 113.6 | 200.0 | — | 0.10 | — | Allen-Dynes | 2024 | 2408.10625 |
| H3Se | 113.6 | 200.0 | — | 0.10 | 1250 | Allen-Dynes | 2024 | 2408.10625 |
| H3Se | 113.6 | 200.0 | — | 0.10 | 1250 | Allen-Dynes | 2024 | 2408.10625 |
| H3Se | 100.0 | 200.0 | 1.35 | 0.10 | 975 | DFT | 2015 | DOI: 10.1103/PhysRevB.92.060508 |
Structure
- Crystal structure
- bcc
- Space group
- Im-3m
Superconducting parameters
- λ_eph (e–ph coupling)
- 4.10
- ω_log
- 975 K