Tc max
138.0 K
Tc ambient
138.0 K
arXiv year
1994
Papers
59
Tc exp.
164.0 K
Tc theo.
163.0 K
Evidence
experimental
Tc max measured at P=31 GPa, polycrystal, resistivity, DOI: 10.1103/PhysRevB.50.4260, confirmed by 2 papers
Evidence (88 records from 59 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 166.0 | 23.0 | polycrystal | resistivity | — | 2004 | T2 | cond-mat/0409662 |
| 164.0 | 31.0 | polycrystal | resistivity | — | 1994 | T1 | DOI: 10.1103/PhysRevB.50.4260 |
| 163.0 | — | — | — | — | 2001 | T3 | cond-mat/0104050 |
| 151.0 | ambient | polycrystal | resistivity, susceptibility | — | 2026 | T1 | DOI: 10.1103/Physics.19.37 |
| 151.0 | ambient | — | — | — | 2026 | T1 | 2603.12437 |
| 146.0 | 30.0 | polycrystal | — | — | 1996 | T1 | DOI: 10.1103/PhysRevB.54.4265 |
| 140.0 | 4.0 | single_crystal | susceptibility | — | 2025 | T1 | DOI: 10.1103/PhysRevApplied.23.064067 |
| 138.0 | 4.0 | — | susceptibility | — | 2026 | T1 | 2601.10838 |
| 135.0 | — | — | — | — | 2004 | T3 | cond-mat/0406142 |
| 135.0 | — | powder | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.15407 |
| 135.0 | — | polycrystal | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.581 |
| 135.0 | ambient | polycrystal | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.52.3756 |
| 134.5 | — | powder | susceptibility | d-wave | 1997 | T1 | DOI: 10.1103/PhysRevLett.79.2320 |
| 134.5 | — | polycrystal | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.3783 |
| 134.0 | ambient | single_crystal | STM | — | 2024 | — | 2401.17079 |
| 134.0 | — | polycrystal | susceptibility | — | 2019 | T1 | 1903.01526 |
| 134.0 | ambient | polycrystal | — | — | 2017 | T1 | DOI: 10.1103/PhysRevLett.119.057001 |
| 134.0 | — | polycrystal | susceptibility | — | 2012 | T1 | DOI: 10.1103/PhysRevB.85.054501 |
| 134.0 | — | polycrystal | resistivity, susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.1330 |
| 134.0 | — | polycrystal | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.581 |
| 134.0 | ambient | polycrystal | resistivity, susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.644 |
| 133.5 | — | polycrystal | susceptibility | — | 1996 | T1 | DOI: 10.1103/PhysRevB.54.7505 |
| 133.5 | — | polycrystal | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.11767 |
| 133.0 | — | single_crystal | ARPES | d-wave | 2026 | T2 | 2602.05624 |
| 133.0 | — | single_crystal | susceptibility | — | 2025 | — | 2502.10737 |
| 133.0 | — | single_crystal | susceptibility | — | 2020 | T1 | 2003.08957 |
| 133.0 | — | polycrystal | susceptibility | — | 2019 | T1 | 1902.05232 |
| 133.0 | ambient | single_crystal | — | — | 2018 | — | 1808.00228 |
| 133.0 | — | — | — | — | 2018 | — | 1808.08198 |
| 133.0 | — | — | — | — | 2011 | T1 | 1106.6163 |
| 133.0 | — | polycrystal | susceptibility | — | 2001 | T1 | DOI: 10.1103/PhysRevB.64.064515 |
| 133.0 | — | single_crystal | susceptibility | d-wave | 1998 | T1 | cond-mat/9804060 |
| 133.0 | — | polycrystal | susceptibility | d-wave | 1996 | T1 | DOI: 10.1103/PhysRevB.53.R8906 |
| 132.0 | ambient | single_crystal | susceptibility | d-wave | 2021 | T1 | 2102.13432 |
| 132.0 | ambient | single_crystal | susceptibility | — | 2021 | T1 | DOI: 10.1103/PhysRevB.103.195130 |
| 132.0 | ambient | thin_film | resistivity | — | 1999 | T1 | cond-mat/9905201 |
| 132.0 | — | thin_film | resistivity | — | 1999 | T2 | cond-mat/9904385 |
| 132.0 | — | polycrystal | susceptibility | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.14790 |
| 132.0 | — | polycrystal | resistivity, susceptibility | — | 1994 | T1 | DOI: 10.1103/PhysRevB.49.15416 |
| 131.6 | — | — | — | — | 2011 | T1 | 1106.6163 |
| 131.0 | — | polycrystal | susceptibility | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.14790 |
| 130.0 | — | — | — | — | 2011 | T1 | 1106.6163 |
| 130.0 | — | single_crystal | — | — | 1999 | T2 | cond-mat/9912338 |
| 129.0 | — | single_crystal | susceptibility | — | 2026 | — | 2605.05800 |
| 128.7 | — | — | — | — | 2011 | T1 | 1106.6163 |
| 128.5 | — | thin_film | susceptibility | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.862 |
| 127.0 | — | single_crystal | susceptibility | — | 2020 | T1 | 2003.08957 |
| 126.0 | — | single_crystal | susceptibility | d-wave | 2000 | T1 | DOI: 10.1103/PhysRevB.61.7122 |
| 126.0 | — | single_crystal | susceptibility | d-wave | 1998 | T1 | cond-mat/9804060 |
| 125.0 | — | single_crystal | — | unknown | 2003 | T1 | cond-mat/0311579 |
| 124.0 | — | polycrystal | susceptibility | — | 2019 | T1 | 1903.01526 |
| 123.6 | — | thin_film | resistivity | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.862 |
| 122.0 | — | single_crystal | — | d-wave | 2016 | T1 | DOI: 10.1103/PhysRevLett.116.197001 |
| 122.0 | — | single_crystal | — | — | 2016 | T1 | 1602.00123 |
| 122.0 | — | single_crystal | susceptibility | — | 2015 | T2 | 1508.06497 |
| 122.0 | — | single_crystal | resistivity | — | 2002 | T1 | DOI: 10.1103/PhysRevB.65.132501 |
| 121.5 | — | thin_film | — | — | 2003 | T1 | cond-mat/0305059 |
| 121.0 | — | single_crystal | susceptibility | d-wave | 2000 | T1 | DOI: 10.1103/PhysRevB.61.7122 |
| 121.0 | — | single_crystal | — | — | 1999 | T2 | cond-mat/9912338 |
| 120.0 | — | single_crystal | susceptibility, STM | d-wave | 2024 | T1 | DOI: 10.1103/PhysRevB.109.085132 |
| 118.0 | — | polycrystal | susceptibility | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.14790 |
| 117.0 | — | single_crystal | susceptibility | — | 2020 | T1 | 2003.08957 |
| 117.0 | — | single_crystal | resistivity | — | 2020 | T1 | DOI: 10.1103/PhysRevB.101.214520 |
| 117.0 | — | — | — | — | 2018 | — | 1808.08198 |
| 117.0 | — | single_crystal | susceptibility | — | 2015 | T2 | 1508.06497 |
| 115.0 | — | polycrystal | susceptibility | — | 2001 | T1 | DOI: 10.1103/PhysRevB.64.064515 |
| 114.0 | — | — | — | — | 2024 | T1 | 2401.15224 |
| 112.0 | — | single_crystal | susceptibility | d-wave | 2025 | T1 | DOI: 10.1103/1gp5-h875 |
| 110.0 | — | single_crystal | susceptibility | — | 2020 | T1 | 2003.08957 |
| 108.0 | — | — | — | — | 2024 | T1 | 2401.15224 |
| 107.0 | — | polycrystal | susceptibility | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.14790 |
| 107.0 | — | powder | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.15407 |
| 105.0 | — | single_crystal | susceptibility | — | 2020 | T1 | 2003.08957 |
| 97.0 | — | polycrystal | susceptibility | — | 1997 | T1 | DOI: 10.1103/PhysRevB.56.14790 |
| 96.0 | — | — | — | — | 2024 | T1 | 2401.15224 |
| 95.0 | — | single_crystal | susceptibility | d-wave | 2025 | T1 | DOI: 10.1103/1gp5-h875 |
| 95.0 | — | — | — | — | 2024 | T1 | 2401.15224 |
| 94.0 | — | powder | susceptibility | — | 1995 | T1 | DOI: 10.1103/PhysRevB.51.15407 |
| 92.0 | — | single_crystal | susceptibility | — | 2020 | T1 | 2003.08957 |
| 78.0 | — | single_crystal | susceptibility | d-wave | 2025 | T1 | DOI: 10.1103/1gp5-h875 |
| 74.0 | — | single_crystal | susceptibility | — | 2021 | T1 | 2111.03589 |
| 64.0 | — | single_crystal | susceptibility | — | 2021 | T1 | 2111.03589 |
| — | — | single_crystal | susceptibility | d-wave | 1999 | T1 | cond-mat/9909267 |
| — | — | polycrystal | thermal_conductivity | — | 1999 | T1 | DOI: 10.1103/PhysRevB.59.3823 |
| — | — | polycrystal | resistivity | — | 1999 | T2 | cond-mat/9904116 |
| — | — | single_crystal | — | — | 1998 | T1 | DOI: 10.1103/PhysRevB.58.11721 |
| — | — | — | — | — | 1998 | T2 | cond-mat/9810167 |
| — | — | polycrystal | — | — | 1998 | T2 | cond-mat/9811060 |
Structure
- Crystal structure
- three-layer Hg-cuprate phase
- Space group
- P4/mmm (#123)
- Lattice c (Å)
- 15.860
Superconducting parameters
- Pairing symmetry
- d-wave
- Gap structure
- nodal
- λ_eph (e–ph coupling)
- —
Samples & pressure
- Substrate
- SrTiO3
- Pressure type
- none
- Doping type
- hole
- Doping level
- 0.102