Tc max
10.4 K
Tc ambient
10.4 K
arXiv year
2018
Papers
6
Tc exp.
10.4 K
Tc theo.
16.4 K
Evidence
experimental
Tc max measured at ambient, polycrystal, resistivity, DOI: 10.1103/PhysRevMaterials.5.L021801, confirmed by 3 papers
Evidence (11 records from 6 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 16.4 | — | — | — | s-wave | 2021 | T1 | DOI: 10.1103/PhysRevB.103.094512 |
| 15.2 | — | — | — | s-wave | 2021 | T1 | DOI: 10.1103/PhysRevB.103.094512 |
| 10.4 | ambient | polycrystal | resistivity | — | 2021 | T1 | DOI: 10.1103/PhysRevMaterials.5.L021801 |
| 10.4 | — | polycrystal | resistivity, susceptibility, specific_heat | — | 2018 | T1 | 1805.05257 |
| 10.0 | — | powder | neutron | — | 2023 | T1 | DOI: 10.1103/PhysRevB.107.L180504 |
| 9.2 | 1.2 | polycrystal | resistivity | — | 2021 | T1 | DOI: 10.1103/PhysRevMaterials.5.L021801 |
| 8.1 | 30.0 | polycrystal | resistivity | — | 2021 | T1 | DOI: 10.1103/PhysRevMaterials.5.L021801 |
| 4.6 | 18.2 | polycrystal | resistivity | — | 2021 | T1 | DOI: 10.1103/PhysRevMaterials.5.L021801 |
| — | — | — | — | s-wave | 2021 | — | 2103.07249 |
| — | ambient | — | — | — | 2020 | T1 | 2010.14710 |
| — | — | — | — | — | 2020 | T1 | 2010.14710 |
Structure
- Crystal structure
- hexagonal
- Space group
- P-6m2 (#187)
- Lattice a (Å)
- 10.256
- Lattice c (Å)
- 4.463
Superconducting parameters
- Pairing symmetry
- s-wave
- Gap structure
- multi_gap
- λ_eph (e–ph coupling)
- 1.92
- ω_log
- 123 K
Samples & pressure
- Sample form
- polycrystal