Tc max
30.0 K
Tc ambient
—
arXiv year
2023
Papers
14
Tc exp.
30.0 K
Tc theo.
—
Evidence
mixed
Tc max measured at P=77.9 GPa, single_crystal, resistivity, arXiv:2501.13511, confirmed by 4 papers
Evidence (23 records from 14 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 30.0 | 77.9 | single_crystal | resistivity | — | 2025 | T1 | 2501.13511 |
| 25.0 | 42.5 | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevX.15.021005 |
| 23.5 | 56.8 | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevX.15.021005 |
| 23.0 | 25.6 | — | ultrafast_spectroscopy | — | 2025 | — | 2503.05176 |
| 22.0 | 22.0 | — | ultrafast_spectroscopy | — | 2025 | — | 2503.05176 |
| 21.8 | 50.2 | single_crystal | resistivity | — | 2026 | T1 | DOI: 10.1103/h5sv-dzd1 |
| 19.0 | 48.0 | single_crystal | susceptibility | — | 2025 | T1 | DOI: 10.1103/PhysRevX.15.021005 |
| 18.6 | 50.0 | single_crystal | susceptibility | — | 2026 | T1 | DOI: 10.1103/h5sv-dzd1 |
| 18.5 | 50.2 | single_crystal | resistivity | — | 2026 | T1 | DOI: 10.1103/h5sv-dzd1 |
| 17.0 | 17.4 | — | ultrafast_spectroscopy | — | 2025 | — | 2503.05176 |
| 14.9 | 50.0 | single_crystal | susceptibility | — | 2026 | T1 | DOI: 10.1103/h5sv-dzd1 |
| 12.3 | 38.5 | single_crystal | susceptibility | — | 2025 | T1 | DOI: 10.1103/PhysRevX.15.021005 |
| — | — | single_crystal | — | — | 2025 | — | 2502.14410 |
| — | — | — | — | s_pm | 2024 | — | 2402.05447 |
| — | — | — | — | s_pm | 2024 | T1 | 2402.05285 |
| — | ambient | — | — | — | 2024 | T1 | 2411.12349 |
| — | 40.0 | — | — | — | 2024 | T1 | 2411.12349 |
| — | — | — | — | — | 2024 | — | 2403.05012 |
| — | — | — | — | — | 2024 | T1 | 2404.09162 |
| — | — | — | — | s_pm | 2024 | T3 | 2405.04340 |
| — | 40.0 | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.144511 |
| — | — | — | — | s_pm | 2024 | T3 | 2402.07902 |
| — | 40.0 | — | — | — | 2023 | T1 | 2309.09462 |
Structure
- Crystal structure
- tetragonal
- Space group
- I4/mmm
- Phase
- n=3 RP
Superconducting parameters
- Pairing symmetry
- s_pm
- Gap structure
- nodal
- Hc2
- 24.4 T (1.8 K, H parallel c)
- λ_eph (e–ph coupling)
- 0.12
Competing orders
- Competing order
- CDW
- T_CDW
- 130.0 K
- ρ(T) exponent
- 1.00
Samples & pressure
- Sample form
- single_crystal
- Pressure type
- hydrostatic
- Doping level
- 0.234