Tc max
250.0 K
Tc ambient
—
arXiv year
2018
Papers
27
Tc exp.
250.0 K
Tc theo.
250.0 K
Evidence
theoretical
Tc max measured at P=170 GPa, resistivity, arXiv:1812.01561
Evidence (42 records from 27 papers)
the flat columns above are aggregates — each line here is one paper's claimHydride Tc parameters (375)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| LaH10 | 280.0 | 100.0 | — | — | — | DFT | 2018 | 1812.01561 |
| LaH10 | 250.0 | 100.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevB.106.134509 |
| LaH10 | 245.0 | 100.0 | — | — | — | Eliashberg | 2021 | 2101.03481 |
| LaH10 | 233.0 | 100.0 | — | — | — | Eliashberg | 2021 | 2101.03481 |
| LaH10 | 250.0 | 129.0 | — | — | — | DFT | 2024 | 2407.12922 |
| LaH10 | 250.0 | 129.0 | 3.60 | — | — | Eliashberg | 2019 | 1907.11916 |
| LaH10 | 233.0 | 130.0 | — | — | — | resistivity | 2022 | 2202.04254 |
| LaH10 | 246.0 | 136.0 | — | — | — | resistivity | 2023 | 2312.12706 |
| LaH10 | 250.0 | 138.0 | — | — | — | resistivity | 2024 | 2407.12922 |
| LaH10 | 159.0 | 140.0 | — | — | — | resistivity | 2025 | 2511.10784 |
| LaH10 | 115.0 | 140.0 | — | — | — | resistivity | 2025 | 2511.10784 |
| LaH10 | 252.0 | 143.0 | — | — | — | DFT | 2023 | 2309.13919 |
| LaH10 | 174.0 | 145.0 | 2.40 | — | 859 | Eliashberg | 2025 | 2511.10784 |
| LaH10 | 160.0 | 145.0 | 2.40 | — | 859 | Eliashberg | 2025 | 2511.10784 |
| LaH10 | 285.0 | 150.0 | — | — | — | Allen-Dynes | 2023 | 2312.12706 |
| LaH10 | 265.0 | 150.0 | — | — | — | DFT | 2019 | 1902.07993 |
| LaH10 | 250.0 | 150.0 | — | — | — | cited | 2025 | 2505.14048 |
| LaH10 | 250.0 | 150.0 | — | — | — | DFT | 2025 | 2507.06749 |
| LaH10 | 250.0 | 150.0 | — | — | — | cited | 2025 | 2506.17456 |
| LaH10 | 250.0 | 150.0 | — | — | — | DFT | 2024 | 2403.13496 |
| LaH10 | 250.0 | 150.0 | — | — | — | resistivity | 2024 | 2412.18341 |
| LaH10 | 250.0 | 150.0 | — | — | — | resistivity | 2024 | 2403.13496 |
| LaH10 | 250.0 | 150.0 | — | — | — | cited | 2023 | 2307.10728 |
| LaH10 | 250.0 | 150.0 | — | — | — | cited | 2022 | DOI: 10.1103/PhysRevB.106.214508 |
| LaH10 | 250.0 | 150.0 | — | — | — | cited | 2022 | 2205.07955 |
| LaH10 | 250.0 | 150.0 | — | — | — | DFT | 2020 | 2010.06446 |
| LaH10 | 249.0 | 150.0 | — | — | — | Allen-Dynes | 2023 | 2312.12706 |
| LaH10 | 249.0 | 150.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 249.0 | 150.0 | — | — | — | resistivity | 2019 | 1912.09663 |
| LaH10 | 247.0 | 150.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.103.134505 |
| LaH10 | 246.0 | 150.0 | — | — | — | cited | 2022 | 2202.04254 |
| LaH10 | 215.0 | 150.0 | 2.19 | 0.10 | — | Eliashberg | 2020 | 1905.12308 |
| LaH10 | 215.0 | 150.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.140501 |
| LaH10 | 215.0 | 150.0 | — | — | — | resistivity | 2018 | 1810.12338 |
| LaH10 | 215.0 | 150.0 | — | — | — | resistivity | 2018 | 1811.08548 |
| LaH10 | 203.0 | 150.0 | 2.77 | 0.20 | 833 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 112.0 | 150.0 | — | — | — | cited | 2022 | 2202.04254 |
| LaH10 | 73.0 | 150.0 | — | — | — | cited | 2022 | 2202.04254 |
| LaH10 | 255.0 | 155.0 | — | — | — | cited | 2021 | 2106.10379 |
| LaH10 | 246.0 | 158.0 | 2.30 | 0.10 | 1490 | Eliashberg | 2024 | 2409.09836 |
| LaH10 | 294.0 | 160.0 | — | — | — | resistivity | 2020 | 2006.03004 |
| LaH10 | 233.0 | 165.0 | — | — | — | cited | 2022 | 2202.04254 |
| LaH10 | 197.0 | 165.0 | 2.63 | 0.20 | 840 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 74.0 | 165.0 | — | — | — | cited | 2022 | 2202.04254 |
| LaH10 | 251.0 | 168.0 | — | — | — | resistivity | 2023 | 2312.12706 |
| LaH10 | 240.0 | 168.0 | — | — | — | cited | 2024 | 2408.13419 |
| LaH10 | 271.0 | 170.0 | — | — | — | SCDFT | 2018 | 1810.01113 |
| LaH10 | 260.0 | 170.0 | — | — | — | cited | 2025 | 2508.04835 |
| LaH10 | 260.0 | 170.0 | — | — | — | cited | 2025 | DOI: 10.1103/2l5v-x76p |
| LaH10 | 259.0 | 170.0 | 3.94 | 0.20 | 801 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 259.0 | 170.0 | — | — | — | Eliashberg | 2018 | 1810.01113 |
| LaH10 | 255.0 | 170.0 | — | — | — | experimental | 2025 | 2504.21101 |
| LaH10 | 255.0 | 170.0 | — | — | — | cited | 2025 | 2504.21101 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevB.108.L020506 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2023 | 2302.12988 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevMaterials.5.024801 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2021 | 2101.03481 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2021 | 2102.12077 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.104.L020504 |
| LaH10 | 255.0 | 170.0 | — | — | — | cited | 2021 | 2111.10797 |
| LaH10 | 255.0 | 170.0 | — | — | — | cited | 2021 | 2112.10090 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2020 | 2007.01531 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2020 | 2007.03914 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.101.104506 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2019 | 1907.07820 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.100.060502 |
| LaH10 | 255.0 | 170.0 | — | — | — | resistivity | 2019 | 1910.05875 |
| LaH10 | 251.0 | 170.0 | — | — | — | resistivity | 2018 | 1812.01561 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2026 | DOI: 10.1103/rltl-vgzj |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2026 | 2601.02966 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2026 | DOI: 10.1103/8b43-4dvw |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2026 | DOI: 10.1103/jrvy-fy1f |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2025 | 2507.08009 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2025 | DOI: 10.1103/3w8q-c26h |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2025 | 2509.20742 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.134509 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2025 | 2509.17501 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2025 | 2508.10912 |
| LaH10 | 250.0 | 170.0 | — | — | — | DFT | 2025 | 2511.17868 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2025 | 2512.20228 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2025 | DOI: 10.1103/PhysRevB.111.134516 |
| LaH10 | 250.0 | 170.0 | — | — | — | BCS | 2025 | 2512.16274 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2025 | DOI: 10.1103/lswp-5cxx |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2024 | 2411.09966 |
| LaH10 | 250.0 | 170.0 | — | — | — | susceptibility | 2024 | 2408.12675 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.110.184113 |
| LaH10 | 250.0 | 170.0 | — | — | — | DFT | 2024 | 2411.09966 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2023 | 2310.06804 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevB.108.174507 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevB.108.174513 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2023 | 2312.12694 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2022 | 2209.05014 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevResearch.4.013248 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevMaterials.6.034801 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevB.105.245420 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2021 | 2107.12316 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.104.174106 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2021 | DOI: 10.1103/PhysRevB.103.094505 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2020 | 2007.06640 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2020 | DOI: 10.1103/PhysRevMaterials.4.114802 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2020 | 2010.00160 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.102.144524 |
| LaH10 | 250.0 | 170.0 | — | — | — | cited | 2020 | DOI: 10.1103/PhysRevB.102.134510 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2020 | 2006.08390 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | 1905.05419 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | 1910.00922 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.100.094505 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevLett.123.097001 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.140501 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.100.174513 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.100505 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2019 | 1910.02991 |
| LaH10 | 250.0 | 170.0 | — | — | — | resistivity | 2018 | 1811.08548 |
| LaH10 | 260.0 | 175.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.109.014501 |
| LaH10 | 255.0 | 175.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.094520 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2025 | 2510.10720 |
| LaH10 | 255.0 | 175.0 | — | — | — | cited | 2025 | 2510.21877 |
| LaH10 | 255.0 | 175.0 | — | — | — | cited | 2024 | 2405.13752 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.110.104504 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevB.108.184102 |
| LaH10 | 255.0 | 175.0 | — | — | — | cited | 2023 | 2305.06103 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevB.105.104511 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevB.106.104508 |
| LaH10 | 255.0 | 175.0 | — | — | — | cited | 2022 | DOI: 10.1103/PhysRevLett.128.047001 |
| LaH10 | 255.0 | 175.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.101.174102 |
| LaH10 | 255.0 | 175.0 | — | — | — | cited | 2019 | DOI: 10.1103/PhysRevB.100.184505 |
| LaH10 | 250.0 | 175.0 | — | — | — | cited | 2025 | DOI: 10.1103/gwc3-myp7 |
| LaH10 | 250.0 | 175.0 | — | — | — | cited | 2025 | DOI: 10.1103/6vwp-j9sd |
| LaH10 | 250.0 | 175.0 | — | — | — | cited | 2024 | 2412.09340 |
| LaH10 | 255.0 | 177.5 | — | — | — | resistivity | 2020 | 2011.12891 |
| LaH10 | 250.0 | 177.5 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 250.0 | 177.5 | — | — | — | cited | 2021 | 2107.04776 |
| LaH10 | 250.0 | 177.5 | — | — | — | resistivity | 2019 | 1907.11916 |
| LaH10 | 255.0 | 179.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.109.174507 |
| LaH10 | 260.0 | 180.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.109.L180501 |
| LaH10 | 260.0 | 180.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevB.108.174507 |
| LaH10 | 260.0 | 180.0 | — | — | — | resistivity | 2023 | 2312.12706 |
| LaH10 | 260.0 | 180.0 | — | — | — | cited | 2023 | 2311.01656 |
| LaH10 | 260.0 | 180.0 | — | — | — | resistivity | 2020 | 2006.03004 |
| LaH10 | 260.0 | 180.0 | — | — | — | resistivity | 2019 | 1907.02313 |
| LaH10 | 255.0 | 180.0 | — | — | — | cited | 2026 | DOI: 10.1103/mhxb-8yqd |
| LaH10 | 255.0 | 180.0 | — | — | — | DFT | 2025 | DOI: 10.1103/sn9r-3cx2 |
| LaH10 | 255.0 | 180.0 | — | — | — | cited | 2025 | 2502.06821 |
| LaH10 | 255.0 | 180.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.109.094106 |
| LaH10 | 255.0 | 180.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.110.174514 |
| LaH10 | 255.0 | 180.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.109.064513 |
| LaH10 | 255.0 | 180.0 | — | — | — | resistivity | 2023 | 2312.01290 |
| LaH10 | 255.0 | 180.0 | — | — | — | resistivity | 2022 | DOI: 10.1103/PhysRevB.106.024519 |
| LaH10 | 255.0 | 180.0 | — | — | — | cited | 2021 | 2111.03276 |
| LaH10 | 253.0 | 180.0 | — | — | — | resistivity | 2021 | 2109.07051 |
| LaH10 | 250.0 | 180.0 | — | — | — | resistivity | 2025 | DOI: 10.1103/PhysRevB.111.054505 |
| LaH10 | 250.0 | 180.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.054505 |
| LaH10 | 250.0 | 180.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.109.L020503 |
| LaH10 | 250.0 | 180.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.109.L020503 |
| LaH10 | 250.0 | 180.0 | — | — | — | resistivity | 2023 | 2308.02977 |
| LaH10 | 260.0 | 185.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.101.224511 |
| LaH10 | 255.0 | 185.0 | — | — | — | cited | 2023 | 2305.08058 |
| LaH10 | 255.0 | 185.0 | — | — | — | cited | 2023 | 2301.09032 |
| LaH10 | 255.0 | 185.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevB.108.054515 |
| LaH10 | 255.0 | 185.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevB.108.054515 |
| LaH10 | 250.0 | 185.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevB.108.064102 |
| LaH10 | 260.0 | 188.0 | — | — | — | resistivity | 2026 | 2601.01398 |
| LaH10 | 260.0 | 188.0 | — | — | — | cited | 2026 | DOI: 10.1103/lf3k-r97c |
| LaH10 | 260.0 | 188.0 | — | — | — | cited | 2025 | DOI: 10.1103/gnq4-b1gr |
| LaH10 | 260.0 | 188.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevB.108.174513 |
| LaH10 | 260.0 | 188.0 | — | — | — | cited | 2022 | DOI: 10.1103/PhysRevB.105.024504 |
| LaH10 | 260.0 | 188.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevLett.122.027001 |
| LaH10 | 255.0 | 188.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.110.144523 |
| LaH10 | 248.0 | 188.0 | — | — | — | cited | 2022 | 2202.04254 |
| LaH10 | 265.0 | 190.0 | — | — | — | resistivity | 2022 | 2212.09789 |
| LaH10 | 265.0 | 190.0 | — | — | — | resistivity | 2019 | 1901.04001 |
| LaH10 | 265.0 | 190.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.220502 |
| LaH10 | 260.0 | 190.0 | — | — | — | cited | 2025 | 2505.11964 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2024 | 2408.10625 |
| LaH10 | 260.0 | 190.0 | — | — | — | cited | 2024 | 2408.17416 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 260.0 | 190.0 | — | — | — | cited | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 260.0 | 190.0 | 3.35 | — | — | Eliashberg | 2021 | 2105.05463 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.104.174106 |
| LaH10 | 260.0 | 190.0 | — | — | — | cited | 2021 | 2106.12371 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| LaH10 | 260.0 | 190.0 | 2.82 | 0.10 | — | Eliashberg | 2020 | 1905.12308 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2020 | 2001.05305 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2020 | 2007.06640 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevLett.123.097001 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.140501 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2019 | 1902.01772 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.100505 |
| LaH10 | 260.0 | 190.0 | — | — | — | resistivity | 2018 | 1811.08548 |
| LaH10 | 255.0 | 190.0 | — | — | — | resistivity | 2025 | DOI: 10.1103/PhysRevB.111.054517 |
| LaH10 | 255.0 | 190.0 | — | — | — | cited | 2025 | DOI: 10.1103/ckk3-mwqq |
| LaH10 | 255.0 | 190.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.054517 |
| LaH10 | 255.0 | 190.0 | — | — | — | cited | 2021 | 2111.02765 |
| LaH10 | 250.0 | 190.0 | — | — | — | cited | 2023 | 2301.13153 |
| LaH10 | 262.5 | 195.0 | — | — | — | resistivity | 2018 | 1810.12338 |
| LaH10 | 301.0 | 200.0 | — | — | — | Allen-Dynes | 2023 | 2312.12706 |
| LaH10 | 288.0 | 200.0 | — | 0.10 | — | Eliashberg | 2018 | 1806.00163 |
| LaH10 | 288.0 | 200.0 | 2.28 | 0.10 | — | McMillan | 2018 | 1810.12338 |
| LaH10 | 288.0 | 200.0 | — | 0.10 | — | Eliashberg | 2017 | DOI: 10.1103/PhysRevLett.119.107001 |
| LaH10 | 280.0 | 200.0 | — | — | — | DFT | 2026 | DOI: 10.1103/jrvy-fy1f |
| LaH10 | 280.0 | 200.0 | — | — | — | DFT | 2023 | 2311.08070 |
| LaH10 | 280.0 | 200.0 | — | — | — | DFT | 2022 | DOI: 10.1103/PhysRevMaterials.6.034801 |
| LaH10 | 271.0 | 200.0 | 3.75 | 0.20 | 906 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 271.0 | 200.0 | — | 0.11 | — | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.134509 |
| LaH10 | 260.0 | 200.0 | — | — | — | resistivity | 2025 | DOI: 10.1103/PhysRevB.111.134516 |
| LaH10 | 260.0 | 200.0 | — | — | — | resistivity | 2025 | DOI: 10.1103/c7w9-7tgy |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2025 | 2502.06700 |
| LaH10 | 260.0 | 200.0 | — | — | — | DFT | 2024 | 2411.09966 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2024 | 2411.09966 |
| LaH10 | 260.0 | 200.0 | — | — | — | resistivity | 2024 | 2405.18544 |
| LaH10 | 260.0 | 200.0 | — | — | — | experimental | 2023 | 2401.00088 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2023 | 2303.15622 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2023 | 2304.04310 |
| LaH10 | 260.0 | 200.0 | — | — | — | resistivity | 2023 | 2401.00088 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2023 | 2401.00088 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2022 | 2205.11569 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2021 | 2103.00193 |
| LaH10 | 260.0 | 200.0 | — | — | — | cited | 2021 | 2109.09898 |
| LaH10 | 260.0 | 200.0 | — | — | — | resistivity | 2019 | 1906.03462 |
| LaH10 | 255.0 | 200.0 | — | — | — | cited | 2025 | 2501.14420 |
| LaH10 | 255.0 | 200.0 | — | — | — | resistivity | 2025 | DOI: 10.1103/PhysRevResearch.7.013049 |
| LaH10 | 255.0 | 200.0 | — | — | — | DFT | 2025 | 2508.18429 |
| LaH10 | 255.0 | 200.0 | — | — | — | DFT | 2023 | 2305.12977 |
| LaH10 | 255.0 | 200.0 | — | — | — | DFT | 2023 | DOI: 10.1103/PhysRevB.108.174514 |
| LaH10 | 255.0 | 200.0 | — | — | — | resistivity | 2020 | 2012.14985 |
| LaH10 | 255.0 | 200.0 | — | — | — | cited | 2020 | 2002.00549 |
| LaH10 | 250.0 | 200.0 | — | — | — | resistivity | 2024 | 2402.19384 |
| LaH10 | 250.0 | 200.0 | — | — | — | DFT | 2022 | 2206.04146 |
| LaH10 | 250.0 | 200.0 | — | — | — | resistivity | 2019 | 1910.00385 |
| LaH10 | 240.0 | 200.0 | — | — | — | Allen-Dynes | 2023 | 2312.12706 |
| LaH10 | 238.0 | 200.0 | 3.57 | — | 733 | Eliashberg | 2018 | DOI: 10.1103/PhysRevB.98.100102 |
| LaH10 | 237.0 | 200.0 | 3.57 | 0.12 | — | Allen-Dynes | 2021 | 2111.03697 |
| LaH10 | 237.0 | 200.0 | 3.57 | 0.12 | — | Eliashberg | 2018 | 1810.12338 |
| LaH10 | 237.0 | 200.0 | 3.57 | 0.12 | 733 | McMillan | 2018 | DOI: 10.1103/PhysRevB.98.100102 |
| LaH10 | 209.0 | 200.0 | 3.57 | 0.12 | — | McMillan | 2018 | 1810.12338 |
| LaH10 | 160.0 | 200.0 | — | — | — | DFT | 2023 | 2312.12694 |
| LaH10 | 275.0 | 202.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.100.060502 |
| LaH10 | 275.0 | 202.0 | — | — | — | resistivity | 2019 | 1907.07820 |
| LaH10 | 164.0 | 205.0 | 4.43 | 0.13 | 467 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 145.0 | 205.0 | 3.90 | 0.13 | 467 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 286.0 | 210.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.109.054505 |
| LaH10 | 286.0 | 210.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.109.054505 |
| LaH10 | 286.0 | 210.0 | — | — | — | DFT | 2019 | DOI: 10.1103/PhysRevB.99.100505 |
| LaH10 | 286.0 | 210.0 | — | — | — | Eliashberg | 2019 | DOI: 10.1103/PhysRevB.100.174513 |
| LaH10 | 286.0 | 210.0 | — | — | — | DFT | 2018 | 1809.08323 |
| LaH10 | 286.0 | 210.0 | — | — | — | cited | 2018 | 1804.08224 |
| LaH10 | 280.0 | 210.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.174521 |
| LaH10 | 280.0 | 210.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.014510 |
| LaH10 | 280.0 | 210.0 | — | — | — | cited | 2025 | 2503.07042 |
| LaH10 | 280.0 | 210.0 | — | — | — | resistivity | 2025 | 2503.07042 |
| LaH10 | 280.0 | 210.0 | — | — | — | cited | 2024 | 2403.15283 |
| LaH10 | 280.0 | 210.0 | — | — | — | cited | 2024 | 2410.18405 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2023 | DOI: 10.1103/PhysRevB.108.104502 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2022 | DOI: 10.1103/PhysRevB.105.214503 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2021 | DOI: 10.1103/PhysRevLett.126.117003 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2021 | 2106.07322 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2021 | DOI: 10.1103/PhysRevB.104.L100504 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2020 | 2007.06640 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2020 | DOI: 10.1103/PhysRevB.101.134108 |
| LaH10 | 280.0 | 210.0 | — | — | — | DFT | 2019 | 1911.09293 |
| LaH10 | 280.0 | 210.0 | 3.41 | 0.12 | — | Eliashberg | 2018 | 1810.12338 |
| LaH10 | 275.0 | 210.0 | — | — | — | DFT | 2020 | DOI: 10.1103/PhysRevB.101.224511 |
| LaH10 | 274.0 | 210.0 | — | — | — | cited | 2024 | DOI: 10.1103/PhysRevB.110.224507 |
| LaH10 | 273.0 | 210.0 | — | 0.10 | — | DFT | 2019 | DOI: 10.1103/PhysRevB.100.174513 |
| LaH10 | 270.0 | 210.0 | — | — | — | DFT | 2019 | DOI: 10.1103/PhysRevLett.122.027001 |
| LaH10 | 261.0 | 210.0 | 2.96 | 0.11 | 1090 | Allen-Dynes | 2021 | DOI: 10.1103/PhysRevB.104.214505 |
| LaH10 | 249.0 | 210.0 | 3.42 | 0.20 | 851 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 238.0 | 210.0 | — | 0.10 | — | Allen-Dynes | 2019 | DOI: 10.1103/PhysRevB.100.174506 |
| LaH10 | 238.0 | 210.0 | — | — | — | Allen-Dynes | 2019 | 1908.00746 |
| LaH10 | 237.9 | 210.0 | 2.16 | 0.13 | 1184 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| LaH10 | 228.5 | 210.0 | 3.41 | 0.12 | — | McMillan | 2018 | 1810.12338 |
| LaH10 | 237.9 | 214.0 | 2.02 | 0.15 | 1311 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| LaH10 | 265.0 | 220.0 | 4.24 | 0.13 | 672 | Eliashberg | 2019 | DOI: 10.1103/PhysRevB.100.060502 |
| LaH10 | 265.0 | 220.0 | 4.24 | 0.13 | 672 | Eliashberg | 2019 | 1907.07820 |
| LaH10 | 225.0 | 229.0 | 3.68 | 0.13 | 784 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 201.0 | 229.0 | 3.24 | 0.13 | 784 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 280.0 | 250.0 | 2.29 | — | 877 | DFT | 2023 | 2304.08992 |
| LaH10 | 274.0 | 250.0 | 2.29 | 0.10 | 1253 | DFT | 2022 | DOI: 10.1103/PhysRevB.106.104508 |
| LaH10 | 274.0 | 250.0 | — | — | — | cited | 2021 | DOI: 10.1103/PhysRevB.104.214511 |
| LaH10 | 269.0 | 250.0 | 2.38 | 0.10 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 269.0 | 250.0 | 2.38 | 0.10 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 265.5 | 250.0 | 2.20 | 0.12 | — | Eliashberg | 2021 | 2111.03697 |
| LaH10 | 265.5 | 250.0 | 2.20 | 0.12 | — | Eliashberg | 2018 | DOI: 10.1103/PhysRevB.98.100102 |
| LaH10 | 257.0 | 250.0 | 2.29 | 0.13 | 1253 | DFT | 2022 | DOI: 10.1103/PhysRevB.106.104508 |
| LaH10 | 256.0 | 250.0 | 2.53 | 0.13 | — | Eliashberg | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 250.0 | 250.0 | — | — | — | cited | 2022 | 2201.09500 |
| LaH10 | 249.0 | 250.0 | 2.38 | 0.15 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 249.0 | 250.0 | 2.38 | 0.15 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 246.0 | 250.0 | 2.29 | 0.20 | 1253 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.024508 |
| LaH10 | 234.0 | 250.0 | 2.38 | 0.20 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 234.0 | 250.0 | 2.38 | 0.20 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 230.0 | 250.0 | — | — | — | Eliashberg | 2020 | 2004.08591 |
| LaH10 | 230.0 | 250.0 | — | — | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.102.134503 |
| LaH10 | 227.5 | 250.0 | 2.29 | 0.10 | 1253 | DFT | 2019 | DOI: 10.1103/PhysRevB.100.184502 |
| LaH10 | 223.9 | 250.0 | 2.25 | 0.10 | 1445 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.144524 |
| LaH10 | 220.0 | 250.0 | 2.53 | 0.13 | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 217.2 | 250.0 | 2.25 | 0.12 | — | Allen-Dynes | 2021 | 2111.03697 |
| LaH10 | 210.4 | 250.0 | 2.25 | 0.13 | 1445 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.144524 |
| LaH10 | 206.0 | 250.0 | 2.46 | — | 1068 | DFT | 2019 | 1906.02695 |
| LaH10 | 187.0 | 250.0 | — | — | — | DFT | 2023 | 2312.12694 |
| LaH10 | 263.0 | 255.0 | 3.07 | 0.13 | 1127 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 236.0 | 255.0 | 2.70 | 0.13 | 1127 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 250.0 | 260.0 | 2.35 | 0.13 | 1147 | Eliashberg | 2019 | DOI: 10.1103/PhysRevB.100.060502 |
| LaH10 | 250.0 | 260.0 | 2.35 | 0.13 | 1147 | Eliashberg | 2019 | 1907.07820 |
| LaH10 | 215.0 | 262.0 | — | 0.13 | — | Eliashberg | 2020 | 2001.05305 |
| LaH10 | 215.0 | 262.0 | — | 0.13 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.224511 |
| LaH10 | 250.0 | 267.0 | — | — | — | resistivity | 2021 | DOI: 10.1103/PhysRevB.104.024503 |
| LaH10 | 250.0 | 267.0 | — | — | — | resistivity | 2021 | 2107.12255 |
| LaH10 | 245.5 | 269.0 | — | 0.13 | — | Eliashberg | 2020 | 2001.05305 |
| LaH10 | 245.5 | 269.0 | — | 0.13 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.224511 |
| LaH10 | 258.0 | 283.0 | 2.57 | 0.13 | 1293 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 230.0 | 283.0 | 2.27 | 0.13 | 1293 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 335.0 | 300.0 | — | 0.13 | — | Eliashberg | 2018 | 1811.08548 |
| LaH10 | 270.0 | 300.0 | — | 0.13 | — | Allen-Dynes | 2018 | 1811.08548 |
| LaH10 | 255.0 | 300.0 | — | 0.13 | — | Eliashberg | 2019 | DOI: 10.1103/PhysRevB.99.140501 |
| LaH10 | 252.0 | 300.0 | 1.82 | 0.10 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 252.0 | 300.0 | — | 0.13 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.104506 |
| LaH10 | 252.0 | 300.0 | — | 0.13 | — | Eliashberg | 2019 | 1910.05875 |
| LaH10 | 252.0 | 300.0 | 1.82 | 0.10 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 249.0 | 300.0 | 1.90 | 0.10 | 1575 | Eliashberg | 2021 | 2106.07266 |
| LaH10 | 233.0 | 300.0 | — | — | — | Eliashberg | 2021 | DOI: 10.1103/PhysRevB.104.L020504 |
| LaH10 | 233.0 | 300.0 | 1.86 | 0.13 | 1076 | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.104506 |
| LaH10 | 233.0 | 300.0 | 1.86 | 0.13 | 1341 | Eliashberg | 2019 | 1907.07820 |
| LaH10 | 233.0 | 300.0 | 1.86 | 0.13 | 1341 | Eliashberg | 2019 | DOI: 10.1103/PhysRevB.100.060502 |
| LaH10 | 233.0 | 300.0 | — | 0.13 | — | Eliashberg | 2019 | 1910.05875 |
| LaH10 | 231.0 | 300.0 | 1.82 | 0.15 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 231.0 | 300.0 | 1.82 | 0.15 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 231.0 | 300.0 | 1.74 | 0.10 | 1427 | Eliashberg | 2017 | 1708.08870 |
| LaH10 | 220.0 | 300.0 | — | 0.22 | — | Eliashberg | 2019 | DOI: 10.1103/PhysRevB.99.140501 |
| LaH10 | 220.0 | 300.0 | — | 0.38 | — | Eliashberg | 2018 | 1811.08548 |
| LaH10 | 214.0 | 300.0 | 1.82 | 0.20 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 214.0 | 300.0 | 1.82 | 0.20 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 204.0 | 300.0 | — | 0.13 | — | Allen-Dynes | 2019 | 1910.05875 |
| LaH10 | 203.2 | 300.0 | — | — | — | Eliashberg | 2022 | DOI: 10.1103/PhysRevB.105.174516 |
| LaH10 | 195.5 | 300.0 | — | 0.10 | — | Allen-Dynes | 2022 | DOI: 10.1103/PhysRevB.105.174516 |
| LaH10 | 189.0 | 300.0 | 1.90 | 0.12 | 1414 | DFT | 2025 | DOI: 10.1103/PhysRevB.111.014110 |
| LaH10 | 189.0 | 300.0 | 1.80 | — | 1335 | DFT | 2019 | 1906.02695 |
| LaH10 | 185.0 | 300.0 | — | — | — | DFT | 2023 | 2312.12694 |
| LaH10 | 250.0 | 315.0 | 2.15 | 0.13 | 1483 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 221.0 | 315.0 | 1.89 | 0.13 | 1483 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 232.0 | 348.0 | 1.76 | 0.13 | 1679 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 202.0 | 348.0 | 1.55 | 0.13 | 1679 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 248.7 | 350.0 | 1.69 | 0.00 | — | Eliashberg | 2021 | 2107.04776 |
| LaH10 | 248.7 | 350.0 | 1.69 | 0.00 | — | Eliashberg | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 237.0 | 350.0 | 1.54 | 0.10 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 237.0 | 350.0 | 1.54 | 0.10 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 231.0 | 350.0 | 1.69 | 0.00 | — | Allen-Dynes | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 214.0 | 350.0 | 1.54 | 0.15 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 214.0 | 350.0 | 1.54 | 0.15 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 195.0 | 350.0 | 1.54 | 0.20 | — | Eliashberg | 2020 | DOI: 10.1103/PhysRevB.101.214501 |
| LaH10 | 195.0 | 350.0 | 1.54 | 0.20 | — | Eliashberg | 2019 | 1912.09663 |
| LaH10 | 184.0 | 350.0 | 1.69 | 0.10 | — | Allen-Dynes | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 175.5 | 350.0 | 1.69 | 0.10 | — | Eliashberg | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 175.5 | 350.0 | 1.69 | 0.10 | — | Eliashberg | 2021 | 2107.04776 |
| LaH10 | 136.0 | 350.0 | 1.69 | 0.20 | — | Allen-Dynes | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 122.0 | 350.0 | 1.69 | 0.20 | — | Eliashberg | 2021 | 2107.04776 |
| LaH10 | 122.0 | 350.0 | 1.69 | 0.20 | — | Eliashberg | 2021 | DOI: 10.1103/PhysRevB.104.174506 |
| LaH10 | 218.0 | 385.0 | 1.49 | 0.13 | 1905 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 186.0 | 385.0 | 1.32 | 0.13 | 1905 | Allen-Dynes | 2020 | DOI: 10.1103/PhysRevB.101.060506 |
| LaH10 | 207.0 | 400.0 | 1.41 | 0.13 | — | Eliashberg | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 184.3 | 400.0 | — | — | — | DMFT | 2022 | 2202.11773 |
| LaH10 | 174.0 | 400.0 | 1.41 | 0.13 | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevMaterials.7.L101801 |
| LaH10 | 156.0 | 400.0 | — | — | — | DFT | 2022 | 2202.11773 |
| LaH10 | 260.0 | — | 3.00 | — | — | DFT | 2025 | DOI: 10.1103/PhysRevB.111.174524 |
| LaH10 | 250.0 | — | — | 0.13 | — | Eliashberg | 2026 | DOI: 10.1103/82zm-by55 |
| LaH10 | 250.0 | — | 2.52 | 0.13 | — | Allen-Dynes | 2019 | 1907.07597 |
| LaH10 | 250.0 | — | 2.39 | 0.13 | — | McMillan | 2019 | 1907.07597 |
Structure
- Crystal structure
- Fm-3m
- Space group
- Fm-3m
- Lattice a (Å)
- 3.812
- Lattice c (Å)
- 23.047
Superconducting parameters
- Hc2
- 120.0 T (0 K)
- λ_eph (e–ph coupling)
- 3.57
- ω_log
- 1905 K
Samples & pressure
- Pressure type
- hydrostatic
- Doping level
- 0.300