Tc max
2.1 K
Tc ambient
2.0 K
arXiv year
2002
Papers
18
Tc exp.
2.1 K
Tc theo.
—
Evidence
experimental
Tc max measured at polycrystal, muSR, arXiv:1206.5905, confirmed by 2 papers
Evidence (24 records from 18 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 3.2 | 16.0 | single_crystal | resistivity | — | 2026 | T1 | DOI: 10.1103/cbbg-r8ns |
| 2.1 | — | polycrystal | muSR | p-wave | 2012 | T1 | 1206.5905 |
| 2.1 | — | single_crystal | susceptibility | s-wave | 2024 | T1 | DOI: 10.1103/PhysRevB.109.024515 |
| 2.0 | — | polycrystal | resistivity | — | 2002 | T1 | DOI: 10.1103/PhysRevB.66.092503 |
| 2.0 | — | single_crystal | resistivity | s-wave | 2024 | T1 | DOI: 10.1103/PhysRevB.109.024515 |
| 2.0 | — | single_crystal | susceptibility | unknown | 2024 | T1 | DOI: 10.1103/PhysRevB.109.104517 |
| 2.0 | — | single_crystal | resistivity | s-wave | 2023 | T1 | 2311.12222 |
| 2.0 | ambient | single_crystal | resistivity | — | 2026 | T1 | DOI: 10.1103/cbbg-r8ns |
| 2.0 | — | polycrystal | susceptibility, specific_heat | — | 2002 | T1 | DOI: 10.1103/PhysRevB.66.092503 |
| 2.0 | — | single_crystal | resistivity | s-wave | 2023 | T1 | 2311.12222 |
| 1.8 | — | single_crystal | muSR | unknown | 2024 | T1 | DOI: 10.1103/PhysRevB.109.104517 |
| 1.8 | — | powder | resistivity | — | 2026 | T1 | DOI: 10.1103/tsnb-1mxc |
| 1.8 | — | powder | — | s-wave | 2025 | T1 | 2510.23800 |
| 1.8 | — | single_crystal | resistivity | p-wave | 2024 | — | 2412.09257 |
| 1.8 | — | polycrystal | resistivity, susceptibility, specific_heat | — | 2016 | T1 | DOI: 10.1103/PhysRevLett.117.027001 |
| 1.8 | — | polycrystal | specific_heat, susceptibility | triplet | 2016 | T1 | 1605.08356 |
| 1.8 | — | single_crystal | susceptibility, specific_heat | p-wave | 2024 | — | 2412.09257 |
| — | 7.0 | — | resistivity | — | 2024 | T1 | 2412.10818 |
| — | — | single_crystal | muSR | p-wave | 2023 | T1 | 2311.00069 |
| — | — | single_crystal | specific_heat, susceptibility | unknown | 2021 | T1 | 2109.06983 |
| — | — | — | specific_heat | p-wave | 2020 | T1 | DOI: 10.1103/PhysRevB.101.100506 |
| — | — | — | — | p-wave | 2019 | T1 | 1912.08160 |
| — | — | powder | muSR | unknown | 2012 | T1 | DOI: 10.1103/PhysRevLett.109.097001 |
| — | — | — | — | unknown | 2012 | T1 | 1209.6584 |
Structure
- Crystal structure
- orthorhombic NdNiGa2-type
- Space group
- Cmmm
- Lattice a (Å)
- 4.281
- Lattice c (Å)
- 4.258
Superconducting parameters
- λ_eph (e–ph coupling)
- 0.55