Tc max
—
Tc ambient
—
arXiv year
2026
Papers
2
Evidence (2 records from 2 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| — | 250.0 | — | — | s-wave | 2026 | T2 | 2601.01398 |
| — | — | — | — | — | 2026 | T3 | 2604.04719 |
Hydride Tc parameters (14)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| LaSc2H24 | 316.0 | 167.0 | — | — | — | DFT | 2026 | DOI: 10.1103/2pv4-zcym |
| LaSc2H24 | 316.0 | 167.0 | — | — | — | cited | 2025 | DOI: 10.1103/7lg7-l3x8 |
| LaSc2H24 | 316.0 | 167.0 | — | — | — | DFT | 2025 | DOI: 10.1103/7lg7-l3x8 |
| LaSc2H24 | 287.0 | 167.0 | — | — | — | Allen-Dynes | 2026 | 2604.04719 |
| LaSc2H24 | 284.5 | 230.5 | — | — | — | resistivity | 2025 | 2510.01273 |
| LaSc2H24 | 331.0 | 250.0 | — | — | — | DFT | 2025 | DOI: 10.1103/4hr1-vcvk |
| LaSc2H24 | 331.0 | 250.0 | — | — | — | cited | 2025 | DOI: 10.1103/gnq4-b1gr |
| LaSc2H24 | 298.0 | 250.0 | — | — | — | cited | 2026 | DOI: 10.1103/b62f-sggp |
| LaSc2H24 | 298.0 | 250.0 | — | — | — | DFT | 2026 | 2601.01398 |
| LaSc2H24 | 298.0 | 255.0 | — | — | — | resistivity | 2026 | DOI: 10.1103/2pv4-zcym |
| LaSc2H24 | 298.0 | 260.0 | — | — | — | cited | 2025 | 2511.04222 |
| LaSc2H24 | 339.0 | 290.0 | — | — | — | DFT | 2026 | DOI: 10.1103/2pv4-zcym |
| LaSc2H24 | 329.0 | 300.0 | 3.34 | 0.10 | 968 | Allen-Dynes | 2026 | DOI: 10.1103/5fmy-qlr7 |
| LaSc2H24 | 286.0 | 300.0 | 2.57 | 0.10 | 839 | Eliashberg | 2025 | DOI: 10.1103/7lg7-l3x8 |
Structure
- Crystal structure
- P6/mmm
- Space group
- P6/mmm
Superconducting parameters
- λ_eph (e–ph coupling)
- —