Tc max
14.0 K
Tc ambient
—
arXiv year
2003
Papers
19
Tc exp.
14.0 K
Tc theo.
23.3 K
Evidence
theoretical
Tc max measured at P=30 GPa, polycrystal, susceptibility, DOI: 10.1103/PhysRevLett.91.167001, confirmed by 3 papers
Evidence (64 records from 19 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 40.4 | 165.0 | — | — | — | 2004 | T1 | DOI: 10.1103/PhysRevB.70.132504 |
| 23.3 | 30.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 22.0 | 41.0 | — | — | — | 2010 | T2 | 1008.2822 |
| 20.0 | 36.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 20.0 | 15.0 | — | — | — | 2006 | T1 | DOI: 10.1103/PhysRevB.73.184516 |
| 20.0 | 20.0 | — | — | — | 2005 | — | cond-mat/0510558 |
| 19.0 | 25.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 19.0 | 48.0 | — | — | — | 2004 | T1 | DOI: 10.1103/PhysRevB.70.132504 |
| 16.7 | 48.0 | — | — | — | 2004 | T1 | DOI: 10.1103/PhysRevB.70.132504 |
| 15.2 | 20.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 14.2 | 36.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 14.0 | 30.0 | — | — | — | 2006 | T1 | DOI: 10.1103/PhysRevLett.96.047003 |
| 14.0 | 30.0 | — | — | — | 2005 | T2 | cond-mat/0510670 |
| 14.0 | 30.0 | — | susceptibility | — | 2004 | T2 | cond-mat/0408438 |
| 14.0 | 30.0 | polycrystal | susceptibility | — | 2003 | T1 | DOI: 10.1103/PhysRevLett.91.167001 |
| 14.0 | 30.0 | polycrystal | susceptibility | — | 2003 | T2 | cond-mat/0304598 |
| 12.2 | 30.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 12.0 | 30.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 10.0 | 14.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 9.2 | 25.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 9.1 | 30.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 9.1 | 30.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 7.8 | 22.0 | — | — | — | 2023 | T1 | 2304.14682 |
| 6.8 | 25.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 6.8 | 30.0 | — | — | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.057006 |
| 6.8 | 25.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 6.8 | 20.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 6.8 | 30.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 6.5 | 20.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 6.5 | 25.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 6.5 | 25.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 6.0 | 21.9 | polycrystal | susceptibility | — | 2003 | T1 | DOI: 10.1103/PhysRevLett.91.167001 |
| 6.0 | 21.9 | polycrystal | susceptibility | — | 2003 | T2 | cond-mat/0304598 |
| 5.5 | 20.3 | polycrystal | susceptibility | — | 2003 | T1 | DOI: 10.1103/PhysRevLett.91.167001 |
| 5.5 | 20.3 | polycrystal | susceptibility | — | 2003 | T2 | cond-mat/0304598 |
| 5.0 | 30.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 5.0 | 10.0 | — | — | — | 2005 | — | cond-mat/0510558 |
| 5.0 | 20.0 | — | susceptibility | — | 2004 | T2 | cond-mat/0408438 |
| 4.4 | 20.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 4.4 | 25.0 | — | — | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.057006 |
| 4.4 | 20.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 4.1 | 20.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 4.1 | 20.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 3.8 | 14.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 3.2 | 25.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 2.7 | 20.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 2.2 | 500.0 | — | — | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.060502 |
| 2.2 | 14.0 | — | — | — | 2014 | T3 | 1401.1578 |
| 2.2 | 20.0 | — | — | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.057006 |
| 2.2 | 14.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 2.0 | 14.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 1.8 | 20.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 1.4 | 14.0 | — | — | — | 2013 | T1 | DOI: 10.1103/PhysRevLett.111.057006 |
| 1.0 | 600.0 | — | — | — | 2022 | T1 | DOI: 10.1103/PhysRevB.106.L220501 |
| 0.7 | 14.0 | — | — | — | 2013 | T1 | 1303.5152 |
| 0.5 | 8.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 0.4 | ambient | — | — | — | 2005 | — | cond-mat/0510558 |
| 0.3 | 14.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| 0.0 | 8.0 | — | — | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.184509 |
| — | 20.0 | — | — | — | 2022 | T1 | 2203.15648 |
| — | ambient | — | — | — | 2009 | T1 | DOI: 10.1103/PhysRevB.79.054524 |
| — | ambient | — | — | — | 2005 | T2 | cond-mat/0510670 |
| — | 8.0 | — | — | — | 2005 | T2 | cond-mat/0510670 |
| — | ambient | polycrystal | susceptibility | — | 2004 | T1 | DOI: 10.1103/PhysRevLett.93.157201 |
Structure
- Crystal structure
- bcc
- Space group
- P4132
Superconducting parameters
- λ_eph (e–ph coupling)
- 3.10
- ω_log
- 546 K
Samples & pressure
- Sample form
- polycrystal
- Pressure type
- hydrostatic