Tc max
121.7 K
Tc ambient
—
arXiv year
2017
Papers
3
Tc exp.
—
Tc theo.
121.7 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=25 GPa, DOI: 10.1103/xw5d-vsyg, confirmed by 3 papers
Evidence (6 records from 3 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 121.7 | 25.0 | — | — | — | 2026 | T1 | DOI: 10.1103/xw5d-vsyg |
| 121.5 | 50.0 | — | — | — | 2026 | T1 | DOI: 10.1103/xw5d-vsyg |
| 121.3 | 16.0 | — | — | — | 2026 | T1 | DOI: 10.1103/xw5d-vsyg |
| 100.0 | 200.0 | — | — | — | 2017 | T1 | DOI: 10.1103/PhysRevMaterials.1.074803 |
| 80.0 | 200.0 | — | — | — | 2017 | T1 | DOI: 10.1103/PhysRevMaterials.1.074803 |
| 80.0 | 200.0 | — | — | — | 2017 | T1 | 1705.06977 |
Hydride Tc parameters (18)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| Li2BH6 | 121.3 | 16.0 | 1.48 | 0.10 | 855 | Eliashberg | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 96.3 | 16.0 | 1.48 | 0.10 | 855 | Allen-Dynes | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 121.7 | 25.0 | 1.31 | 0.10 | 1022 | Eliashberg | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 101.4 | 25.0 | 1.31 | 0.10 | 1022 | Allen-Dynes | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 121.5 | 50.0 | 1.07 | 0.10 | 1296 | Eliashberg | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 99.6 | 50.0 | 1.07 | 0.10 | 1296 | Allen-Dynes | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 100.0 | 100.0 | — | — | — | DFT | 2023 | 2301.12320 |
| Li2BH6 | 100.0 | 100.0 | — | — | — | DFT | 2023 | DOI: 10.1103/PhysRevB.107.L180501 |
| Li2BH6 | 100.0 | 100.0 | — | — | — | cited | 2022 | 2209.05014 |
| Li2BH6 | 98.0 | 100.0 | 0.94 | — | 1551 | DFT | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 98.0 | 100.0 | — | — | — | DFT | 2020 | DOI: 10.1103/PhysRevB.102.014516 |
| Li2BH6 | 98.0 | 100.0 | — | — | — | cited | 2020 | 2006.00960 |
| Li2BH6 | 98.0 | 100.0 | 0.94 | 0.10 | 1551 | Allen-Dynes | 2017 | 1705.06977 |
| Li2BH6 | 98.0 | 100.0 | 0.94 | 0.10 | 1551 | Allen-Dynes | 2017 | DOI: 10.1103/PhysRevMaterials.1.074803 |
| Li2BH6 | 100.0 | 150.0 | — | — | — | DFT | 2021 | DOI: 10.1103/PhysRevB.104.174106 |
| Li2BH6 | 81.0 | 200.0 | 0.76 | — | 1940 | DFT | 2026 | DOI: 10.1103/xw5d-vsyg |
| Li2BH6 | 81.0 | 200.0 | 0.76 | 0.10 | 1940 | Allen-Dynes | 2017 | DOI: 10.1103/PhysRevMaterials.1.074803 |
| Li2BH6 | 81.0 | 200.0 | 0.76 | 0.10 | 1940 | Allen-Dynes | 2017 | 1705.06977 |
Structure
- Crystal structure
- Fm-3m
- Space group
- Fm-3m
- Lattice a (Å)
- 5.435
Superconducting parameters
- λ_eph (e–ph coupling)
- 1.48
- ω_log
- 1296 K