Tc max
77.0 K
Tc ambient
—
arXiv year
2020
Papers
1
Tc exp.
—
Tc theo.
77.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=250 GPa, DOI: 10.1103/PhysRevB.102.184103
Evidence (3 records from 1 paper)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 77.0 | 250.0 | — | — | — | 2020 | T1 | DOI: 10.1103/PhysRevB.102.184103 |
| 73.0 | 300.0 | — | — | — | 2020 | T1 | DOI: 10.1103/PhysRevB.102.184103 |
| 68.0 | 350.0 | — | — | — | 2020 | T1 | DOI: 10.1103/PhysRevB.102.184103 |
Hydride Tc parameters (7)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| LiSiH8 | 77.0 | 250.0 | — | — | — | cited | 2022 | 2209.05014 |
| LiSiH8 | 77.0 | 250.0 | 1.08 | 0.10 | 989 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.184103 |
| LiSiH8 | 67.0 | 250.0 | 1.08 | 0.13 | 989 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.184103 |
| LiSiH8 | 73.0 | 300.0 | 0.91 | 0.10 | 1226 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.184103 |
| LiSiH8 | 62.0 | 300.0 | 0.91 | 0.13 | 1226 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.184103 |
| LiSiH8 | 68.0 | 350.0 | 0.84 | 0.10 | 1315 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.184103 |
| LiSiH8 | 56.0 | 350.0 | 0.84 | 0.13 | 1315 | DFT | 2020 | DOI: 10.1103/PhysRevB.102.184103 |
Structure
- Crystal structure
- C2/m
- Space group
- C2/m
Superconducting parameters
- λ_eph (e–ph coupling)
- 1.08
- ω_log
- 1315 K