Tc max
71.0 K
Tc ambient
—
arXiv year
2023
Papers
2
Tc exp.
71.0 K
Tc theo.
225.0 K
Evidence
mixed
Tc max measured at P=218 GPa, resistivity, arXiv:2303.05117
Evidence (6 records from 2 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 225.0 | 200.0 | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.224511 |
| 210.0 | 218.0 | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.224511 |
| 103.0 | 218.0 | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.224511 |
| 71.0 | 218.0 | — | resistivity | — | 2023 | T1 | 2303.05117 |
| 69.0 | 200.0 | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.224511 |
| 65.0 | 181.0 | — | resistivity | — | 2023 | T1 | 2303.05117 |
Hydride Tc parameters (13)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| Lu4H23 | 65.0 | 181.0 | — | — | — | resistivity | 2023 | 2303.05117 |
| Lu4H23 | 68.0 | 199.5 | — | — | — | DFT | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| Lu4H23 | 68.0 | 199.5 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| Lu4H23 | 68.0 | 199.5 | 2.66 | 0.10 | 606 | Eliashberg | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| Lu4H23 | 156.5 | 200.0 | — | 0.10 | — | Eliashberg | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| Lu4H23 | 71.0 | 200.0 | — | — | — | cited | 2023 | 2308.16420 |
| Lu4H23 | 156.5 | 209.0 | — | — | — | DFT | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| Lu4H23 | 156.5 | 218.0 | 2.66 | 0.10 | 606 | Eliashberg | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| Lu4H23 | 71.0 | 218.0 | — | — | — | resistivity | 2023 | 2303.11063 |
| Lu4H23 | 71.0 | 218.0 | — | — | — | resistivity | 2023 | 2303.15622 |
| Lu4H23 | 71.0 | 218.0 | — | — | — | resistivity | 2023 | 2305.06103 |
| Lu4H23 | 71.0 | 218.0 | — | — | — | resistivity | 2023 | 2303.05117 |
| Lu4H23 | 175.0 | 250.0 | — | — | — | DFT | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
Structure
- Crystal structure
- Pm-3n
- Space group
- Pm-3n
Superconducting parameters
- Hc2
- 36.0 T (zero temperature)
- λ_eph (e–ph coupling)
- 2.66