Tc max
55.0 K
Tc ambient
—
arXiv year
2023
Papers
4
Tc exp.
—
Tc theo.
55.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), ambient, arXiv:2304.04447, confirmed by 4 papers
Evidence (6 records from 4 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 55.0 | ambient | — | — | — | 2023 | T1 | 2304.04447 |
| 55.0 | 2.8 | — | — | — | 2023 | T1 | 2304.06685 |
| 53.7 | ambient | — | — | — | 2023 | T2 | 2306.13981 |
| 38.5 | — | — | — | — | 2023 | T1 | 2304.04447 |
| 32.0 | — | — | — | — | 2023 | T1 | 2304.04447 |
| 30.0 | — | — | — | — | 2023 | T1 | 2307.10699 |
Hydride Tc parameters (27)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| LuH3 | 53.7 | ambient | 1.45 | — | 356 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 53.7 | ambient | 1.45 | — | 356 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 43.0 | ambient | 1.15 | — | 401 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 43.0 | ambient | 1.15 | — | 401 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 38.5 | ambient | 1.70 | — | 250 | Eliashberg | 2023 | 2304.04447 |
| LuH3 | 32.0 | ambient | 1.65 | — | 204 | Eliashberg | 2023 | 2304.04447 |
| LuH3 | 31.9 | ambient | 1.70 | — | 250 | McMillan-Allen-Dynes | 2023 | 2304.04447 |
| LuH3 | 29.5 | ambient | 0.91 | — | 423 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 29.5 | ambient | 0.91 | — | 423 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 25.4 | ambient | 1.65 | — | 204 | Allen-Dynes | 2023 | 2304.04447 |
| LuH3 | 20.9 | ambient | 0.77 | — | 428 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 20.9 | ambient | 0.77 | — | 428 | Eliashberg | 2023 | 2306.13981 |
| LuH3 | 294.0 | 1.0 | — | — | — | resistivity | 2023 | 2304.04310 |
| LuH3 | 60.0 | 2.8 | 1.70 | 0.10 | — | anisotropic Eliashberg | 2023 | 2304.06685 |
| LuH3 | 53.0 | 2.8 | 1.70 | 0.10 | — | isotropic Eliashberg | 2023 | 2304.06685 |
| LuH3 | 55.0 | 4.4 | — | — | — | DFT | 2023 | 2306.09868 |
| LuH3 | 19.0 | 6.0 | — | — | — | Eliashberg | 2023 | 2305.06751 |
| LuH3 | 30.0 | 20.0 | — | — | — | DFT | 2023 | 2307.10699 |
| LuH3 | 22.0 | 30.0 | — | — | — | DFT | 2023 | 2306.13981 |
| LuH3 | 12.4 | 122.0 | — | — | — | resistivity | 2024 | DOI: 10.1103/PhysRevB.109.224511 |
| LuH3 | 12.4 | 122.0 | — | — | — | resistivity | 2023 | 2303.15622 |
| LuH3 | 12.4 | 122.0 | — | — | — | resistivity | 2023 | 2306.09868 |
| LuH3 | 12.4 | 122.0 | — | — | — | resistivity | 2023 | DOI: 10.1103/PhysRevB.108.014511 |
| LuH3 | 12.4 | 122.0 | — | — | — | DFT | 2023 | 2306.09868 |
| LuH3 | 15.0 | 128.0 | — | — | — | resistivity | 2023 | 2303.11063 |
| LuH3 | 13.5 | 140.0 | — | — | — | DFT | 2023 | DOI: 10.1103/PhysRevB.108.L020102 |
| LuH3 | 62.0 | — | — | — | 220 | Eliashberg | 2023 | 2306.09868 |
Structure
- Crystal structure
- Fm-3m
- Space group
- Fm-3m
Superconducting parameters
- λ_eph (e–ph coupling)
- 1.70
- ω_log
- 250 K
Samples & pressure
- Doping level
- 0.300