Tc max
—
Tc ambient
—
arXiv year
2019
Papers
1
Evidence (1 record from 1 paper)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| — | — | — | — | — | 2019 | — | 1906.02695 |
Hydride Tc parameters (22)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| MgH6 | 228.0 | 200.0 | 3.02 | 0.10 | 1260 | McMillan-Allen-Dynes | 2023 | DOI: 10.1103/PhysRevMaterials.7.054806 |
| MgH6 | 221.0 | 200.0 | — | — | — | DFT | 2023 | 2312.12694 |
| MgH6 | 286.0 | 300.0 | 2.28 | — | — | Eliashberg | 2021 | DOI: 10.1103/PhysRevB.104.054501 |
| MgH6 | 279.0 | 300.0 | 2.54 | — | 1439 | DFT | 2019 | 1906.02695 |
| MgH6 | 271.0 | 300.0 | — | — | — | cited | 2025 | DOI: 10.1103/PhysRevB.111.014510 |
| MgH6 | 271.0 | 300.0 | — | — | — | cited | 2025 | 2503.07042 |
| MgH6 | 271.0 | 300.0 | — | — | — | resistivity | 2025 | 2503.07042 |
| MgH6 | 271.0 | 300.0 | — | — | — | DFT | 2022 | DOI: 10.1103/PhysRevMaterials.6.034801 |
| MgH6 | 271.0 | 300.0 | — | — | — | DFT | 2020 | 2007.06640 |
| MgH6 | 271.0 | 300.0 | — | — | — | DFT | 2020 | DOI: 10.1103/PhysRevB.102.024501 |
| MgH6 | 263.0 | 300.0 | 3.29 | 0.12 | — | Allen-Dynes | 2021 | 2111.03697 |
| MgH6 | 263.0 | 300.0 | — | 0.12 | — | Allen-Dynes | 2019 | DOI: 10.1103/PhysRevB.100.174506 |
| MgH6 | 263.0 | 300.0 | — | — | — | Allen-Dynes | 2019 | 1908.00746 |
| MgH6 | 263.0 | 300.0 | 3.29 | 0.12 | — | McMillan | 2018 | 1810.12338 |
| MgH6 | 260.0 | 300.0 | — | — | — | cited | 2023 | 2308.15031 |
| MgH6 | 260.0 | 300.0 | — | — | — | DFT | 2021 | 2109.07051 |
| MgH6 | 231.0 | 300.0 | — | — | — | DFT | 2023 | 2312.12694 |
| MgH6 | 271.0 | 400.0 | — | — | — | DFT | 2019 | 1911.09293 |
| MgH6 | 271.0 | 400.0 | — | — | — | cited | 2018 | 1804.08224 |
| MgH6 | 271.0 | 400.0 | — | 0.12 | — | McMillan | 2018 | 1806.00163 |
| MgH6 | 269.0 | 400.0 | 2.00 | — | 1729 | DFT | 2019 | 1906.02695 |
| MgH6 | 214.0 | 500.0 | — | — | — | DFT | 2023 | 2312.12694 |
Structure
- Crystal structure
- bcc
Superconducting parameters
- λ_eph (e–ph coupling)
- —