Tc max
9.2 K
Tc ambient
9.2 K
arXiv year
2010
Papers
11
Tc exp.
9.2 K
Tc theo.
—
Evidence
experimental
Tc max measured at polycrystal, specific_heat, arXiv:1007.0160, confirmed by 3 papers
Evidence (18 records from 11 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 9.3 | — | single_crystal | susceptibility | s-wave | 2018 | T1 | 1803.08366 |
| 9.3 | — | single_crystal | resistivity | s-wave | 2018 | T1 | 1803.08366 |
| 9.2 | — | polycrystal | specific_heat | unknown | 2010 | T1 | 1007.0160 |
| 9.2 | — | polycrystal | resistivity | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064512 |
| 9.2 | — | single_crystal | resistivity | s-wave | 2018 | T1 | 1803.08366 |
| 9.1 | — | polycrystal | resistivity, susceptibility | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064512 |
| 9.0 | — | polycrystal | muSR, specific_heat, susceptibility | s-wave | 2014 | T1 | DOI: 10.1103/PhysRevB.90.054522 |
| 9.0 | — | polycrystal | susceptibility | s-wave | 2011 | T1 | DOI: 10.1103/PhysRevB.84.134506 |
| 9.0 | — | polycrystal | resistivity, specific_heat, susceptibility | — | 2010 | T1 | DOI: 10.1103/PhysRevB.82.064511 |
| 9.0 | — | — | resistivity, specific_heat, muSR | unknown | 2010 | T1 | 1007.0420 |
| 8.9 | — | single_crystal | susceptibility | s-wave | 2018 | T1 | DOI: 10.1103/PhysRevB.97.214518 |
| 8.6 | — | single_crystal | susceptibility | s-wave | 2018 | T1 | 1803.08366 |
| 8.5 | — | single_crystal | resistivity | s-wave | 2018 | T1 | 1803.08366 |
| 8.3 | — | single_crystal | resistivity | s-wave | 2018 | T1 | 1803.08366 |
| 8.0 | — | single_crystal | resistivity, susceptibility | — | 2024 | T1 | 2410.20921 |
| 7.8 | ambient | single_crystal | resistivity | — | 2025 | T1 | 2512.13601 |
| 6.2 | — | polycrystal | muSR | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.212501 |
| — | ambient | single_crystal | resistivity | — | 2025 | T1 | 2512.13601 |
Structure
- Crystal structure
- Cubic, β-Mn type
- Space group
- P4132
- Lattice a (Å)
- 6.863
Superconducting parameters
- Pairing symmetry
- s-wave
- Gap structure
- full_gap
- Hc2
- 15.7 T (0 K)
- λ_eph (e–ph coupling)
- 0.80
Competing orders
- Competing order
- CDW
- T_CDW
- 155.0 K
- ρ(T) exponent
- 2.00
Samples & pressure
- Pressure type
- none