Tc max
201.4 K
Tc ambient
—
arXiv year
2023
Papers
1
Tc exp.
—
Tc theo.
201.4 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=350 GPa, DOI: 10.1103/PhysRevB.107.214511
Evidence (3 records from 1 paper)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 201.4 | 350.0 | — | — | — | 2023 | T1 | DOI: 10.1103/PhysRevB.107.214511 |
| 112.2 | 200.0 | — | — | — | 2023 | T1 | DOI: 10.1103/PhysRevB.107.214511 |
| 95.9 | 350.0 | — | — | — | 2023 | T1 | DOI: 10.1103/PhysRevB.107.214511 |
Hydride Tc parameters (21)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| NaPH6 | 110.5 | 150.0 | 3.31 | 0.10 | 377 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 112.2 | 200.0 | 1.31 | 0.10 | 1128 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 100.8 | 200.0 | 1.31 | 0.13 | 1128 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 83.2 | 200.0 | 1.29 | 0.10 | 854 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 74.6 | 200.0 | 1.29 | 0.13 | 854 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 118.8 | 300.0 | 1.50 | 0.10 | 906 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 96.3 | 300.0 | 0.98 | 0.10 | 1418 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 93.9 | 300.0 | 1.50 | 0.13 | 906 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 82.4 | 300.0 | 0.98 | 0.13 | 1418 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 196.1 | 340.0 | 2.26 | 0.10 | 997 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 145.6 | 340.0 | 2.26 | 0.13 | 997 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 201.4 | 350.0 | 2.35 | 0.10 | 1010 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 151.2 | 350.0 | 2.35 | 0.13 | 1010 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 95.9 | 350.0 | 1.31 | 0.10 | 964 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 93.4 | 350.0 | 0.90 | 0.10 | 1581 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 86.1 | 350.0 | 1.31 | 0.13 | 964 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 78.2 | 350.0 | 0.90 | 0.13 | 1581 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 145.2 | 400.0 | 2.23 | 0.10 | 727 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 105.5 | 400.0 | 2.23 | 0.13 | 727 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 85.1 | 400.0 | 0.88 | 0.10 | 1503 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
| NaPH6 | 70.8 | 400.0 | 0.88 | 0.13 | 1503 | DFT | 2023 | DOI: 10.1103/PhysRevB.107.214511 |
Structure
- Crystal structure
- P6-m2
- Space group
- P6-m2 (#187)
Superconducting parameters
- λ_eph (e–ph coupling)
- 2.35
- ω_log
- 1128 K