Tc max
6.0 K
Tc ambient
6.0 K
arXiv year
2008
Papers
21
Tc exp.
6.0 K
Tc theo.
—
Evidence
experimental
Tc max measured at single_crystal, specific_heat, arXiv:1401.1025, confirmed by 5 papers
Evidence (23 records from 21 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 6.1 | ambient | polycrystal | susceptibility | — | 2021 | T1 | 2102.11933 |
| 6.0 | — | single_crystal | specific_heat | — | 2014 | T1 | 1401.1025 |
| 6.0 | — | single_crystal | susceptibility | — | 2013 | T1 | 1301.1845 |
| 6.0 | — | single_crystal | specific_heat | s-wave | 2010 | T1 | DOI: 10.1103/PhysRevB.82.014518 |
| 6.0 | ambient | single_crystal | specific_heat | s-wave | 2010 | T1 | 1010.5630 |
| 6.0 | — | single_crystal | resistivity, susceptibility | — | 2024 | T1 | DOI: 10.1103/PhysRevResearch.6.L042006 |
| 5.8 | — | thin_film | resistivity | — | 2022 | T1 | 2211.01609 |
| 5.8 | — | single_crystal | resistivity | — | 2024 | T1 | DOI: 10.1103/PhysRevResearch.6.L012046 |
| 5.7 | ambient | polycrystal | specific_heat, susceptibility | — | 2021 | T1 | 2102.11933 |
| 5.7 | — | — | STM | — | 2008 | — | 0807.1809 |
| 5.6 | ambient | single_crystal | susceptibility | s-wave | 2020 | T1 | DOI: 10.1103/PhysRevMaterials.4.084005 |
| 4.9 | — | single_crystal | resistivity | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.174505 |
| — | — | single_crystal | resistivity | — | 2024 | T1 | 2404.03461 |
| — | — | — | resistivity | — | 2024 | T1 | 2411.08980 |
| — | — | thin_film | — | — | 2023 | T1 | 2305.02216 |
| — | — | single_crystal | susceptibility | — | 2022 | — | 2201.09428 |
| — | ambient | polycrystal | specific_heat, susceptibility | — | 2021 | T1 | 2102.11933 |
| — | — | single_crystal | resistivity | — | 2021 | T3 | 2110.09379 |
| — | — | — | — | — | 2020 | — | 2004.01839 |
| — | — | single_crystal | specific_heat | — | 2020 | T1 | 2011.04880 |
| — | — | single_crystal | — | — | 2020 | T1 | DOI: 10.1103/PhysRevB.102.155115 |
| — | — | — | — | — | 2017 | — | 1708.01487 |
| — | — | — | — | — | 2016 | T1 | 1604.02867 |
Structure
- Crystal structure
- 2H
- Space group
- P3-m1 (#164)
- Lattice a (Å)
- 3.365
- Lattice c (Å)
- 5.954
Superconducting parameters
- Pairing symmetry
- s-wave
- Gap structure
- multi_gap
- λ_eph (e–ph coupling)
- —
Competing orders
- Competing order
- CDW
Samples & pressure
- Substrate
- Cr1/3NbS2
- Pressure type
- none
- Doping type
- none