NdFeAs(O,F)

iron_based

ambient SCunconventionaldisputed

Tc max

56.0 K

Tc ambient

56.0 K

arXiv year

2008

Papers

Tc exp.

48.0 K

Tc theo.

—

Evidence

experimental

Tc max measured at thin_film, resistivity, arXiv:2003.09105, confirmed by 2 papers

Evidence (27 records from 12 papers)

the flat columns above are aggregates — each line here is one paper's claim

Tc (K)	P (GPa)	Sample	Method	Pairing	Year	Tier	Paper
56.0	—	thin_film	resistivity	—	2020	T1	2003.09105
49.0	—	thin_film	resistivity	—	2020	T1	2003.09105
48.0	—	thin_film	resistivity	—	2010	T1	1005.0186
47.0	—	thin_film	resistivity	—	2017	T1	1712.05966
46.0	—	thin_film	susceptibility, resistivity	—	2021	T1	2111.10215
46.0	—	thin_film	resistivity	—	2020	T1	2003.09105
46.0	—	thin_film	resistivity	—	2017	T1	1712.05966
45.0	—	thin_film	resistivity	—	2020	T1	2003.09105
45.0	—	thin_film	resistivity	—	2019	T1	1904.03561
45.0	—	thin_film	resistivity	—	2010	T1	1005.0186
44.2	—	thin_film	resistivity	—	2019	T1	1901.02218
44.0	—	thin_film	resistivity	—	2020	T1	2003.09105
43.0	—	thin_film	resistivity	—	2020	T1	2003.09105
43.0	—	thin_film	susceptibility	—	2014	T1	1410.8743
42.0	—	thin_film	resistivity	—	2020	T1	2003.09105
42.0	—	thin_film	resistivity	—	2010	T1	1005.0186
40.0	—	thin_film	susceptibility	—	2010	T1	1005.0186
38.0	—	thin_film	resistivity	—	2019	T1	1904.03561
38.0	—	thin_film	resistivity	—	2010	T1	1005.0186
37.0	—	thin_film	resistivity	—	2014	T1	1410.8743
36.0	—	thin_film	resistivity	—	2020	T1	2003.09105
35.0	—	single_crystal	specific_heat	—	2008	—	0812.3953
34.0	—	single_crystal	susceptibility	—	2008	—	0812.3953
—	—	thin_film	resistivity, specific_heat	p-wave	2019	T1	1905.00183
—	—	thin_film	—	—	2018	T1	1802.06160
—	—	single_crystal	ARPES	—	2017	T1	DOI: 10.1103/PhysRevB.96.060501
—	—	single_crystal	resistivity	—	2009	—	0910.5198