Tc max
11.0 K
Tc ambient
—
arXiv year
2019
Papers
13
Tc exp.
11.0 K
Tc theo.
10.0 K
Evidence
theoretical
Tc max measured at thin_film, resistivity, DOI: 10.1103/PhysRevX.15.021048
Evidence (21 records from 13 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 11.0 | — | thin_film | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevX.15.021048 |
| 10.0 | — | — | — | — | 2019 | T1 | DOI: 10.1103/PhysRevB.100.205138 |
| 3.5 | — | — | — | — | 2023 | T1 | 2309.05486 |
| 1.7 | — | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.184505 |
| 1.7 | — | — | — | — | 2023 | T1 | 2309.05486 |
| 0.5 | — | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.184505 |
| 0.5 | — | — | — | — | 2023 | T1 | 2309.05486 |
| 0.3 | — | — | — | — | 2023 | T1 | 2309.05486 |
| 0.3 | — | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.184505 |
| 0.3 | — | — | — | — | 2023 | T1 | 2309.05486 |
| 0.0 | — | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.184505 |
| 0.0 | — | — | — | — | 2023 | T1 | 2309.05486 |
| — | — | — | resistivity | — | 2026 | T3 | 2601.19473 |
| — | — | — | — | — | 2026 | T1 | DOI: 10.1103/hl65-tls5 |
| — | — | thin_film | resistivity | — | 2023 | T1 | DOI: 10.1103/PhysRevMaterials.7.013802 |
| — | — | — | — | d-wave | 2023 | T1 | 2312.08260 |
| — | — | — | — | — | 2022 | — | 2205.15355 |
| — | — | polycrystal | — | d-wave | 2022 | T1 | DOI: 10.1103/PhysRevB.105.205131 |
| — | — | — | — | d-wave | 2022 | T3 | 2201.06950 |
| — | — | thin_film | — | d-wave | 2020 | T1 | DOI: 10.1103/PhysRevB.101.060504 |
| — | — | — | — | — | 2020 | T1 | DOI: 10.1103/PhysRevB.102.100501 |
Structure
- Crystal structure
- infinite-layer
- Space group
- P4/mmm
- Phase
- infinite_layer
- Lattice a (Å)
- 3.920
- Lattice c (Å)
- 3.280
Superconducting parameters
- Pairing symmetry
- d-wave
- λ_eph (e–ph coupling)
- 0.50
- ω_log
- 321 K
Samples & pressure
- Sample form
- thin_film
- Substrate
- SrTiO3
- Doping type
- none