Tc max
25.0 K
Tc ambient
—
arXiv year
2011
Papers
5
Tc exp.
—
Tc theo.
25.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=77 GPa, DOI: 10.1103/PhysRevLett.107.117002, confirmed by 3 papers
Evidence (13 records from 5 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 30.6 | 76.0 | — | — | — | 2013 | T1 | 1303.1223 |
| 25.0 | 77.0 | — | — | — | 2011 | T1 | DOI: 10.1103/PhysRevLett.107.117002 |
| 25.0 | 80.0 | — | — | — | 2011 | T1 | 1104.2313 |
| 20.0 | 100.0 | — | — | — | 2015 | T1 | 1504.01349 |
| 17.2 | 113.0 | — | — | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.054543 |
| 16.8 | 76.0 | — | — | — | 2013 | T1 | 1303.1223 |
| 15.8 | 100.0 | — | — | — | 2015 | T1 | 1504.01349 |
| 15.1 | 130.0 | — | — | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.054543 |
| 15.0 | 100.0 | — | — | — | 2011 | T1 | DOI: 10.1103/PhysRevLett.107.117002 |
| 12.9 | 100.0 | — | — | — | 2015 | T1 | 1504.01349 |
| 10.0 | 70.0 | — | — | — | 2011 | T1 | 1104.2313 |
| 9.7 | 160.0 | — | — | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.054543 |
| 7.1 | 192.0 | — | — | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.054543 |
Hydride Tc parameters (24)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| PtH | 7.0 | 30.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.144511 |
| PtH | 6.7 | 32.0 | — | — | — | susceptibility | 2019 | DOI: 10.1103/PhysRevB.99.144511 |
| PtH | 7.5 | 35.0 | — | — | — | resistivity | 2019 | DOI: 10.1103/PhysRevB.99.144511 |
| PtH | 4.8 | 36.0 | — | — | — | susceptibility | 2019 | DOI: 10.1103/PhysRevB.99.144511 |
| PtH | 17.5 | 75.0 | — | — | — | DFT | 2011 | 1104.2313 |
| PtH | 30.6 | 76.0 | 1.24 | 0.10 | — | Eliashberg | 2013 | 1303.1223 |
| PtH | 23.7 | 76.0 | 1.24 | 0.20 | — | Eliashberg | 2013 | 1303.1223 |
| PtH | 16.8 | 76.0 | 1.24 | 0.30 | — | Eliashberg | 2013 | 1303.1223 |
| PtH | 25.0 | 77.0 | — | 0.13 | — | McMillan | 2018 | 1806.00163 |
| PtH | 25.0 | 77.0 | — | 0.10 | — | DFT | 2011 | 1104.2313 |
| PtH | 25.0 | 77.0 | — | 0.10 | — | DFT | 2011 | DOI: 10.1103/PhysRevLett.107.117002 |
| PtH | 20.0 | 100.0 | 0.84 | 0.05 | — | Eliashberg | 2015 | 1504.01349 |
| PtH | 15.8 | 100.0 | 0.84 | 0.10 | — | Eliashberg | 2015 | 1504.01349 |
| PtH | 15.0 | 100.0 | — | — | — | DFT | 2011 | 1104.2313 |
| PtH | 15.0 | 100.0 | — | 0.10 | — | DFT | 2011 | DOI: 10.1103/PhysRevLett.107.117002 |
| PtH | 12.9 | 100.0 | 0.84 | 0.15 | — | Eliashberg | 2015 | 1504.01349 |
| PtH | 17.2 | 113.0 | 0.85 | 0.10 | 329 | Allen-Dynes | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 17.0 | 113.0 | — | — | — | resistivity | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 15.0 | 125.0 | — | — | — | resistivity | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 15.1 | 130.0 | 0.62 | 0.10 | 591 | Allen-Dynes | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 10.0 | 160.0 | — | — | — | resistivity | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 9.7 | 160.0 | 0.53 | 0.10 | 659 | Allen-Dynes | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 12.0 | 192.0 | — | — | — | resistivity | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
| PtH | 7.1 | 192.0 | 0.48 | 0.10 | 707 | Allen-Dynes | 2011 | DOI: 10.1103/PhysRevB.84.054543 |
Structure
- Crystal structure
- P63/mmc
- Space group
- P63/mmc
- Lattice a (Å)
- 2.700
- Lattice c (Å)
- 4.530
Superconducting parameters
- λ_eph (e–ph coupling)
- 0.85
- ω_log
- 707 K
Samples & pressure
- Pressure type
- hydrostatic