Tc max
6.0 K
Tc ambient
6.0 K
arXiv year
2016
Papers
7
Tc exp.
6.0 K
Tc theo.
—
Evidence
experimental
Tc max measured at ambient, polycrystal, resistivity, DOI: 10.1103/PhysRevB.105.224505, confirmed by 4 papers
Evidence (15 records from 7 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 6.4 | — | polycrystal | resistivity | s-wave | 2016 | T1 | DOI: 10.1103/PhysRevB.94.024518 |
| 6.2 | — | polycrystal | susceptibility, resistivity, specific_heat | s-wave | 2016 | T1 | DOI: 10.1103/PhysRevB.94.024518 |
| 6.0 | ambient | polycrystal | resistivity | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.224505 |
| 6.0 | — | polycrystal | resistivity, specific_heat | s-wave | 2016 | T1 | DOI: 10.1103/PhysRevB.94.054515 |
| 6.0 | — | polycrystal | resistivity, specific_heat | s-wave | 2016 | T1 | 1605.03812 |
| 6.0 | ambient | polycrystal | susceptibility | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.224505 |
| 5.9 | — | polycrystal | susceptibility | s-wave | 2016 | T1 | DOI: 10.1103/PhysRevB.94.054515 |
| 5.9 | — | polycrystal | magnetization, susceptibility | s-wave | 2016 | T1 | 1605.03812 |
| 5.9 | — | polycrystal | muSR | s-wave | 2017 | T1 | DOI: 10.1103/PhysRevB.96.180501 |
| 5.9 | 1.2 | polycrystal | susceptibility | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.224505 |
| 5.6 | 8.0 | polycrystal | resistivity | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.224505 |
| 5.6 | ambient | polycrystal | resistivity | — | 2022 | T1 | DOI: 10.1103/PhysRevB.105.224505 |
| 5.5 | — | polycrystal | resistivity | s-wave | 2016 | T1 | 1605.03812 |
| — | — | polycrystal | resistivity, susceptibility | — | 2022 | — | 2205.06500 |
| — | — | — | muSR | s-wave | 2017 | T1 | 1710.08598 |
Structure
- Crystal structure
- alpha-Mn
- Space group
- I4-3m (#217)
- Lattice a (Å)
- 9.685
Superconducting parameters
- Pairing symmetry
- s-wave
- Gap structure
- full_gap
- Hc2
- 12.2 T (0 K)
- λ_eph (e–ph coupling)
- 0.67
Competing orders
- ρ(T) exponent
- 2.20
Samples & pressure
- Sample form
- polycrystal
- Pressure type
- none