Tc max
196.0 K
Tc ambient
—
arXiv year
2017
Papers
2
Tc exp.
—
Tc theo.
196.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), arXiv:2106.10732, confirmed by 2 papers
Evidence (2 records from 2 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 196.0 | — | — | — | — | 2021 | T1 | 2106.10732 |
| 129.0 | 130.0 | — | — | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.094513 |
Hydride Tc parameters (28)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| ScH6 | 144.0 | 100.0 | — | — | — | DFT | 2023 | 2312.12694 |
| ScH6 | 229.0 | 114.0 | — | 0.13 | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 229.0 | 114.0 | — | — | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 129.0 | 130.0 | — | — | — | DFT | 2017 | DOI: 10.1103/PhysRevB.96.094513 |
| ScH6 | 119.0 | 130.0 | 1.39 | 0.10 | 1163 | Allen-Dynes | 2017 | DOI: 10.1103/PhysRevB.96.094513 |
| ScH6 | 100.0 | 130.0 | — | 0.10 | — | Eliashberg | 2021 | 2107.08669 |
| ScH6 | 100.0 | 130.0 | — | 0.15 | — | Eliashberg | 2021 | 2107.08669 |
| ScH6 | 63.0 | 145.0 | — | — | — | harmonic | 2021 | 2107.08669 |
| ScH6 | 217.0 | 161.0 | — | — | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 217.0 | 161.0 | — | 0.13 | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 186.0 | 200.0 | — | — | — | Eliashberg | 2025 | DOI: 10.1103/4hr1-vcvk |
| ScH6 | 186.0 | 200.0 | — | — | — | DFT | 2025 | DOI: 10.1103/4hr1-vcvk |
| ScH6 | 144.0 | 200.0 | 1.93 | 0.10 | 1026 | McMillan-Allen-Dynes | 2023 | DOI: 10.1103/PhysRevMaterials.7.054806 |
| ScH6 | 137.0 | 200.0 | — | — | — | DFT | 2023 | 2312.12694 |
| ScH6 | 98.0 | 200.0 | 1.38 | 0.10 | 938 | McMillan-Allen-Dynes | 2023 | DOI: 10.1103/PhysRevMaterials.7.054806 |
| ScH6 | 211.0 | 225.0 | — | — | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 211.0 | 225.0 | — | 0.13 | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 138.5 | 285.0 | 1.33 | 0.12 | — | Allen-Dynes | 2021 | 2111.03697 |
| ScH6 | 138.5 | 285.0 | 1.33 | 0.12 | — | McMillan | 2018 | 1810.12338 |
| ScH6 | 148.0 | 300.0 | 1.26 | — | — | Eliashberg | 2021 | DOI: 10.1103/PhysRevB.104.054501 |
| ScH6 | 95.0 | 300.0 | 1.20 | 0.12 | — | Eliashberg | 2021 | 2111.03697 |
| ScH6 | 95.0 | 300.0 | 1.20 | 0.12 | — | Eliashberg | 2018 | 1810.12338 |
| ScH6 | 187.0 | 310.0 | — | — | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 187.0 | 310.0 | — | 0.13 | — | Allen-Dynes | 2023 | DOI: 10.1103/PhysRevB.108.224508 |
| ScH6 | 169.0 | 350.0 | 1.25 | 0.10 | — | Eliashberg | 2021 | 2111.03697 |
| ScH6 | 169.0 | 350.0 | 1.25 | 0.10 | — | Eliashberg | 2018 | 1810.12338 |
| ScH6 | 135.0 | 350.0 | 1.25 | 0.10 | — | Allen-Dynes | 2021 | 2111.03697 |
| ScH6 | 135.0 | 350.0 | 1.25 | 0.10 | — | McMillan | 2018 | 1810.12338 |
Structure
- Crystal structure
- P63/mmc
- Space group
- P63/mmc
Superconducting parameters
- λ_eph (e–ph coupling)
- 1.39