Tc max
0.6 K
Tc ambient
—
arXiv year
2025
Papers
1
Tc exp.
0.6 K
Tc theo.
—
Evidence
experimental
Tc max measured at single_crystal, resistivity, DOI: 10.1103/PhysRevB.111.054522
Evidence (17 records from 1 paper)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 0.6 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.6 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.6 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.6 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.6 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.6 | — | single_crystal | susceptibility | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.5 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
| 0.4 | — | single_crystal | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevB.111.054522 |
Structure
- Crystal structure
- perovskite
- Lattice a (Å)
- 3.911
Superconducting parameters
- λ_eph (e–ph coupling)
- —
Samples & pressure
- Doping level
- 0.018