Tc max
6.5 K
Tc ambient
2.3 K
arXiv year
2015
Papers
22
Tc exp.
6.5 K
Tc theo.
3.3 K
Evidence
mixed
Tc max measured at P=15 GPa, resistivity, arXiv:1502.00493, confirmed by 2 papers
Evidence (26 records from 22 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 7.0 | 16.8 | — | — | — | 2015 | — | 1501.07394 |
| 6.5 | 15.0 | — | resistivity, susceptibility | — | 2015 | T1 | 1502.00493 |
| 6.0 | 9.8 | single_crystal | resistivity | — | 2017 | T1 | DOI: 10.1103/PhysRevB.96.180504 |
| 6.0 | 9.8 | single_crystal | resistivity | — | 2017 | — | 1711.00666 |
| 3.3 | — | thin_film | — | p-wave | 2020 | T1 | DOI: 10.1103/PhysRevLett.125.237006 |
| 3.3 | 9.8 | single_crystal | resistivity | — | 2017 | — | 1711.00666 |
| 2.6 | 25.0 | — | resistivity, susceptibility | — | 2015 | T1 | 1502.00493 |
| 2.3 | — | — | — | — | 2019 | T1 | 1911.02228 |
| 1.2 | — | thin_film | resistivity | unknown | 2020 | T1 | 2007.04752 |
| 1.0 | — | thin_film | resistivity | — | 2025 | T1 | DOI: 10.1103/PhysRevResearch.7.013224 |
| 1.0 | — | thin_film | resistivity | — | 2018 | — | 1809.04637 |
| — | — | single_crystal | resistivity | — | 2026 | T1 | DOI: 10.1103/jxks-s35x |
| — | — | thin_film | resistivity | unknown | 2025 | — | 2501.16699 |
| — | — | — | — | — | 2024 | T1 | 2405.09616 |
| — | — | — | — | s-wave | 2023 | T1 | 2308.07674 |
| — | — | — | — | — | 2023 | T1 | DOI: 10.1103/PhysRevB.107.064310 |
| — | — | thin_film | STM | p-wave | 2023 | T3 | 2304.08142 |
| — | — | — | — | — | 2022 | T1 | 2212.08117 |
| — | — | — | STM | — | 2022 | T1 | 2203.05171 |
| — | — | — | — | unknown | 2021 | T3 | 2103.12060 |
| — | — | thin_film | — | p-wave | 2020 | T2 | 2005.11012 |
| — | — | thin_film | — | — | 2019 | T1 | 1909.02433 |
| — | — | thin_film | resistivity | — | 2018 | T1 | 1811.06322 |
| — | — | thin_film | — | — | 2018 | — | 1809.04691 |
| — | 9.8 | single_crystal | resistivity | — | 2017 | — | 1711.00666 |
| — | 2.5 | — | — | — | 2015 | — | 1501.07394 |
Structure
- Crystal structure
- 1T'
Superconducting parameters
- Pairing symmetry
- p-wave
- Hc2
- 4.2 T (0.03 K, H perpendicular ab-plane)
- λ_eph (e–ph coupling)
- —
Competing orders
- Competing order
- CDW
Samples & pressure
- Sample form
- thin_film
- Substrate
- NbSe2
- Pressure type
- hydrostatic
- Doping type
- electron