YBa_2Cu_3O_x

cuprate · orthorhombic · cuprate_123

ambient SCunconventional2D / interfacedisputed

Tc max

93.2 K

Tc ambient

93.2 K

Discovery

1996

Papers

Tc max measured at ambient, single_crystal, susceptibility, arXiv:cond-mat/9612058, confirmed by 2 papers

Evidence (25 records from 20 papers)

the flat columns above are aggregates — each line here is one paper's claim

Tc (K)	P (GPa)	Sample	Method	Pairing	Year	Paper
100.0	ambient	—	—	—	1997	cond-mat/9701028
93.2	ambient	single_crystal	susceptibility	d-wave	1996	cond-mat/9612058
92.0	ambient	—	—	—	2002	cond-mat/0210560
92.0	ambient	—	—	d-wave	2001	cond-mat/0106251
89.5	ambient	polycrystal	resistivity	—	2003	cond-mat/0306560
89.0	ambient	thin_film	susceptibility	unknown	2001	cond-mat/0106559
89.0	ambient	thin_film	susceptibility	d-wave	2001	cond-mat/0107379
89.0	ambient	thin_film	susceptibility	d-wave	2000	cond-mat/0008077
89.0	ambient	single_crystal	susceptibility	d-wave	1996	cond-mat/9612058
87.2	ambient	ceramic	susceptibility	—	2001	cond-mat/0108060
87.0	ambient	thin_film	resistivity	d-wave	1999	cond-mat/9903065
85.0	ambient	thin_film	resistivity	—	1997	cond-mat/9701153
64.0	ambient	—	—	—	2003	cond-mat/0303383
63.0	ambient	—	—	—	2003	cond-mat/0303383
59.0	ambient	single_crystal	susceptibility	d-wave	1996	cond-mat/9612058
—	ambient	polycrystal	susceptibility	—	2004	cond-mat/0401239
—	ambient	polycrystal	susceptibility	—	2004	cond-mat/0406523
—	ambient	single_crystal	resistivity	—	2003	cond-mat/0302511
—	ambient	—	STM, susceptibility	d-wave	2003	cond-mat/0306716
—	ambient	thin_film	susceptibility	d-wave	2003	cond-mat/0306722
—	—	—	specific_heat	—	2001	cond-mat/0103195
—	ambient	single_crystal	—	—	2000	cond-mat/0012199
—	ambient	single_crystal	—	—	1999	cond-mat/9912357
—	0.6	single_crystal	—	—	1999	cond-mat/9912357
—	ambient	single_crystal	susceptibility, resistivity, ARPES, STM	d-wave	1996	cond-mat/9612058