Tc max
1.9 K
Tc ambient
1.9 K
arXiv year
2013
Papers
10
Tc exp.
1.9 K
Tc theo.
—
Evidence
experimental
Tc max measured at polycrystal, resistivity, arXiv:1810.00947, confirmed by 2 papers
Evidence (15 records from 10 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 1.9 | — | polycrystal | resistivity | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.020501 |
| 1.9 | — | polycrystal | resistivity | — | 2018 | T1 | 1810.00947 |
| 1.8 | ambient | polycrystal | resistivity, specific_heat, susceptibility | — | 2016 | T1 | DOI: 10.1103/PhysRevLett.116.127001 |
| 1.8 | ambient | polycrystal | resistivity | — | 2013 | T1 | 1311.0247 |
| 1.5 | ambient | polycrystal | susceptibility | — | 2013 | T1 | 1311.0247 |
| 1.4 | — | single_crystal | resistivity | — | 2014 | T1 | 1408.3319 |
| 1.4 | ambient | polycrystal | resistivity | — | 2013 | T1 | 1311.0247 |
| 1.1 | — | single_crystal | specific_heat, susceptibility, resistivity | unknown | 2020 | T1 | DOI: 10.1103/PhysRevLett.125.237002 |
| 1.0 | — | polycrystal | specific_heat | — | 2019 | T1 | DOI: 10.1103/PhysRevB.99.020501 |
| — | — | single_crystal | — | — | 2022 | T1 | DOI: 10.1103/PhysRevLett.129.046402 |
| — | — | single_crystal | resistivity, specific_heat | — | 2021 | T1 | 2104.11791 |
| — | — | single_crystal | resistivity, specific_heat | unknown | 2020 | — | 2007.13584 |
| — | — | polycrystal | specific_heat | — | 2018 | T1 | 1810.00947 |
| — | — | — | — | s_pm | 2013 | T1 | 1311.2922 |
| — | ambient | polycrystal | resistivity | — | 2013 | T1 | 1311.0247 |
Structure
- Crystal structure
- ThCr2Si2
- Space group
- I4/mmm
- Lattice a (Å)
- 3.964
- Lattice c (Å)
- 10.457
Superconducting parameters
- Hc2
- 1.7 T (low temperature limit)
- λ_eph (e–ph coupling)
- —
Competing orders
- Competing order
- AFM
- ρ(T) exponent
- 1.50
Samples & pressure
- Pressure type
- none