Tc max
3.0 K
Tc ambient
0.8 K
arXiv year
2011
Papers
22
Tc exp.
3.0 K
Tc theo.
—
Evidence
experimental
Tc max measured at susceptibility, arXiv:2312.17213, confirmed by 2 papers
Evidence (37 records from 22 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 3.0 | — | single_crystal | susceptibility | — | 2025 | T1 | DOI: 10.1103/qt3v-yypc |
| 3.0 | — | — | susceptibility | — | 2023 | T1 | 2312.17213 |
| 2.6 | — | single_crystal | STM | — | 2025 | T1 | DOI: 10.1103/qt3v-yypc |
| 2.6 | — | — | STM | — | 2023 | T1 | 2312.17213 |
| 1.0 | — | single_crystal | resistivity | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.035130 |
| 0.9 | ambient | single_crystal | resistivity | — | 2026 | T2 | 2603.11464 |
| 0.9 | 2.1 | single_crystal | resistivity | — | 2026 | T2 | 2603.11464 |
| 0.9 | 2.5 | single_crystal | resistivity | odd-parity | 2012 | T1 | 1206.3758 |
| 0.9 | 2.5 | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064515 |
| 0.9 | — | single_crystal | susceptibility | — | 2016 | T1 | DOI: 10.1103/PhysRevB.94.035130 |
| 0.9 | 2.0 | single_crystal | resistivity | odd-parity | 2012 | T1 | 1206.3758 |
| 0.8 | 2.0 | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064515 |
| 0.8 | 1.4 | single_crystal | resistivity | odd-parity | 2012 | T1 | 1206.3758 |
| 0.8 | 1.4 | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064515 |
| 0.8 | — | single_crystal | susceptibility | d-wave | 2021 | T1 | 2104.05908 |
| 0.8 | — | single_crystal | susceptibility | unknown | 2021 | T1 | DOI: 10.1103/PhysRevB.104.014510 |
| 0.8 | 0.7 | single_crystal | resistivity | odd-parity | 2012 | T1 | 1206.3758 |
| 0.8 | 0.7 | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064515 |
| 0.8 | 0.3 | single_crystal | resistivity | odd-parity | 2012 | T1 | 1206.3758 |
| 0.8 | — | single_crystal | susceptibility | unknown | 2023 | T1 | DOI: 10.1103/PhysRevLett.130.266002 |
| 0.8 | — | single_crystal | susceptibility | — | 2023 | T1 | 2305.09437 |
| 0.8 | — | single_crystal | susceptibility, muSR | — | 2013 | T1 | 1312.3229 |
| 0.8 | ambient | single_crystal | resistivity, susceptibility | odd-parity | 2012 | T1 | 1206.3758 |
| 0.8 | ambient | single_crystal | resistivity, susceptibility | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064515 |
| 0.8 | 0.3 | single_crystal | resistivity | — | 2012 | T1 | DOI: 10.1103/PhysRevB.86.064515 |
| 0.8 | — | single_crystal | resistivity, susceptibility | — | 2011 | T1 | DOI: 10.1103/PhysRevB.84.220504 |
| 0.8 | — | single_crystal | resistivity, susceptibility | — | 2011 | T1 | 1109.0979 |
| 0.7 | — | thin_film | resistivity | — | 2023 | T1 | DOI: 10.1103/PhysRevMaterials.7.024802 |
| — | — | single_crystal | resistivity | — | 2024 | T2 | 2402.18735 |
| — | — | — | resistivity, susceptibility | nodal | 2023 | T1 | 2312.17213 |
| — | — | — | — | s-wave | 2019 | — | 1911.03712 |
| — | — | — | — | s-wave | 2019 | T3 | 1908.09476 |
| — | — | — | — | — | 2018 | — | 1806.03773 |
| — | — | single_crystal | susceptibility | unknown | 2016 | T1 | 1603.03375 |
| — | — | — | — | d-wave | 2016 | T1 | 1603.03376 |
| — | — | — | STM | — | 2015 | T1 | 1510.00362 |
| — | — | thin_film | STM | — | 2015 | T1 | DOI: 10.1103/PhysRevB.92.094510 |
Structure
- Crystal structure
- cubic
- Space group
- F-43m (216)
- Lattice a (Å)
- 6.650
Superconducting parameters
- Gap structure
- nodal
- Hc2
- 2.2 T (T → 0 K)
- λ_eph (e–ph coupling)
- —
Competing orders
- ρ(T) exponent
- 1.85
Samples & pressure
- Sample form
- single_crystal
- Substrate
- Al2O3
- Doping type
- none